Amorphous/crystalline high-entropy-alloy (HEA) composites show great promise as structural materials due to their exceptional mechanical properties. However, there is still a lack of understanding of the dynamic nanoindentation response of HEA composites at the atomic scale. Here, the mechanical behavior of amorphous/crystalline HEA composites under nanoindentation is investigated through a large-scale molecular dynamics simulation and a dislocation-based strength model, in terms of the indentation force, microstructural evolution, stress distribution, shear strain distribution, and surface topography. The results show that the uneven distribution of elements within the crystal leads to a strong heterogeneity of the surface tension during elastic deformation. The severe mismatch of the amorphous/crystalline interface combined with the rapid accumulation of elastic deformation energy causes a significant number of dislocation-based plastic deformation behaviors. The presence of surrounding dislocations inhibits the free slip of dislocations below the indenter, while the amorphous layer prevents the movement or disappearance of dislocations towards the substrate. A thin amorphous layer leads to great indentation force, and causes inconsistent stacking and movement patterns of surface atoms, resulting in local bulges and depressions at the macroscopic level. The increasing thickness of the amorphous layer hinders the extension of shear bands towards the lower part of the substrate. These findings shed light on the mechanical properties of amorphous/crystalline HEA composites and offer insights for the design of high-performance materials.
more »
« less
A continuum dislocation-based model of wedge microindentation of single crystals
Recent Electron Backscatter Diffraction (EBSD) experiments have revealed the emergence of heterogeneous dislocation microstructures forming under a wedge indenter in fcc crystals, where micro-meter dislocation patterns challenge the predictions of traditional models of plasticity. In order to explain the formation of these features and develop a relationship between the forcedisplacement curve and the dislocation substructure, we present here a model of wedge indentation based on the continuum theory of dislocations. The model accounts for large deformation kinematics through the multiplicative split of the deformation gradient tensor, where the incompatible plastic component of deformation results from the flux of dislocations on different and interacting slips systems. Constitutive equations for dislocation fluxes are determined from a dissipative variational principle. As a result, each dislocation density satisfies an initialboundary value problem with convective-diffusive character, which is coupled to the macroscopic stress and displacement fields governing the deformation process. Solution to the selfconsistent continuum formulation is found using the finite element method. Computer simulations mimic the experimental conditions of wedge micro-indentation experiments into Ni singlecrystals used by Kysar et al. (2010a). A comparison of overall dislocation density distribution and macroscopic mechanical response shows good overall agreement with the experimental results in terms of the detailed features of dislocation patterns and lattice rotations as well as the macroscopic force-displacement response.
more »
« less
- Award ID(s):
- 1727740
- PAR ID:
- 10190971
- Date Published:
- Journal Name:
- International journal of plasticity
- ISSN:
- 0749-6419
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
In powder metallurgy (PM), the compaction step is fundamental to determining the final properties of the sintered components. The deformation and defectiveness introduced in the powder material during uniaxial die compaction can be correlated to the activation and enhancement of the dislocation pipe diffusion, a lattice diffusion mechanism during the sintering process. Its coefficient depends on the dislocation density. The powder particles are mostly deformed along the direction of the compaction (longitudinal direction) rather than along the compaction plane; consequently, the contact areas perpendicular to the direction of the compaction present a higher density of dislocations and lattice defects. This high density intensifies the shrinkage along the direction of compaction. To demonstrate the influence of uniaxial cold compaction on the material’s stress state the powder particles and their contacts were modeled using spheres made of pure copper. These spheres are compacted in a die at different pressures to better analyze the system’s response at the grade of deformation and the consequent influence on the material’s behavior during the sintering. In the different zones of the sphere, the micro-hardness was measured and correlated to the concentration of dislocations using the model for indentation size effect (ISE). After the compaction, the spheres were more deformed along the longitudinal than the transversal direction. The results obtained using hardness indentation show differences in the dislocation density between the undeformed and deformed spheres and, in the case of the compacted sphere, between the contact area along the longitudinal and the transversal direction.more » « less
-
Creep is a serious concern reducing the efficiency and service life of components in various structural applications. Multi-principal element alloys are attractive as a new generation of structural materials due to their desirable elevated temperature mechanical properties. Here, time-dependent plastic deformation behavior of two multi-principal element alloys, CoCrNi and CoCrFeMnNi, was investigated using nano-indentation technique over the temperature range of 298 K to 573 K under static and dynamic loads with applied load up to 1000 mN. The stress exponent was determined to be in the range of 15 to 135 indicating dislocation creep as the dominant mechanism. The activation volume was ~25b3 for both CoCrNi and CoCrFeMnNi alloys, which is in the range indicating dislocation glide. The stress exponent increased with increasing indentation depth due to higher density and entanglement of dislocations, and decreased with increasing temperature owing to thermally activated dislocations. The results for the two multi-principal element alloys were compared with pure Ni. CoCrNi showed the smallest creep displacement and the highest activation energy among the three systems studied indicating its superior creep resistance.more » « less
-
For the past century, dislocations have been understood to be the carriers of plastic deformation in crystalline solids. However, their collective behavior is still poorly understood. Progress in understanding the collective behavior of dislocations has primarily come in one of two modes: the simulation of systems of interacting discrete dislocations and the treatment of density measures of varying complexity that are considered as continuum fields. A summary of contemporary models of continuum dislocation dynamics is presented. These include, in order of complexity, the two-dimensional statistical theory of dislocations, the field dislocation mechanics treating the total Kröner–Nye tensor, vector density approaches that treat geometrically necessary dislocations on each slip system of a crystal, and high-order theories that examine the effect of dislocation curvature and distribution over orientation. Each of theories contain common themes, including statistical closure of the kinetic dislocation transport equations and treatment of dislocation reactions such as junction formation. An emphasis is placed on how these common themes rely on closure relations obtained by analysis of discrete dislocation dynamics experiments. The outlook of these various continuum theories of dislocation motion is then discussed.more » « less
-
The equations of dislocation transport at finite crystal deformation were developed, with a special emphasis on a vector density representation of dislocations. A companion thermodynamic analysis yielded a generalized expression for the driving force of dislocations that depend on Mandel (Cauchy) stress in the reference (spatial) configurations and the contribution of the dislocation core energy to the free energy of the crystal. Our formulation relied on several dislocation density tensor measures linked to the incompatibility of the plastic distortion in the crystal. While previous works develop such tensors starting from the multiplicative decomposition of the deformation gradient, we developed the tensor measures of the dislocation density and the dislocation flux from the additive decomposition of the displacement gradient and the crystal velocity fields. The two-point dislocation density measures defined by the referential curl of the plastic distortion and the spatial curl of the inverse elastic distortion and the associate dislocation currents were found to be more useful in deriving the referential and spatial forms of the transport equations for the vector density of dislocations. A few test problems showing the effect of finite deformation on the static dislocation fields are presented, with a particular attention to lattice rotation. The framework developed provides the theoretical basis for investigating crystal plasticity and dislocation patterning at the mesoscale, and it bears the potential for realistic comparison with experiments upon numerical solution.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript
- Journal Article:
- https://doi.org/10.1016/j.ijplas.2018.10.008