Title: Effect of electrospinning processing variables on polyacrylonitrile nanoyarns
ABSTRACT

With recent developments in the field of smart textiles, researchers have been working toward fabricating architectures of nanofibers, known as nanoyarns, which mimic the geometry of a conventional yarn. In doing so, one can leverage the unique properties of nanoscale fibers, including high surface‐to‐volume ratio and tunable porosity, for the development of smart garments. In the last 5 years, researchers have produced nanoyarns from a limited number of polymers, including polyacrylonitrile (PAN) and poly(vinylidene fluoride) and its co‐polymers. However, to our knowledge, there has been little research on the solution properties and electrospinning parameters needed to fabricate these higher‐order architectures from nonwoven mats. In this work, a modified electrospinning setup, enclosed in a humidity‐controlled chamber, was developed to fabricate nanoyarns for integration into knitted textiles. We fabricated nanofibers and nanoyarns from PAN/DMF solutions and conducted a systematic study to analyze the effect of solution conductivity, viscosity, and electrospinning parameters (applied voltage, collector distance, and humidity) on fiber and yarn fabrication and morphology. Polymer concentration had a significant effect on fibrous cone and yarn fabrication. Low polymer concentrations resulted in poor cone formation, whereas high concentration resulted in dense cones that were difficult to draw into nanoyarns. Overall, the matrix of electrospinning parameters that resulted in the formation of homogenous nanofiber mats was larger than that of nanoyarn formation. Nanoyarn formation required higher polymer concentration and/or applied voltage than nonwoven mat formation. The influence of these parameters on nanoyarn formation and fiber diameter can be used to expand the library of spinnable nanoyarns and optimize their properties for specific applications. © 2018 Wiley Periodicals, Inc. J. Appl. Polym. Sci.2018,135, 46404.

 
more » « less
NSF-PAR ID:
10054520
Author(s) / Creator(s):
 ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Journal of Applied Polymer Science
Volume:
135
Issue:
25
ISSN:
0021-8995
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ABSTRACT

    This work addresses a systematic study for the process development and optimization of poly(d,l‐lactic acid) (PDLLA) submicrometer fibers utilizing the centrifugal spinning technique known as Forcespinning. This study analyzes the effect of polymer concentration (8, 10, and 12 wt %) and angular speed on the fiber morphology, diameter distribution, and fiber yield. The increase in polymer concentration and angular speed favored the formation of continuous and homogeneous submicrometer fibers with an absence of bead formation and higher output. The optimal conditions were established considering the morphological characteristics that exhibit a greater surface area (homogeneous and submicrometer fibers); and they were achieved at a polymer concentration of 10 wt % at an angular speed ranging from 8000 to 10 000 rpm. Optimization of PDLLA submicrometer fiber fabrication lays the groundwork for scaling up the process and serves as a platform to further develop promising applications of PDLLA nonwoven mats, particularly in the biomedical area such as in scaffolds for tissue engineering. © 2019 Wiley Periodicals, Inc. J. Appl. Polym. Sci.2019,136, 47643.

     
    more » « less
  2. null (Ed.)
    Abstract

    Electrospinning is a promising process to fabricate functional parts from macrofibers and nanofibers of bio-compatible materials including collagen, polylactide (PLA), and polyacrylonitrile (PAN). However, the functionality of the produced parts highly rely on quality, repeatability, and uniformity of the electrospun fibers. Due to the variations in material composition, process settings, and ambient conditions, the process suffers from large variations. In particular, the fiber formation in the stable regime (i.e., Taylor cone and jet) and its propagation to the substrate plays the most significant role in the process stability. This work aims to designing a fast process monitoring tool from scratch for monitoring the dynamic electrospinning process based on the Taylor cone and jet videos. Nevertheless, this is challenging since the videos are of high frequency and high dimension, and the monitoring statistics may not have a parametric distribution. To achieve this goal, a framework integrating image analysis, sketch-based tensor decomposition, and non-parametric monitoring, is proposed. In particular, we use Tucker tensor-sketch (Tucker-TS) based tensor decomposition to extract the sparse structure representations of the videos. Additionally, the extracted monitoring variables are non-normally distributed, hence non-parametric bootstrap Hotelling T2 control chart is deployed to handle this issue during the monitoring. The framework is demonstrated by electrospinning a PAN-based polymeric solution. Finally, it is demonstrated that the proposed framework, which uses Tucker-TS, largely outperformed the computational speed of the alternating least squares (ALS) approach for the Tucker tensor decomposition, i.e., Tucker-ALS, in various anomaly detection tasks while keeping the comparable anomaly detection accuracy.

