Bifunctional oxygen catalysts for oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) with high activities and low‐cost are of prime importance and challenging in the development of fuel cells and rechargeable metal–air batteries. This study reports a porous carbon nanomaterial loaded with cobalt nanoparticles (Co@NC‐
Efficient electrocatalysts are critical in various clean energy conversion and storage systems. Polyelemental nanomaterials are attractive as multifunctional catalysts due to their wide compositions and synergistic properties. However, controlled synthesis of polyelemental nanomaterials is difficult due to their complex composition. Herein, a one‐step synthetic strategy is presented to fabricate a hierarchical polyelemental nanomaterial, which contains ultrasmall precious metal nanoparticles (IrPt, ≈5 nm) anchored on spinel‐structure transition metal oxide nanoparticles. The polyelemental nanoparticles serve as excellent bifunctional catalysts for the oxygen evolution reaction (OER) and oxygen reduction reaction (ORR). The mass catalytic activity of the polyelemental nanoparticles is 7‐times higher than that of Pt in ORR and 28‐times that of Ir in OER at the same overpotentials, demonstrating the high activity of the bifunctional electrocatalyst. This outstanding performance is attributed to the controlled multiple elemental composition, mixed chemical states, and large electroactive surface area. The hierarchical nanostructure and polyelemental design of these nanoparticles offer a general and powerful alternative material for catalysis, solar cells, and more.
more » « less- Award ID(s):
- 1635221
- NSF-PAR ID:
- 10456297
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Energy Materials
- Volume:
- 10
- Issue:
- 25
- ISSN:
- 1614-6832
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract x /y ) derived from pyrolysis of a Co/Zn bimetallic zeolitic imidazolite framework, which exhibits incredibly high activity as bifunctional oxygen catalysts. For instance, the optimal catalyst of Co@NC‐3/1 has the interconnected framework structure between porous carbon and embedded carbon nanotubes, which shows the superb ORR activity with onset potential of ≈1.15 V and half‐wave potential of ≈0.93 V. Moreover, it presents high OER activity that can be further enhanced to over commercial RuO2by P‐doped with overpotentials of 1.57 V versus reversible hydrogen electrode at 10 mA cm−2and long‐term stability for 2000 circles and a Tafel slope of 85 mV dec−1. Significantly, the nanomaterial demonstrates better catalytic performance and durability than Pt/C for ORR and commercial RuO2and IrO2for OER. These findings suggest the importance of a synergistic effect of graphitic carbon, nanotubes, exposed Co–Nx active sites, and interconnected framework structure of various carbons for bifunctional oxygen electrocatalysts. -
more » « less
Abstract Developing high performance nonprecious metal‐based electrocatalysts has become a critical first step towards commercial applications of metal‐air batteries. Herein, nanocomposites based on Co/Co2P nanoparticles encapsulated within hierarchically porous N, P, S co‐doped carbon are prepared by controlled pyrolysis of zeolitic imidazolate frameworks (ZIF‐67) and poly(cyclotriphosphazene‐co‐4,4’‐sulfonyldiphenol) (PZS). The resulting Co/Co2P@NPSC nanocomposites exhibit apparent oxygen reduction reaction (ORR) and evolution reaction (OER) catalytic performance, and are used as the reversible oxygen catalyst for zinc‐air batteries (ZABs). Density functional theory (DFT) calculations exhibit that Co2P could provide active sites for the ORR and promote the conversion between the adsorbed intermediates, and porous N,P,S co‐doped carbon with Co2P nanoparticles also improves the exposure of actives sites and endows charge transport. Liquid‐state ZABs with Co/Co2P@NPSC as the cathode catalysts demonstrate the greater power density of 198.1 mW cm−2and a long cycling life of 50 h at 10 mA cm−2, likely due to the encapsulation of Co/Co2P nanoparticles by the carbon shell. Solid‐state ZABs also display a remarkable performance with a high peak power density of 74.3 mW cm−2. Therefore, this study indicates the meaning of the design and engineering of hierarchical porous carbon nanomaterial as electrocatalyst for rechargeable metal‐air batteries.
