Rapid advancements within photovoltaics realm necessitates swift fabrication of the modules using cheap materials through cost effective manufacturing processes to achieve short cost payback time. Photovoltaics manufacturing includes chemical processing of the materials followed by thermal annealing. Yet, long-term annealing of the materials using high temperature furnaces have remained the prevalent post-processing approach in industry which necessitates alternative methods to achieve high performance modules through rapid and economical processes. Intense pulse light (IPL) has been successfully applied as a promising rapid post-process annealing for various thin film photovoltaics, particularly to process the organic-inorganic perovskite solar cell (PSC) layers. In this paper, several results pertinent to the application of IPL on perovskite and SnO2 electron transport thin films are presented and the role of IPL on rapid thermal annealing (RTA) is explained. We show that swift fabrication of PSCs through IPL can result in efficiencies exceeding 16% when the Perovskite film is annealed with aid of CH2I2 alkyl halide additive in the ambient with 60% relative humidity. In addition, the synergy of IPL-alkyl halide interaction for other perovskite chemistries is introduced. We show that achieving to PSCs exceeding 12% efficiency was possible when the perovskite and SnO2 ETL was annealed sequentially through IPL.more » « less
-
Rapid chemistry and processing development has increased the performance of perovskite solar cells (PSCs) in an unprecedented manner, yet postdeposition annealing impedes high‐throughput manufacturing. Herein, SnO2and carbon charge transport films are fabricated entirely through an integrated robotic setup utilizing inkjet printing and intense pulse light (IPL) as a high‐speed postprocess annealing method; hence, process optimization is crucial for successful fabrication of PSCs. This work investigates the role of inkjet deposition parameters as well as IPL annealing on the morphology and uniformity of films with aid of spectroscopy and spectrophotometry. Initially PSCs exceeding 13% efficiency are developed by only fabricating the SnO2film through the robotic setup, but spin coating all other films followed by IPL annealing to demonstrate successful fabrication of SnO2layer. Finally, SnO2and carbon back contact films are entirely fabricated through the integrated robotic setup in a high humid ambient environment (>60%), resulting in PSCs exceeding 5% efficiency. Unlike successful direct annealing of SnO2wet films, IPL annealing of wet carbon severely damaged the phase and morphology necessitating rapid solvent removal before IPL annealing. This work establishes pioneering steps towards utilizing IPL in an entirely automated fabrication line, allowing for scalable fabrication of PSCs through non‐roll‐to‐roll.
-
Abstract The two‐step conversion process consisting of metal halide deposition followed by conversion to hybrid perovskite has been successfully applied toward producing high‐quality solar cells of the archetypal MAPbI3hybrid perovskite, but the conversion of other halide perovskites, such as the lower bandgap FAPbI3, is more challenging and tends to be hampered by the formation of hexagonal nonperovskite polymorph of FAPbI3, requiring Cs addition and/or extensive thermal annealing. Here, an efficient room‐temperature conversion route of PbI2into the α‐FAPbI3perovskite phase without the use of cesium is demonstrated. Using in situ grazing incidence wide‐angle X‐ray scattering (GIWAXS) and quartz crystal microbalance with dissipation (QCM‐D), the conversion behaviors of the PbI2precursor from its different states are compared. α‐FAPbI3forms spontaneously and efficiently at room temperature from P2(ordered solvated polymorphs with DMF) without hexagonal phase formation and leads to complete conversion after thermal annealing. The average power conversion efficiency (PCE) of the fabricated solar cells is greatly improved from 16.0(±0.32)% (conversion from annealed PbI2) to 17.23(±0.28)% (from solvated PbI2) with a champion device PCE > 18% due to reduction of carrier recombination rate. This work provides new design rules toward the room‐temperature phase transformation and processing of hybrid perovskite films based on FA+cation without the need for Cs+or mixed halide formulation.
-
Organic–inorganic lead halide perovskite solar cells are regarded as one of the most promising technologies for the next generation of photovoltaics due to their high power conversion efficiency (PCE) and simple solution manufacturing. Among the different compositions, the formamidinium lead iodide (FAPbI3) photoactive phase has a bandgap of 1.4 eV, which enables the corresponding higher PCEs according to the Shockley–Queisser limit. However, the photoactive crystal phase of FAPbI3is not stable at room temperature. The most high‐performing compositions to date have reduced this problem by incorporating the methylammonium (MA) cation into the FAPbI3composition, although MA has poor stability at high temperatures and in humid environments, which can limit the lifetime of FA
x MA1−x PbI3films. Csx FA1−x PbI3perovskites are also explored, but despite better stability they still lag in performance. Herein, the additive engineering of MA‐free organic−inorganic lead halide perovskites using divalent cations Sr2+and Ca2+to enhance the performances of Csx FA1−x PbI3perovskite compositions is explored. It is revealed that the addition of up to 0.5% of Sr2+and Ca2+leads to improvements in morphology and reduction in microstrain. The structural improvements observed correlate with improved solar cell performances at low additive concentrations. -
Abstract Understanding interfacial reactions that occur between the active layer and charge‐transport layers can extend the stability of perovskite solar cells. In this study, the exposure of methylammonium lead iodide (CH3NH3PbI3) thin films prepared on poly(3,4‐ethylenedioxythiophene):poly(styrenesulfonate) (PEDOT:PSS)‐coated glass to 70% relative humidity (R.H.) leads to a perovskite crystal structure change from tetragonal to cubic within 2 days. Interface‐sensitive photoluminescence measurements indicate that the structural change originates at the PEDOT:PSS/perovskite interface. During exposure to 30% R.H., the same structural change occurs over a much longer time scale (>200 days), and a reflection consistent with the presence of (CH3)2NH2PbI3is detected to coexist with the cubic phase by X‐ray diffraction pattern. The authors propose that chemical interactions at the PEDOT:PSS/perovskite interface, facilitated by humidity, promote the formation of dimethylammonium, (CH3)2NH2+. The partial A‐site substitution of CH3NH3+for (CH3)2NH2+to produce a cubic (CH3NH3)1−
x [(CH3)2NH2]x PbI3phase explains the structural change from tetragonal to cubic during short‐term humidity exposure. When (CH3)2NH2+content exceeds its solubility limit in the perovskite during longer humidity exposures, a (CH3)2NH2+‐rich, hexagonal phase of (CH3NH3)1−x [(CH3)2NH2]x PbI3emerges. These interfacial interactions may have consequences for device stability and performance beyond CH3NH3PbI3model systems and merit close attention from the perovskite research community.