Title: Synthesis and Photoluminescence Properties of 2D Phenethylammonium Lead Bromide Perovskite Nanocrystals
Abstract

Organic–inorganic hybrid perovskites have emerged as promising optoelectronic materials for applications in photovoltaic and optoelectronic devices. Particularly, 2D layer‐structured hybrid perovskites are of great interest due to their remarkable optical and electrical properties, which can be easily tuned by selecting suitable organic and inorganic moieties during the material synthesis. Here, the solution‐phase growth of a large square‐shaped single‐crystalline 2D hybrid perovskite, phenethylammonium lead bromide (C6H5C2H4NH3)2PbBr4(PEPB), with thickness as few as 3 unit cell layers is demonstrated. Compared to bulk crystals, the 2D PEPB nanocrystals show a major blueshifted photoluminescence (PL) peak at 409 nm indicating an increase in bandgap of 40 meV. Besides the major peak, two new PL peaks located at 480 and 525 nm are observed from the hybrid perovskite nanocrystals. PEPB nanocrystals with different thicknesses show different colors, which can be used to estimate the thickness of the nanocrystals. Time‐resolved reflectance spectroscopy is used to investigate the exciton dynamics, which exhibits a biexponential decay with an amplitude‐weighted lifetime of 16.7 ps. The high‐quality 2D (C6H5C2H4NH3)2PbBr4nanocrystals are expected to have high PL quantum efficiency and potential applications for light‐emitting devices.

 
more » « less
NSF-PAR ID:
10041453
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Small Methods
Volume:
1
Issue:
10
ISSN:
2366-9608
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. null (Ed.)
    The past decade has witnessed tremendous advances in synthesis of metal halide perovskites and their use for a rich variety of optoelectronics applications. Metal halide perovskite has the general formula ABX 3 , where A is a monovalent cation (which can be either organic ( e.g. , CH 3 NH 3 + (MA), CH(NH 2 ) 2 + (FA)) or inorganic ( e.g. , Cs + )), B is a divalent metal cation (usually Pb 2+ ), and X is a halogen anion (Cl − , Br − , I − ). Particularly, the photoluminescence (PL) properties of metal halide perovskites have garnered much attention due to the recent rapid development of perovskite nanocrystals. The introduction of capping ligands enables the synthesis of colloidal perovskite nanocrystals which offer new insight into dimension-dependent physical properties compared to their bulk counterparts. It is notable that doping and ion substitution represent effective strategies for tailoring the optoelectronic properties ( e.g. , absorption band gap, PL emission, and quantum yield (QY)) and stabilities of perovskite nanocrystals. The doping and ion substitution processes can be performed during or after the synthesis of colloidal nanocrystals by incorporating new A′, B′, or X′ site ions into the A, B, or X sites of ABX 3 perovskites. Interestingly, both isovalent and heterovalent doping and ion substitution can be conducted on colloidal perovskite nanocrystals. In this review, the general background of perovskite nanocrystals synthesis is first introduced. The effects of A-site, B-site, and X-site ionic doping and substitution on the optoelectronic properties and stabilities of colloidal metal halide perovskite nanocrystals are then detailed. Finally, possible applications and future research directions of doped and ion-substituted colloidal perovskite nanocrystals are also discussed. 
    more » « less
  2. Zero-dimensional (0D) halides perovskites, in which anionic metal-halide octahedra (MX 6 ) 4− are separated by organic or inorganic countercations, have recently shown promise as excellent luminescent materials. However, the origin of the photoluminescence (PL) and, in particular, the different photophysical properties in hybrid organic–inorganic and all inorganic halides are still poorly understood. In this work, first-principles calculations were performed to study the excitons and intrinsic defects in 0D hybrid organic–inorganic halides (C 4 N 2 H 14 X) 4 SnX 6 (X = Br, I), which exhibit a high photoluminescence quantum efficiency (PLQE) at room temperature (RT), and also in the 0D inorganic halide Cs 4 PbBr 6 , which suffers from strong thermal quenching when T > 100 K. We show that the excitons in all three 0D halides are strongly bound and cannot be detrapped or dissociated at RT, which leads to immobile excitons in (C 4 N 2 H 14 X) 4 SnX 6 . However, the excitons in Cs 4 PbBr 6 can still migrate by tunneling, enabled by the resonant transfer of excitation energy (Dexter energy transfer). The exciton migration in Cs 4 PbBr 6 leads to a higher probability of trapping and nonradiative recombination at the intrinsic defects. We show that a large Stokes shift and the negligible electronic coupling between luminescent centers are important for suppressing exciton migration; thereby, enhancing the photoluminescence quantum efficiency. Our results also suggest that the frequently observed bright green emission in Cs 4 PbBr 6 is not due to the exciton or defect-induced emission in Cs 4 PbBr 6 but rather the result of exciton emission from CsPbBr 3 inclusions trapped in Cs 4 PbBr 6 . 
    more » « less
  3. Abstract

