Resonant tunneling diodes (RTDs) have come full-circle in the past 10 years after their demonstration in the early 1990s
as the fastest room-temperature semiconductor oscillator, displaying experimental results up to 712 GHz and fmax values
exceeding 1.0 THz [1]. Now the RTD is once again the preeminent electronic oscillator above 1.0 THz and is being
implemented as a coherent source [2] and a self-oscillating mixer [3], amongst other applications. This paper concerns
RTD electroluminescence – an effect that has been studied very little in the past 30+ years of RTD development, and not
at room temperature. We present experiments and modeling of an n-type In0.53Ga0.47As/AlAs double-barrier RTD
operating as a cross-gap light emitter at ~300K. The MBE-growth stack is shown in Fig. 1(a). A 15-μm-diam-mesa
device was defined by standard planar processing including a top annular ohmic contact with a 5-μm-diam pinhole in the
center to couple out enough of the internal emission for accurate free-space power measurements [4]. The emission spectra
have the behavior displayed in Fig. 1(b), parameterized by bias voltage (VB). The long wavelength emission edge is at
= 1684 nm - close to the In0.53Ga0.47As bandgap energy of Ug ≈ 0.75 eV at 300 K. The spectral peaks for VB = 2.8 and
3.0 V both occur around = 1550 nm (h = 0.75 eV), so blue-shifted relative to the peak of the “ideal”, bulk InGaAs
emission spectrum shown in Fig. 1(b) [5]. These results are consistent with the model displayed in Fig. 1(c), whereby
the broad emission peak is attributed to the radiative recombination between electrons accumulated on the emitter side,
and holes generated on the emitter side by interband tunneling with current density Jinter. The blue-shifted main peak is
attributed to the quantum-size effect on the emitter side, which creates a radiative recombination rate RN,2 comparable to
the band-edge cross-gap rate RN,1. Further support for this model is provided by the shorter wavelength and weaker
emission peak shown in Fig. 1(b) around = 1148 nm. Our quantum mechanical calculations attribute this to radiative
recombination RR,3 in the RTD quantum well between the electron ground-state level E1,e, and the hole level E1,h.
To further test the model and estimate quantum efficiencies, we conducted optical power measurements using a
large-area Ge photodiode located ≈3 mm away from the RTD pinhole, and having spectral response between 800 and
1800 nm with a peak responsivity of ≈0.85 A/W at =1550 nm. Simultaneous I-V and L-V plots were obtained and
are plotted in Fig. 2(a) with positive bias on the top contact (emitter on the bottom). The I-V curve displays a pronounced
NDR region having a current peak-to-valley current ratio of 10.7 (typical for In0.53Ga0.47As RTDs). The external quantum
efficiency (EQE) was calculated from EQE = e∙IP/(∙IE∙h) where IP is the photodiode dc current and IE the RTD current.
The plot of EQE is shown in Fig. 2(b) where we see a very rapid rise with VB, but a maximum value (at VB= 3.0 V) of
only ≈2×10-5. To extract the internal quantum efficiency (IQE), we use the expression EQE= c ∙i ∙r ≡ c∙IQE where
ci, and r are the optical-coupling, electrical-injection, and radiative recombination efficiencies, respectively [6]. Our
separate optical calculations yield c≈3.4×10-4 (limited primarily by the small pinhole) from which we obtain the curve
of IQE plotted in Fig. 2(b) (right-hand scale). The maximum value of IQE (again at VB = 3.0 V) is 6.0%. From the implicit
definition of IQE in terms of i and r given above, and the fact that the recombination efficiency in In0.53Ga0.47As is
likely limited by Auger scattering, this result for IQE suggests that i might be significantly high.
To estimate i, we have used the experimental total current of Fig. 2(a), the Kane two-band model of interband
tunneling [7] computed in conjunction with a solution to Poisson’s equation across the entire structure, and a rate-equation
model of Auger recombination on the emitter side [6] assuming a free-electron density of 2×1018 cm3. We focus on the
high-bias regime above VB = 2.5 V of Fig. 2(a) where most of the interband tunneling should occur in the depletion region
on the collector side [Jinter,2 in Fig. 1(c)]. And because of the high-quality of the InGaAs/AlAs heterostructure (very few
traps or deep levels), most of the holes should reach the emitter side by some combination of drift, diffusion, and tunneling
through the valence-band double barriers (Type-I offset) between InGaAs and AlAs. The computed interband current
density Jinter is shown in Fig. 3(a) along with the total current density Jtot. At the maximum Jinter (at VB=3.0 V) of 7.4×102
A/cm2, we get i = Jinter/Jtot = 0.18, which is surprisingly high considering there is no p-type doping in the device. When
combined with the Auger-limited r of 0.41 and c ≈ 3.4×10-4, we find a model value of IQE = 7.4% in good agreement
with experiment. This leads to the model values for EQE plotted in Fig. 2(b) - also in good agreement with experiment.
