Porous organic cages (POCs) are individual soluble, porous molecules. When fabricated into mixed‐matrix membranes (MMMs), the soluble POC molecules have the potential to exhibit intimate molecular‐level mixing with the polymer matrix. POCs have only recently been incorporated into mixed matrix membrane materials, but this process has not yet resulted in significant improvements of membrane performance. Now, vertex‐functionalized amorphous scrambled porous organic cages (ASPOCs) have been utilized as membrane performance enhancers and the amorphous ASPOC mixtures are observed to distribute throughout the matrix without any indication of particle formation or agglomeration, creating unique, molecularly mixed composite membranes. Overall, the molecularly mixed composite membrane provide significant increases in both membrane permeability and selectivity, offering new avenues for creation of membranes with unique properties in industrially relevant separations.
Porous organic cages (POCs) are individual soluble, porous molecules. When fabricated into mixed‐matrix membranes (MMMs), the soluble POC molecules have the potential to exhibit intimate molecular‐level mixing with the polymer matrix. POCs have only recently been incorporated into mixed matrix membrane materials, but this process has not yet resulted in significant improvements of membrane performance. Now, vertex‐functionalized amorphous scrambled porous organic cages (ASPOCs) have been utilized as membrane performance enhancers and the amorphous ASPOC mixtures are observed to distribute throughout the matrix without any indication of particle formation or agglomeration, creating unique, molecularly mixed composite membranes. Overall, the molecularly mixed composite membrane provide significant increases in both membrane permeability and selectivity, offering new avenues for creation of membranes with unique properties in industrially relevant separations.
more » « less- PAR ID:
- 10083942
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Angewandte Chemie International Edition
- Volume:
- 58
- Issue:
- 9
- ISSN:
- 1433-7851
- Page Range / eLocation ID:
- p. 2638-2643
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
Membrane-based separations offer the potential for the lowest energy demand requirements of all separation options. Among all nanoporous membranes, the carbon molecular sieves (CMS), metal-organic frameworks (MOFs), and mixed-matrix membranes (MMMs) with angstrom level molecular discrimination properties makes them appealing for separating a wide spectrum of gas-pairs. Here we present results of gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) in porous organic cages (POCs) incorporated into fluorinated copolyimides polymers (FCPs). The FCPs were synthesized by the iridization reaction of fluorinated dianhydrides, nonfluorinated dianhydride, and nonfluorinated diamine. Asymmetric hollow fiber membranes formed by the dry-jet/wet-quench spinning process. Once fresh FCP fibers were synthesized, they were crosslinked with POCs, vacuum dried at 90 °C. We investigated the uptake, gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) over synthesized POC-mixed matrixed membranes (POC-MMM) at 25 °C and pressures up to 1 bar. At 1 bar and 25 °C, C2H6, C2H4, C3H8, C3H6 adsorption capacities reached to 42.61, 2.56, 2.77 and 2.65 mmol/g over POC-MMM, respectively, while CO2, CH4, CO, N2 and H2 adsorption capacities of 1.48, 0.84, 0.33, 0.11, and 0.068 mmol/g, respectively. Furthermore, stable CMS membrane were formed by pyrolysis of POC-MMMs under an inert argon atmosphere at 1 atm. To test the gas transport properties of CMS-derived POC/MMM, a lab-scale hollow fiber module with two-five fibers was constructed. The results of longer-term operation of synthesized CMS membrane that was continuously operated for 264 h (10 days) with an equimolar binary H2/CO2, CH4/CO2 and C3H6/C3H8 feed at 25°C and 1 bar feed pressure. The modification yielded promising results in the reduction of physical aging of CMS membranes.more » « less
-
Here we present results of gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) in porous organic cages (POCs) incorporated into fluorinated copolyimides polymers (FCPs). The FCPs were synthesized by the thermal and chemical imidization reaction of fluorinated dianhydrides, nonfluorinated dianhydride, and nonfluorinated diamine. Asymmetric hollow fiber membranes formed by the dry-jet/wet-quench spinning process. Once fresh FCP fibers were synthesized, they were crosslinked with POCs, vacuum dried at 90 °C. We investigated the uptake, gas selectivity and diffusion of different gases (C3H8, C3H6, CO2, and H2) over synthesized POC-mixed matrixed membranes (POC-MMM) at 25 °C and pressures up to 1 bar. At 1 bar and 25 °C, C3H8, C3H6 adsorption capacities reached 2.77 and 2.65 mmol/g over POC-MMM, respectively, while CO2, CH4, CO, N2 and H2 adsorption capacities of 1.48, 0.84, 0.33, 0.11, and 0.068 mmol/g, respectively. Furthermore, stable CMS membrane was formed by pyrolysis of POC-MMMs under an inert argon atmosphere at 1 atm. To test the gas transport properties of CMS-derived POC/MMM, a lab-scale hollow fiber module with two-five fibers was constructed. The results of longer-term operation of synthesized CMS membrane that was continuously operated for 264 h (10 days) with an equimolar binary H2/CO2, CH4/CO2 and C3H6/C3H8 feed at 25°C and 1 bar feed pressure. The modification yielded promising results in the reduction of physical aging of CMS membranes.more » « less
-
more » « less
Abstract 2D covalent organic frameworks (2D COFs) are attractive candidates for next‐generation membranes due to their robust linkages and uniform, tunable pores. Many publications have claimed to achieve selective molecular transport through COF pores, but reported performance metrics for similar networks vary dramatically, and in several cases the reported experiments are inadequate to support such conclusions. These issues require a reevaluation of the literature. Published examples of 2D COF membranes for liquid‐phase separations can be broadly divided into two categories, each with common performance characteristics: polycrystalline COF films (most >1 µm thick) and weakly crystalline or amorphous films (most <500 nm thick). Neither category has demonstrated consistent relationships between the designed COF pore structure and separation performance, suggesting that these imperfect materials do not sieve molecules through uniform pores. In this perspective, rigorous practices for evaluating COF membrane structures and separation performance are described, which will facilitate their development toward molecularly precise membranes capable of performing previously unrealized chemical separations. In the absence of this more rigorous standard of proof, reports of COF‐based membranes should be treated with skepticism. As methods to control 2D polymerization improve, precise 2D polymer membranes may exhibit exquisite and energy efficient performance relevant for contemporary separation challenges.
-
more » « less
Abstract Desalination by membrane distillation (MD) using low‐grade or waste heat provides a potential route for sustainable water supply. Nonwetting, porous membranes that provide a selective pathway for water vapor over nonvolatile salt are at the core of MD desalination. Conventional water‐repelling MD membranes (i.e., hydrophobic and superhydrophobic membranes) fail to ensure long‐term desalination performance due to pore wetting and surface fouling. To address these challenges, a defect‐free carbon nanotube forest (CNTF) is engineered in situ on a porous electrospun silica fiber substrate. The engineered CNTF forms an ultrarough and porous interface structure, allowing outstanding wetting resistance against water in air and oil underwater. As a result of this antiwetting property, the composite CNTF membrane displays a stable water vapor flux and a near complete salt rejection (>99.9%) in the desalination of highly saline water containing low surface tension contaminants. The antimicrobial property of the composite CNTF membrane imparted by the unique forest‐like architecture and the oxidative effect of carbon nanotubes (CNTs) are further demonstrated. The results exemplify an effective strategy for engineering CNT architecture to elucidate the structure–property–performance relationship of the nanocomposite membranes and to guide the design of robust thermal desalination membranes.