    2D hybrid organic–inorganic perovskites (HOIPs) are commonly found under subcritical cyclic stresses and suffer from fatigue issues during device operation. However, their fatigue properties remain unknown. Here, the fatigue behavior of (C4H9‐NH3)2(CH3NH3)2Pb3I10, the archetype 2D HOIP, is systematically investigated by atomic force microscopy (AFM). It is found that 2D HOIPs are much more fatigue resilient than polymers and can survive over 1 billion cycles. 2D HOIPs tend to exhibit brittle failure at high mean stress levels, but behave as ductile materials at low mean stress levels. These results suggest the presence of a plastic deformation mechanism in these ionic 2D HOIPs at low mean stress levels, which may contribute to the long fatigue lifetime, but is inhibited at higher mean stresses. The stiffness and strength of 2D HOIPs are gradually weakened under subcritical loading, potentially as a result of stress‐induced defect nucleation and accumulation. The cyclic loading component can further accelerate this process. The fatigue lifetime of 2D HOIPs can be extended by reducing the mean stress, stress amplitude, or increasing the thickness. These results can provide indispensable insights into designing and engineering 2D HOIPs and other hybrid organic–inorganic materials for long‐term mechanical durability.

     
    more » « less
  4. All-inorganic halide perovskite nanocrystals (NCs) offer impressive optoelectronic properties for light harvesting, energy conversion, and photoredox applications, with two-dimensional (2D) perovskite NCs further increasing these prospects due to their improved photoluminescence (PL) tuneability, impressive color purity, high in-plane charge transport, and large lateral dimensions which is advantageous for device integration. However, the synthesis of 2D perovskites is still challenging, especially toward large-scale applications. In this study, through the control of surface ligand composition and concentration of a mixture of short (octanoic acid and octylamine, 8-carbon chain) and long (oleic acid and oleylamine, 18-carbon chain) ligands, we have developed an extremely facile ligand-mediated synthesis of 2D CsPbX 3 (X = Cl, Br, or mixture thereof) nanoplatelets (NPLs) at room temperature in an open vessel. In addition, the developed method is highly versatile and can be applied to synthesize Mn-doped CsPbX 3 NPLs, showing a systematic increase in the total PL quantum yield (QY) and the Mn-dopant emission around 600 nm with increasing Mn and Cl concentrations. The reaction occurs in toluene by the introduction of CsX, PbX 2 , and MnX 2 precursors under ambient conditions, which requires no harsh acids, avoids excessive lead waste, little thermal energy input, and is potentially scalable toward industrial applications. 
    more » « less
  5. Surface depletion field would introduce the depletion region near surface and thus could significantly alter the optical, electronic and optoelectronic properties of the materials, especially low-dimensional materials. Two-dimensional (2D) organic—inorganic hybrid perovskites with van der Waals bonds in the out-of-plane direction are expected to have less influence from the surface depletion field; nevertheless, studies on this remain elusive. Here we report on how the surface depletion field affects the structural phase transition, quantum confinement and Stark effect in 2D (BA)2PbI4 perovskite microplates by the thickness-, temperature- and power-dependent photoluminescence (PL) spectroscopy. Power dependent PL studies suggest that high-temperature phase (HTP) and low-temperature phase (LTP) can coexist in a wider temperature range depending on the thickness of the 2D perovskite microplates. With the decrease of the microplate thickness, the structural phase transition temperature first gradually decreases and then increases below 25 nm, in striking contrast to the conventional size dependent structural phase transition. Based on the thickness evolution of the emission peaks for both high-temperature phase and low-temperature phase, the anomalous size dependent phase transition could probably be ascribed to the surface depletion field and the surface energy difference between polymorphs. This explanation was further supported by the temperature dependent PL studies of the suspended microplates and encapsulated microplates with graphene and boron nitride flakes. Along with the thickness dependent phase transition, the emission energies of free excitons for both HTP and LTP with thickness can be ascribed to the surface depletion induced confinement and Stark effect. 
    more » « less