The irradiation response of ZrC ceramics under 10 MeV Au3+ ion irradiation at 800 ºC

Florez, Raul; Crespillo, Miguel L.; He, Xiaoqing; White, Tommi A.; Hilmas, Gregory; Fahrenholtz, William; Graham, Joseph

doi:10.1016/j.jeurceramsoc.2020.01.025

Using a scanning electron microscope, we irradiate graphene drums with electrons at an energy of 20 keV and a dosage of about 1.58 × 1017 electrons/cm2. The drums consist of graphene exfoliated in ambient air over holes having a diameter of 4.6 μm and etched into an SiO2 substrate. After irradiation, we observe that the drum’s suspended monolayer (ML) region has a ratio of the Raman D peak height, ID, to the Raman G peak height, IG, as high as 6.3. In contrast, the supported ML on the SiO2 substrate has an ID/IG ratio of 0.49. Previous studies have shown that graphene drums containing air can leak in a vacuum at a low rate. We attribute the high ID/IG ratio of the suspended ML to the air that may be in the drums. We propose that the air produces much adsorbed water on the ML, resulting in a high average defect density during irradiation. We present Raman maps of the full-width-at-half maximum, position, and height of the G, 2D, D, and D’ peaks before and after irradiation and maps of ID/IG and ID/ID’. We anneal the drums at temperatures from 50 to 215 °C and find that ID/IG significantly reduces to 0.42. The annealing data are analyzed using an Arrhenius plot. We also find that ID/ID’ depends on annealing temperature and has values ≥8, in the range expected for sp3 defects, for ID/IG ≤ 3.9. This irradiation method may help achieve high average defect densities in ML graphene, imparting novel and potentially valuable properties.

More Like this