The direct-growth technique was used to synthesize several macromonomers (MMs) employing reversible addition–fragmentation chain transfer (RAFT) polymerization by growing directly from a norbornene-functionalized chain transfer agent (CTA). We aimed to investigate the formation of bisnorbornenyl species resulting from radical termination by combination ( i.e. , coupling) during RAFT polymerization at different monomer conversion values in four types of monomers: styrene, tert -butyl acrylate, methyl methacrylate and N -acryloyl morpholine. Ring-opening metathesis polymerization (ROMP) of these MMs using Grubbs' 3rd generation catalyst (G3) at an MM : G3 ratio of 100 : 1 resulted in the formation of bottlebrush polymers. Analysis by size-exclusion chromatography (SEC) revealed high molar mass shoulders of varying intensities attributed to the incorporation of these bisnorbornenyl species to generate dimeric or higher-order bottlebrush polymer oligomers. The monomer type in the RAFT step heavily influenced the amount of these bottlebrush polymer dimers and oligomers, as did the monomer conversion value in the RAFT step: We found that the ROMP of polystyrene MMs with a target backbone degree of polymerization of 100 produced detectable coupling at ≥20% monomer conversion in the RAFT step, while it took ≥80% monomer conversion to observe coupling in the poly( tert -butyl acrylate) MMs. We did not detect coupling in the poly(methyl methacrylate) MMs, but broadening of the SEC peaks and an increase in dispersity occurred, suggesting the presence of metathesis-active alkene-containing chain ends created by disproportionation. Finally, poly( N -acryloyl morpholine) MMs, even when reaching 90% monomer conversion in the RAFT step, showed no detectable coupling in the bottlebrush polymers. These results highlight the importance of monomer choice and RAFT polymerization conditions in making MMs for ROMP grafting-through to make well-defined bottlebrush polymers.
more »
« less
Computer Simulation of Surface‐Initiated Controlled Radical Polymerization: Effect of Free‐Monomer Model on Brush Properties
Monte Carlo simulation is employed using the bond‐fluctuation model (BFM) to explore the role of free‐monomer model on surface‐initiated controlled polymerization from flat substrates. Three free‐monomer models differ in two aspects: 1) their extent of excluded volume interactions between free‐monomer/polymer segments and 2) monomer availability (finite or infinite) during the simulation. In the explicit monomer (EM) model, free‐monomers behave as a single BFM‑type units. In the phantom monomer (PM) model, free‐monomers act analogously to those in the EM model but lack excluded volume interactions with the growing polymers. In the implicit monomer (IM) model, no explicit monomers are included in the simulation box; the polymers can grow as long as space is available near active chain‐ends. It is found that the breadth of the molecular weight distribution of the grown polymers decreases from EM, to PM, to IM models. With the EM model, free‐monomers are excluded from the near‐surface region, while with the PM model they are not. Due to its excluded volume interactions, the EM model tends to compress the brush against the substrate. Finally, the relaxation of the shape of a polydisperse brush after the polymerization reaction ends has been reported.
more » « less- Award ID(s):
- 1725938
- NSF-PAR ID:
- 10460230
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Macromolecular Theory and Simulations
- Volume:
- 28
- Issue:
- 5
- ISSN:
- 1022-1344
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
more » « less
Abstract Polymer brush patterns have a central role in established and emerging research disciplines, from microarrays and smart surfaces to tissue engineering. The properties of these patterned surfaces are dependent on monomer composition, polymer height, and brush distribution across the surface. No current lithographic method, however, is capable of adjusting each of these variables independently and with micrometer-scale resolution. Here we report a technique termed Polymer Brush Hypersurface Photolithography, which produces polymeric pixels by combining a digital micromirror device (DMD), an air-free reaction chamber, and microfluidics to independently control monomer composition and polymer height of each pixel. The printer capabilities are demonstrated by preparing patterns from combinatorial polymer and block copolymer brushes. Images from polymeric pixels are created using the light reflected from a DMD to photochemically initiate atom-transfer radical polymerization from initiators immobilized on Si/SiO2wafers. Patterning is combined with high-throughput analysis of grafted-from polymerization kinetics, accelerating reaction discovery, and optimization of polymer coatings.
-
Despite adhesives having their origins in natural materials, most glues are formed from petroleum-based products. However, many natural adhesives lack the strength to compete with synthetic glues. Therefore, strong, sustainable alternatives are needed. Data presented here build on prior work that combines elemental sulfur, a petroleum byproduct, and garlic essential oil (GEO) which is composed of allyl sulfides, to make adhesives. Here, we have demonstrated that both sulfur and GEO can initiate polymerization at 160 °C with another petroleum byproduct, dicyclopentadiene, and a variety of natural monomers through the formation of sulfur radicals. In addition to using natural monomers and petroleum byproducts, these processes are solvent free and have high atom economy, limiting waste formation, and meeting many principles of green chemistry. Much of this work has focused on determining the effect of each sulfur source on polymerization and adhesion. A family of polymers were created with varied S : GEO : monomer ratios and characterized to determine differences in their chemical and materials properties. Despite similarities in the reaction mechanism, sulfur tends to polymerize more rapidly and create materials that are more ductile and more easily reprocessed. GEO is slower to react causing more polymerization to take place on the adherend surface yielding a more brittle polymer with higher maximum adhesion strength but lower work of adhesion. Both polymers exhibited effective adhesive recyclability. Overall, a combination of natural oils and petroleum byproducts were combined to make inexpensive, sustainable, recyclable adhesives.more » « less
-
more » « less
ABSTRACT An open‐to‐air method for the efficient synthesis of surface‐tethered polymer brushes based on photoinduced electron transfer‐reversible addition‐fragmentation chain transfer (PET‐RAFT) polymerization is reported. Key to this approach is an enzyme‐assisted strategy using glucose oxidase to facilitate the
in situ removal of oxygen during the polymerization process. Control experiments in the absence of glucose oxidase confirm the importance of enzymatic deoxygenation for successful polymerization of a variety of acrylamide, methacrylate, and acrylate monomers. In accordance with controlled polymerization kinetics, a linear increase in brush height as a function of irradiation time for a range of light intensities is demonstrated. Importantly, the use of light to mediate growth and the inherent monomer versatility of PET‐RAFT allow for the facile fabrication of well‐defined polymer brushes under aqueous conditions. © 2019 Wiley Periodicals, Inc. J. Polym. Sci.2020 ,58 , 70–76 -
null (Ed.)We report poly(isocyanide)-based random copolymers (co-PIC) featuring alkoxycarbonyl-based side-chains synthesized via the metal-catalyzed controlled polymerization of chiral and achiral isocyanide monomers. The pyridine-functionalized achiral monomer provides functional sites while the chiral monomer drives the formation of a one-handed preferred helix. The side-chain functionalized helical polymer undergoes self-assembly with palladated pincer ligands, as evidenced by 1H NMR and UV-Vis spectroscopies. Circular dichroism (CD) spectroscopy confirms that the side-chain self-assembly does not affect the backbone helicity. We construct supramolecular helical brush copolymers via the metal coordination of the co-PIC backbone with telechelic poly(styrene)s. 1H NMR and UV-Vis spectroscopies confirm the metal coordination, and CD measurements suggest that the backbone retains its helical conformation. Additionally, viscometry measurements verify the formation of high molecular weight polymers while dynamic light scattering confirms the increasing hydrodynamic radii of the resulting supramolecular brush copolymers. Our methodology constructs complex 3D materials with fully synthetic, secondary structure containing building blocks. We view this as a platform for building architecturally controlled 3D supramolecular materials with high degrees of complexity.more » « less