-
null (Ed.)Iron single atom catalysts have emerged as one of the most active electrocatalysts towards the oxygen reduction reaction (ORR), but the unsatisfactory durability and limited activity for the oxygen evolution reaction (OER) has hampered their commercial applications in rechargeable metal–air batteries. By contrast, cobalt-based catalysts are known to afford excellent ORR stability and OER activity, due to the weak Fenton reaction and low OER Gibbs free energy. Herein, a bimetal hydrogel template is used to prepare carbon aerogels containing Fe–Co bimetal sites (NCAG/Fe–Co) as bifunctional electrocatalysts towards both ORR and OER, with enhanced activity and stability, as compared to the monometal counterparts. High-resolution transmission electron microscopy, elemental mapping and X-ray photoelectron spectroscopy measurements demonstrate homogeneous distributions of the metal centers within defected carbon lattices by coordination to nitrogen dopants. X-ray absorption spectroscopic measurements, in combination with other results, suggest the formation of FeN 3 and CoN 3 moieties on mutually orthogonal planes with a direct Fe–Co bonding interaction. Electrochemical measurements show that NCAG/Fe–Co delivers a small ORR/OER potential gap of only 0.64 V at the current density of 10 mA cm −2 , 60 mV lower than that (0.70 V) with commercial Pt/C and RuO 2 catalysts. When applied in a flexible Zn–air battery, the dual-metal NCAG/Fe–Co catalyst also shows a remarkable performance, with a high open-circuit voltage of 1.47 V, a maximum power density of 117 mW cm −2 , as well as good rechargeability and flexibility. Results from this study may offer an ingenious protocol in the design and engineering of highly efficient and durable bifunctional electrocatalysts based on dual metal-doped carbons.more » « less
-
more » « less
Abstract It is essential but still challenging to design and construct inexpensive, highly active bifunctional oxygen electrocatalysts for the development of high power density zinc–air batteries (ZABs). Herein, a CoFe‐S@3D‐S‐NCNT electrocatalyst with a 3D hierarchical structure of carbon nanotubes growing on leaf‐like carbon microplates is designed and prepared through chemical vapour deposition pyrolysis of CoFe‐MOF and subsequent hydrothermal sulfurization. Its 3D hierarchical structure shows excellent hydrophobicity, which facilitates the diffusion of oxygen and thus accelerates the oxygen reduction reaction (ORR) kinetic process. Alloying and sulfurization strategies obviously enrich the catalytic species in the catalyst, including cobalt or cobalt ferroalloy sulfides, their heterojunction, core–shell structure, and S, N‐doped carbon, which simultaneously improve the ORR/OER catalytic activity with a small potential gap (Δ
E = 0.71 V). Benefiting from these characteristics, the corresponding liquid ZABs show high peak power density (223 mW cm−2), superior specific capacity (815 mA h gZn−1), and excellent stability at 5 mA cm−2for ≈900 h. The quasi‐solid‐state ZABs also exhibit a very high peak power density of 490 mW cm−2and an excellent voltage round‐trip efficiency of more than 64%. This work highlights that simultaneous composition optimization and microstructure design of catalysts can effectively improve the performance of ZABs. -
Employing the strong metal-support interaction (SMSI) effect for promoting the catalyst's activity toward the oxygen reduction reaction (ORR) is promising due to the electronic structure optimization and high utilization efficiency of platinum group metal (PGM) catalysts. Metal oxides as alternative supports for PGMs facilitate intrinsic activity and improve durability as compared to conventional carbon supports. However, the restricted mass and electron transfer at the metal/support interface need to be addressed. Herein, to strengthen the interaction at the metal/support interfaces and improve the utilization efficiency of PGM, an ultralow loading of Pd was embedded in a surface-oxygenated PdNiMnO porous film. The Mn-doping was designed to promote surface oxygenation using a facile anodization process that created sufficiently exposed interfaces between Pd and the support, strengthening the SMSI effects at the Pd/oxygenated support interface for enhancing ORR performance. Furthermore, the Ni-containing oxygenated catalyst served as both the active component for the oxygen evolution reaction (OER) and the functional support for stabilizing Pd, making PdNiMnO a bifunctional catalyst for zinc–air flow batteries (ZAFB). As a proof-of-concept, the ZAFB (PdNiMnO) shows a maximal power density of 211.6 mW cm −2 and outstanding cycling stability for over 2000 h with a minimal voltage gap of 0.69 V at a current density of 10 mA cm −2 , superior to the state-of-the-art catalysts.more » « less