Finally, we address the high Jinter and consider a possible universal nature of the light-emission mechanism. Fig.
3(b) shows the tunneling probability T according to the Kane two-band model in the three materials, In0.53Ga0.47As, GaAs,
and GaN, following our observation of a similar electroluminescence mechanism in GaN/AlN RTDs (due to strong
polarization field of wurtzite structures) [8]. The expression is Tinter = (2/9)∙exp[(-2 ∙Ug
2 ∙me)/(2h∙P∙E)], where Ug is the
bandgap energy, P is the valence-to-conduction-band momentum matrix element, and E is the electric field. Values for
the highest calculated internal E fields for the InGaAs and GaN are also shown, indicating that Tinter in those structures
approaches values of ~10-5. As shown, a GaAs RTD would require an internal field of ~6×105 V/cm, which is rarely
realized in standard GaAs RTDs, perhaps explaining why there have been few if any reports of room-temperature
electroluminescence in the GaAs devices.
[1] E.R. Brown,et al., Appl. Phys. Lett., vol. 58, 2291, 1991. [5] S. Sze, Physics of Semiconductor Devices, 2nd Ed. 12.2.1 (Wiley, 1981).
[2] M. Feiginov et al., Appl. Phys. Lett., 99, 233506, 2011. [6] L. Coldren, Diode Lasers and Photonic Integrated Circuits, (Wiley, 1995).
[3] Y. Nishida et al., Nature Sci. Reports, 9, 18125, 2019. [7] E.O. Kane, J. of Appl. Phy 32, 83 (1961).
[4] P. Fakhimi, et al., 2019 DRC Conference Digest. [8] T. Growden, et al., Nature Light: Science & Applications 7, 17150 (2018).
[5] S. Sze, Physics of Semiconductor Devices, 2nd Ed. 12.2.1 (Wiley, 1981).
[6] L. Coldren, Diode Lasers and Photonic Integrated Circuits, (Wiley, 1995).
[7] E.O. Kane, J. of Appl. Phy 32, 83 (1961).
[8] T. Growden, et al., Nature Light: Science & Applications 7, 17150 (2018).
more »
« less
Photoluminescence characterization of wetting layer and carrier dynamics for coupled InGaAs/GaAs surface quantum dot pair structures
The optical properties are investigated by spectroscopic characterizations for bilayer InGaAs/GaAs quantum dot (QD) structures consisting of a layer of surface quantum dots (SQDs) separated from a layer of buried quantum dots (BQDs) by different GaAs spacers with thicknesses of 7 nm, 10.5 nm and 70 nm. The coupling from the BQDs to SQDs leads to carrier transfer for the two samples with thin spacers, 7 nm and 10.5 nm, in which QD pairs are obtained while not for the 70 nm spacer sample. The carrier tunneling time is measured to be 0.145 ns and 0.275 ns from BQDs to SQD through the 7 nm and 10.5 nm spacers, respectively. A weak emission band can be observed at the wavelength of ∼ 960 nm, while the excitation intensity dependent PL and PLE spectra show that this is from the wetting layer (WL) of the SQDs. This WL is very important for carrier dynamics in bilayer structures of BQDs and SQDs, including for carrier generation, capture, relaxation, tunneling, and recombination. These results provide useful information for understanding the optical properties of InGaAs SQDs and for using such hybrid structures as building blocks for surface sensing devices.
more » « less- NSF-PAR ID:
- 10166128
- Publisher / Repository:
- Optical Society of America
- Date Published:
- Journal Name:
- Optics Express
- Volume:
- 28
- Issue:
- 14
- ISSN:
- 1094-4087; OPEXFF
- Page Range / eLocation ID:
- Article No. 20704
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
more » « less
Abstract Driven by tensile strain, GaAs quantum dots (QDs) self-assemble on In0.52Al0.48As(111)A surfaces lattice-matched to InP substrates. In this study, we show that the tensile-strained self-assembly process for these GaAs(111)A QDs unexpectedly deviates from the well-known Stranski-Krastanov (SK) growth mode. Traditionally, QDs formed via the SK growth mode form on top of a flat wetting layer (WL) whose thickness is fixed. The inability to tune WL thickness has inhibited researchers’ attempts to fully control QD-WL interactions in these hybrid 0D-2D quantum systems. In contrast, using microscopy, spectroscopy, and computational modeling, we demonstrate that for GaAs(111)A QDs, we can continually increase WL thickness with increasing GaAs deposition, even after the tensile-strained QDs (TSQDs) have begun to form. This anomalous SK behavior enables simultaneous tuning of both TSQD size and WL thickness. No such departure from the canonical SK growth regime has been reported previously. As such, we can now modify QD-WL interactions, with future benefits that include more precise control of TSQD band structure for infrared optoelectronics and quantum optics applications.
