The icy shells of Enceladus and Europa consist from top down of cold (~100 K) ice at low (<0.1 MPa) pressure, cold ice at high pressure up to ~10 MPa, and warm ice near 273 K the base. The pressure ~10 MPa and temperature near 273 K of basal ice within Enceladus and Europa are similar to that within terrestrial glaciers that are known to have seismicity (icequakes). Warm ice easily melts during sliding so its icequakes are qualitatively explained and expected on these satellites if the macroscopic strain rates are comparable to those within terrestrial glaciers subjected to oceanic tides. However, cold ice at high pressures does not readily macroscopically melt during sliding. A dynamic weakening mechanism for crustal faults in rock may be applicable to Enceladus and Europa. Micron‐scale real contacts support ~0.4‐GPa shear tractions and normal tractions on rapidly sliding ice faults. At sliding velocities above ~0.1 m/s, the asperity tips of the contacts become hot and weak in ice. The macroscopic friction depends on the average strength of the asperity tips during the lifetimes of contact. The strength of the asperity tips self‐organizes so that frictional heating balances the heat lost from the asperity tip by conduction. The macroscopic coefficient of friction at coseismic sliding velocities decreases to a modest fraction of the low‐velocity coefficient of friction, but does not approach zero. This velocity‐weakening mechanism likely allows major icequakes within the cold interiors of Europa and Enceladus.
We present experimental evidence for a new mechanism for how smooth surfaces emerge during repetitive sliding contacts, as in polishing. Electron microscopy observations of Ti-6Al-4V surface with a spherical asperity structure—realized via additive manufacturing—during successive polishing stages suggest that asperity-abrasive contacts exhibit viscous behavior, where the asperity material flows in the form of thin (1–10
- NSF-PAR ID:
- 10153631
- Publisher / Repository:
- Nature Publishing Group
- Date Published:
- Journal Name:
- Scientific Reports
- Volume:
- 9
- Issue:
- 1
- ISSN:
- 2045-2322
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
Garcia Aznar, Jose Manuel (Ed.)Human skin enables interaction with diverse materials every day and at all times. The ability to grasp objects, feel textures, and perceive the environment depends on the mechanical behavior, complex structure, and microscale topography of human skin. At the same time, abrasive interactions, such as sometimes occur with prostheses or textiles, can damage the skin and impair its function. Previous theoretical and computational efforts have shown that skin’s surface topography or microrelief is crucial for its tribological behavior. However, current understanding is limited to adult surface profiles and simplified two-dimensional simulations. Yet, the skin has a rich set of features in three dimensions, and the geometry of skin is known to change with aging. Here we create a numerical model of a dynamic indentation test to elucidate the effect of changes in microscale topography with aging on the skin’s response under indentation and sliding contact with a spherical indenter. We create three different microrelief geometries representative of different ages based on experimental reports from the literature. We perform the indentation and sliding steps, and calculate the normal and tangential forces on the indenter as it moves in three distinct directions based on the characteristic skin lines. The model also evaluates the effect of varying the material parameters. Our results show that the microscale topography of the skin in three dimensions, together with the mechanical behavior of the skin layers, lead to distinctive trends on the stress and strain distribution. The major finding is the increasing role of anisotropy which emerges from the geometric changes seen with aging.more » « less
-
more » « less
Abstract Geometric diodes (GDs) represent a relatively unconventional class of diode that produces an asymmetric current response through carrier transport in an asymmetric geometry. Synthesized from the bottom up, Si nanowire‐based GDs are three‐dimensional, cylindrically symmetric nanoscale versions capable of room‐temperature rectification at GHz‐THz frequencies with near zero‐bias turn‐on voltages. Here, by fabricating three‐terminal n‐type Si nanowire GDs with axial contacts and an omega‐gate electrode, a distinct class of reconfigurable self‐switching geometric diodes (SSGDs) is reported. Single‐nanowire SSGD device measurements demonstrate a significant dependence of diode current and polarity on gate potential, where the diode polarity reverses at a gate potential of ≈−1 V under specific grounding conditions. Finite‐element modeling reproduces the experimental results and reveals that the gate potential—in combination with the morphology and dopant profile—produces an asymmetric potential along the nanowire axis that changes asymmetrically with axial bias, altering the effective conductive channel within the nanowire to yield diode behavior. The self‐switching effect is retained in two‐terminal SSGD devices, and modeling demonstrates that both three‐terminal and two‐terminal devices support rectification through THz frequencies. The results reveal a new mechanism of operation for nanowire‐based GDs and characterize a new type of self‐switching diode with reconfigurable polarity.
-
more » « less
Abstract The application of agricultural plastic products such as mulch, greenhouse covers, and silage films is increasing due to their economic benefits in providing an early and better‐quality harvest. However, mechanical abrasion of these plastic materials by soil particles could result in generation of microplastic (MP) pollutants that could harm soil organisms and impact food safety. This study aims to better understand the physicochemical mechanisms resulting in the fragmentation of low‐density polyethylene (LDPE). Herein, we used pellets and films to study the impacts of abrasive wear forces on their surface morphology variations and fragmentation behavior. An innovative laboratory approach was developed to abrade the plastic surface under controlled normal loadings and abrasion durations. The investigation of the plastics’ surface morphology variations due to the abrasion process revealed microcutting as the dominant process at low normal force (4 N). However, a combination of microploughing and microcutting occurred for new LDPE films by increasing the normal force to 8 N. Despite the significant surface morphology variations of the new LDPE film due to the abrasion process; the water contact angle did not alter. Furthermore, the fragmentation behavior of photodegraded LDPE pellets and films was compared to the new plastics. The extent of MPs (3 µm <
d p < 162 µm) generation due to fragmentation was studied using fluorescence microscopy imaging. The localized stress and strains at the contact sites of plastic and sand particles resulted in abrasion of the plastic surface. According to the results, the normal loadings and duration of abrasion played a significant role in the degree of fragmentation of plastics. Increasing the normal loading applied during the abrasion process from 2 to 8 N linearly increased the number of generated plastic fragments by more than five times for pellets and more than three times for film. Photodegradation significantly enhanced the extent of MPs fragmentation. Moreover, the limitations of this study and the implications for agricultural soil health were discussed. -
more » « less
Abstract We present new data from the debris-rich basal ice layers of the NEEM ice core (NW Greenland). Using mineralogical observations, SEM imagery, geochemical data from silicates (meteoric10Be, εNd,87Sr/86Sr) and organic material (C/N, δ13C), we characterize the source material, succession of previous glaciations and deglaciations and the paleoecological conditions during ice-free episodes. Meteoric10Be data and grain features indicate that the ice sheet interacted with paleosols and eroded fresh bedrock, leading to mixing in these debris-rich ice layers. Our analysis also identifies four successive stages in NW Greenland: (1) initial preglacial conditions, (2) glacial advance 1, (3) glacial retreat and interglacial conditions and (4) glacial advance 2 (current ice-sheet development). C/N and δ13C data suggest that deglacial environments favored the development of tundra and taiga ecosystems. These two successive glacial fluctuations observed at NEEM are consistent with those identified from the Camp Century core basal sediments over the last 3 Ma. Further inland, GRIP and GISP2 summit sites have remained glaciated more continuously than the western margin, with less intense ice-substratum interactions than those observed at NEEM.