     
    more » « less
  3. In an effort to develop and design next generation high power target materials for particle physics research, the possibility of fabricating nonwoven metallic or ceramic nanofibers by electrospinning process is explored. A low-cost electrospinning unit is set up for in-house production of various ceramic nanofibers. Yttria-stabilized zirconia nanofibers are successfully fabricated by electrospinning a mixture of zirconium carbonate with high-molecular weight polyvinylpyrrolidone polymer solution. Some of the inherent weaknesses of electrospinning process like thickness of nanofiber mat and slow production rate are overcome by modifying certain parts of electrospinning system and their arrangements to get thicker nanofiber mats of millimeter order at a faster rate. Continuous long nanofibers of about hundred nanometers in diameter are produced and subsequently heat treated to get rid of polymer and allow crystallize zirconia. Specimens were prepared to meet certain minimum physical properties such as thickness, structural integrity, thermal stability, and flexibility. An easy innovative technique based on atomic force microscopy was employed for evaluating mechanical properties of single nanofiber, which were found to be comparable to bulk zirconia. Nanofibers were tested for their high-temperature resistance using an electron beam. It showed resistance to radiation damage when irradiated with 1 MeV Kr2+ ion. Some zirconia nanofibers were also tested under high-intensity pulsed proton beam and maintained their structural integrity. This study shows for the first time that a ceramic nanofiber has been tested under different beams and irradiation condition to qualify their physical properties for practical use as accelerator targets. Advantages and challenges of such nanofibers as potential future targets over bulk material targets are discussed. 
    more » « less
  4. Abstract

    Electrospinning of nanofiber is of growing interest especially in bone tissue engineering because of its similar fibrous properties to the extracellular matrix. To this end, we have fabricated polycaprolactone (PCL) nanofiber shish kebab (NFSK) templates. The novelty of this work is the ability to control the mineral orientation and spatial location on the nanofiber, mimicking natural collagen fibers. However, NFSK templates have properties that need to be investigated in terms of cellular response including fiber alignment and crystallization. In this study, MC3T3 E1 preosteoblast cells were seeded onto the templates to determine the effect of both fiber orientation and kebab size on the cell metabolic activity. PCL was electrospun to form aligned and randomly oriented nanofibers, which were then crystallized in a PCL solution in pentyl acetate for 15 and 60 min, resulting in the formation of homopolymer PCL NFSK templates. We evaluated the cell proliferation and alkaline phosphatase activity of MC3T3 E1 cells after 3, 7, and 14 days in coculture. Aligned nanofiber and polymer crystallization both significantly increased the cell proliferation and alkaline phosphatase activity at each time point. The aligned nanofibers and polymer crystallization resulted in the highest metabolic activities of the cells compared to the randomly oriented fibers and noncrystallized controls. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 1141–1149, 2019.

     
    more » « less
  5. Electrospinning is a versatile approach to generate nanofibers in situ. Yet, recently, wet electrospinning has been introduced as a more efficient way to deposit isolated fibers inside bulk materials. In wet electrospinning, a liquid bath is adopted, instead of a solid collector, for fiber collection. However, despite several studies focused on wet electrospinning to yield polymer composites, few studies have investigated wet electrospinning to yield ceramic composites. In this paper, we propose a novel in-situ fabrication approach for nanofiber-reinforced ceramic composites based on an enhanced wet-electrospinning method. Our method uses electrospinning to draw polymer nanofibers directly into a reactive pre-ceramic gel, which is later activated to yield advanced nanofiber-reinforced ceramic composites. We demonstrate our method by investigating wet electrospun Polyacrylonitrile and Poly(ethylene oxide) fiber-reinforced geopolymer composites, with fiber weight fractions in the range 0.1–1.0 wt%. Wet electrospinning preserves the amorphous structure of geopolymer while changing the molecular arrangement. Wet electrospinning leads to an increase in both the fraction of mesopores and the overall porosity of geopolymer composites. The indentation modulus is in the range 6.76–8.90 GPa and the fracture toughness is in the range 0.49–0.76 MPam with a clear stiffening and toughening effect observed for Poly(ethylene oxide)-reinforced geopolymer composites. This work demonstrates the viability of wet electrospinning to fabricate multifunctional nanofiber-reinforced composites. 
    more » « less