-
null (Ed.)InAs quantum dots (QDs) embedded into a waveguiding GaAs semiconductor matrix may produce scintillation detectors with exceptional speed and yield, making them valuable for nuclear security, medical imaging, and high energy physics applications. In this work, we developed thick (~25um) epitaxial heterostructres with high luminescence efficiency composed of self-assembled nano-engineered InAs QDs grown by molecular beam epitaxy. The bulk GaAs acts as a stopping material for incident particles and as a waveguide when layer-transferred onto a low-index substrate. Waveguiding and self-absorption (<1cm-1) were studied using photoluminescence with scanning laser excitation and modeled with ray optics approximation and geometrical coupling of high-index waveguide to a collection fiber. Scintillating signals from alpha-particles were analyzed with an external photodiode (PD) and an integrated PD which provided an improved optical coupling. The mean charge collected by the integrated PD corresponded to 5×1e4 photoelectrons per 1 MeV of deposited energy, or ~20% of the theoretically achievable light yield. Combined with the previously measured QD scintillation time of 0.3-0.6 ns, this makes the InAs/GaAs QD heterostructures the fastest high yield scintillation material reported.more » « less
-
more » « less
Abstract Deterministic positioning single site-controlled high symmetric InGaAs quantum dots (QDs) in (111)B-oriented GaAs photonic crystal cavities with nanometer-scale accuracy provides an idea component for building integrated quantum photonic circuits. However, it has been a long-standing challenge of improving cavity
Q -factors in such systems. Here, by optimizing the trade-off between the cavity loss and QD spectral quality, we demonstrate our site-controlled QD-nanocavity system operating in the intermediate coupling regime mediated by phonon scattering, with the dynamic coexistence of strong and weak coupling. The cavity-exciton detuning-dependent micro-photoluminescence spectrum reveals concurrence of a trend of exciton-polariton mode avoided crossing, as a signature of Rabi doublet of the strongly coupled system. Meanwhile, a trend of keeping constant or slight blue shift of coupled exciton–cavity mode(CM) energy across zero-detuning is ascribed to the formation of collective states mediated by phonon-assisted coupling, and their rare partial out-of-synchronization linewidth-narrowing is linked to their coexisting strong-weak coupling regime. We further reveal the pump power-dependent anti-bunching photon statistical dynamics of this coexisting strong-weak coupled system and the optical features of strongly confined exciton-polaritons, and dark-exciton-like states. These observations demonstrate the potential capabilities of site-controlled QD-cavity systems as deterministic quantum nodes for on-chip quantum information processing and provide guidelines for future device optimization for achieving the strong coupling regime. -
more » « less
Abstract A simple room‐temperature process of depositing MXene on a III‐V structure with embedded 2D electron gas (2DEG) is used, which results in a large area, , photodetector (PD) device that greatly outperforms vacuum deposited Ti/Au metal‐semiconductor‐metal (MSM) PD's. By co‐optimizing properties of 2D MXene contacts and the III‐V material heterojunctions, this device sets new operating records with responsivity up to 1.04 A W‐1at low optical powers, corresponding to >230% internal quantum efficiency, dark current of 50 , >105.6‐dB dynamic range, and 25–150 ps response time, which improves the previous MXene‐Semiconductor‐MXene responsivity by >2.7 times and is 7 × 103–−106times faster compared to other MXene‐based PDs. This is achieved by enhancing the Schottky barrier height by forming a Van der Waals (vdW) heterojunction between a wide bandgap AlGaAs surface layer and spin coated
Ti 3C 2T z electrodes. A layered architecture transports the optically generated electrons to a 2DEG channel at the GaAs/AlGaAs heterointerface, where they are rapidly collected. The landscaped electric field pushes the slow holes to an underlying low temperature‐grown GaAs (LT‐GaAs) region where they recombine. The proposed Schottky‐2DEG Photoconductor‐Schottky model for device operation shows how this device circumvents the canonical limitations of gain‐bandwidth product, and carrier transit time, while replacing the need for vacuum deposition of gold or other precious metals.