Two-Dimensional MXenes Mo 2 Ti 2 C 3 T z and Mo 2 TiC 2 T z : Microscopic Conductivity and Dynamics of Photoexcited Carriers

Li, Guangjiang; Natu, Varun; Shi, Teng; Barsoum, Michel W.; Titova, Lyubov V.

doi:10.1021/acsaem.9b01966

Titanium carbide/reduced graphene oxide (Ti 3 C 2 T z /rGO) gels were prepared by a one-step hydrothermal process. The gels show a highly porous structure with a surface area of ∼224 m 2 g −1 and average pore diameter of ∼3.6 nm. The content of GO and Ti 3 C 2 T z nanosheets in the reaction precursor was varied to yield different microstructures. The supercapacitor performance of Ti 3 C 2 T z /rGO gels varied significantly with composition. Specific capacitance initially increased with increasing Ti 3 C 2 T z content, but at high Ti 3 C 2 T z content gels cannot be formed. Also, the retention of capacitance decreased with increasing Ti 3 C 2 T z content. Ti 3 C 2 T z /rGO gel electrodes exhibit enhanced supercapacitor properties with high potential window (1.5 V) and large specific capacitance (920 F g −1 ) in comparison to pure rGO and Ti 3 C 2 T z . The synergistic effect of EDLC from rGO and redox capacitance from Ti 3 C 2 T z was the reason for the enhanced supercapacitor performance. A symmetric two-electrode supercapacitor cell was constructed with Ti 3 C 2 T z /rGO, which showed very high areal capacitance (158 mF cm −2 ), large energy density (∼31.5 μW h cm −2 corresponding to a power density of ∼370 μW cm −2 ), and long stability (∼93% retention) after 10 000 cycles.

More Like this