Inorganic−organic hybrid perovskites MAPb(I
Understanding the formation chemistry of metal halide perovskites is key to optimizing processing conditions and realizing enhanced optoelectronic properties. Here, we reveal the structure of the crystalline precursor in the formation of methylammonium lead iodide (MAPbI3) from the single-step deposition of lead chloride and three equivalents of methylammonium iodide (PbCl2 + 3MAI) (MA = CH3NH3). The as-spun film consists of crystalline MA2PbI3Cl, which is composed of one-dimensional chains of lead halide octahedra, coexisting with disordered MACl. We show that the transformation of precursor into perovskite is not favored in the presence of MACl, and thus the gradual evaporation of MACl acts as a self-regulating mechanism to slow the conversion. We propose the stable precursor phase enables dense film coverage and the slow transformation may lead to improved crystal quality. This enhanced chemical understanding is paramount for the rational control of film deposition and the fabrication of superior optoelectronic devices.
more » « less- NSF-PAR ID:
- 10153696
- Publisher / Repository:
- Nature Publishing Group
- Date Published:
- Journal Name:
- Nature Communications
- Volume:
- 9
- Issue:
- 1
- ISSN:
- 2041-1723
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
x Br1−x )3(0 <x < 1) hold promise for efficient multi‐junction or tandem solar cells due to tunable bandgap and improved long‐term stability. However, the phase transformation from Pb(Ix Br1−x )2precursors to perovskites is not fully understood which hinders further improvement of optoelectronic properties and device performance. Here, adaptation of the two‐step deposition method, which enables the direct probe into the growth dynamics of perovskites using in situ diagnostics, and a detailed view of the effects of solvent, lead halide film solvation, and Br incorporation and alloying on the transformation behavior is presented. The in situ measurements indicate a strong tendency of lead halide solvation prior to crystallization during solution‐casting Pb(Ix Br1−x )2precursor from a dimethyl sulfoxide (DMSO) solvent. Highly‐efficient intramolecular exchange is observed between DMSO molecules and organic cations, leading to room‐temperature conversion of perovskite and high‐quality films with tunable bandgap and superior optoelectronic properties in contrast to that obtained from crystalline Pb(Ix Br1−x )2. The improved properties translate to easily tunable and a relatively higher power conversion efficiency of 16.42% based on the mixed‐halide perovskite MAPb(I0.9Br0.1)3. These findings highlight the benefits that solvation of the precursor phases, together with bromide incorporation, can have on the microstructure, morphology, and optoelectronic properties of these films. -
Abstract Recently, the evolved intermediate phase based on iodoplumbate anions that mediates perovskite crystallization has been embodied as the Lewis acid–base adduct formed by metal halides (serve as Lewis acid) and polar aprotic solvents (serve as Lewis base). Based on this principle, it is proposed to constitute efficient Lewis acid–base adduct in the SnI2deposition step to modulate its volume expansion and fast reaction with methylammonium iodide (MAI)/formamidinium iodide (FAI) (FAI is studied hereafter). Herein, trimethylamine (TMA) is employed as the additional Lewis base in the tin halide solution to form SnY2–TMA complexes (Y = I−, F−) in the first‐step deposition, followed by intercalating with FAI to convert into FASnI. It is shown that TMA can facilitate homogeneous film formation of a SnI2(+SnF2) layer by effectively forming intermediate SnY2–TMA complexes. Meanwhile, its relatively larger size and weaker affinity with SnI2than FA+ ions will facilitate the intramolecular exchange with FA+ ions, thereby enabling the formation of dense and compact FASnI3film with large crystalline domain (>1 µm). As a result, high power conversion efficiencies of 4.34% and 7.09% with decent stability are successfully accomplished in both conventional and inverted perovskite solar cells, respectively.
-
The organic metal halide perovskite material is capable of high throughput manufacturing via traditional deposition processes used in roll-to-roll, yet thermal annealing post deposition may require long ovens. We report rapid annealed perovskite thin films using intense pulsed light (IPL) to initiate a radiative thermal response that is enabled by an alkyl halide additive that collectively improves the performance of a device processed in an ambient environment from a baseline of 10 to 16.5% efficiency. Previous reports on CH 3 NH 3 PbI 3 perovskite films using IPL processing achieved functional devices in milli-second time scales and are promising for high throughput manufacturing processes under ambient conditions. In this study, we found that the addition of diiodomethane (CH 2 I 2 ) as an additive to the methylammonium iodide (MAI)/lead iodide (PbI 2 ) precursor ink chemistry and subsequent IPL thermal annealing are inter-dependent. The concentration of CH 2 I 2 and IPL processing parameters have a direct effect on the surface morphology of the films and performance within a perovskite solar cell (PSC). The CH 2 I 2 dissociates under exposure to ultraviolet (UV) radiation from the IPL source liberating iodine ions in the film, influencing the perovskite formation and reducing the defect states. We anticipate that these results can be utilized to further develop different ink formulations using alkyl halides for the IPL technique to improve the performance of perovskite solar cells processed in ambient conditions.more » « less
-
Abstract Composition and film quality of perovskite are crucial for the further improvement of perovskite solar cells (PSCs), including efficiency, reproducibility, and stability. Here, it is demonstrated that by simply mixing 50% of formamidinium (FA+) into methylammonium lead iodide (MAPbI3), a highly crystalline, stable phase, and compact, polycrystalline grain morphology perovskite is formed by using a solvent‐mediated phase transformation process via the synergism of dimethyl sulfoxide and diethyl ether, which shows long carrier lifetime, low trap state density, and a record certified 21.8% power conversion efficiency (PCE) in pure‐iodide, alkaline‐metal‐free MA0.5FA0.5PbI3perovskite‐based PSCs. These PSCs show very high operational stability, with 85% PCE retention upon 1000 h 1 Sun intensity illumination. A 17.33% PCE module (6.5 × 7 cm2) is also demonstrated, attesting to the scalability of such devices.
-
Abstract Composition engineering is a particularly simple and effective approach especially using mixed cations and halide anions to optimize the morphology, crystallinity, and light absorption of perovskite films. However, there are very few reports on the use of anion substitutions to develop uniform and highly crystalline perovskite films with large grain size and reduced defects. Here, the first report of employing tetrafluoroborate (BF4−) anion substitutions to improve the properties of (FA = formamidinium, MA = methylammonium (FAPbI3)0.83(MAPbBr3)0.17) perovskite films is demonstrated. The BF4−can be successfully incorporated into a mixed‐ion perovskite crystal frame, leading to lattice relaxation and a longer photoluminescence lifetime, higher recombination resistance, and 1–2 orders magnitude lower trap density in prepared perovskite films and derived solar cells. These advantages benefit the performance of perovskite solar cells (PVSCs), resulting in an improved power conversion efficiency (PCE) of 20.16% from 17.55% due to enhanced open‐circuit voltage (
V OC) and fill factor. This is the highest PCE for BF4−anion substituted lead halide PVSCs reported to date. This work provides insight for further exploration of anion substitutions in perovskites to enhance the performance of PVSCs and other optoelectronic devices.