Changing the surface properties (i.e., roughness or friction) can be instrumental for many applications but can be a complex and resource-intensive process. In this paper, we demonstrate a novel process of controlling the friction of a continuous rod by delivering inorganic microparticles. A standardized continuous particle transfer protocol has been developed in our laboratory for depositing particles from a liquid carrier system (LCS) to the cylindrical rod substrate. The particle transfer process can produce controllable and tunable surface properties. Polymeric binder is used to deliver the particles as asperities over the rod substrate and by controlling their size, shape, and distribution, the coefficient of friction of the rod is determined. Tabletop experiments are designed and performed to measure the friction coefficient following the Capstan equation. The entrained particles on the substrate will create size- and shape-based asperities, which will alter the surface morphology toward the desired direction. Both oblique and direct quantitative measurements are performed at different particles and binder concentrations. A systematic variation in the friction coefficient is observed and reported in the result section. It is observed from the capstan experiment that adding only 1% irregular shaped particles in the suspension changes the friction coefficient of the rods by almost 115%. The proposed friction control technique is a simple scale-up, low-cost, low-waste, and low-energy manufacturing method for controlling the surface morphology.
In this paper, a new possibility of fabricating a metal lattice structure with a continuous rod is demonstrated. A multi-layer, periodic, and aperiodic lattice structure can be manufactured with a continuous thin rod by bending it with a repetitive pattern. However, joining their nodes are challenging and an important problem to solve. This paper is investigating the joining of nodes in a loose lattice structure by delivering materials through the dipping process. Both liquid state (epoxy) and solid-state (inorganic particles) joining agents are considered for polymer–metal and metal–metal bonding, respectively. Liquid Carrier Systems (LCS) are designed considering their rheological behavior. We found 40% solid loading with the liquid carrier system provides sufficient solid particles transfer at dipping and join the lattice node using transient liquid phase bonding (TLP). 3D metal lattice structures are constructed, and their mechanical properties are investigated. The lattice structure shows comparable strength even with smaller relative density (< 10%). The strength and elastic modulus of all the fabricated samples decreases with the increase in cell size, which is consistent with the traditional wisdom.
more » « less- NSF-PAR ID:
- 10209429
- Publisher / Repository:
- Nature Publishing Group
- Date Published:
- Journal Name:
- Scientific Reports
- Volume:
- 11
- Issue:
- 1
- ISSN:
- 2045-2322
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract In manufacturing industries, spherical micro-particles are commonly used as (e.g., brazing powder, metal filler, and 3D printing powder) which are produced with droplet-based particle fabrication techniques. Such processes create spherical morphology but introduce polydispersity and follow a continuous exponential pattern commonly expressed with Rosin-Rammler expression. Sorting those micro-particles in a narrower size range is an important but difficult, costly, and challenging process. Here we demonstrate the successful separation of the particles from a poly-disperse mixture with a particle volume fraction of 10% by dipping process. Nickel-based micro-particles (avg. dia. 5.69 μm) are added in a binder-based liquid carrier system. To encounter the gravitational force, external kinetic energy in the form of agitation is applied to ensure the uniform dispersion of the particles. The cylindrical substrate is prepared and dipped in the ‘pseudo suspension’ to separate the particles by adhering to it. The substrate is dried, and images are taken to characterize the separated particles using image J software. A clear size distribution can be observed which is also plotted. Additionally, a relationship between the process parameter and sorted particles has been established. The proposed method is quick, controllable, and easy to implement, which can be a useful tool for sorting wide-range poly-disperse particles.
-
more » « less
Abstract This work discusses the attributes, fabrication methods, and applications of gallium‐based liquid metal particles. Gallium‐based liquid metals combine metallic and fluidic properties at room temperature. Unlike mercury, which is toxic and has a finite vapor pressure, gallium possesses low toxicity and effectively zero vapor pressure at room temperature, which makes it amenable to many applications. A variety of fabrication methods produce liquid metal particles with variable sizes, ranging from nm to mm (which is the upper limit set by the capillary length). The liquid nature of gallium enables fabrication methods—such as microfluidics and sonication—that are not possible with solid materials. Gallium‐based liquid metal particles possess several notable attributes, including a metal–metal oxide (liquid–solid) core–shell structure as well as the ability to self‐heal, merge, and change shape. They also have unusual phase behavior that depends on the size of the particles. The particles have no known commercial applications, but they show promise for drug delivery, soft electronics, microfluidics, catalysis, batteries, energy harvesting, and composites. Existing challenges and future opportunities are discussed herein.
-
A severe plastic deformation process, termed accumulative extrusion bonding (AEB), is conceived to steady-state bond metals in the form of multilayered tubes. It is shown that AEB can facilitate bonding of metals in their solid-state, like the process of accumulative roll bonding (ARB). The AEB steps involve iterative extrusion, cutting, expanding, restacking, and annealing. As the process is iterated, the laminated structure layer thicknesses decrease within the tube wall, while the tube wall thickness and outer diameter remain constant. Multilayered bimetallic tubes with approximately 2 mm wall thickness and 25.25 mm outer diameter of copper-aluminum are produced at 52% radial strain per extrusion pass to contain eight layers. Furthermore, tubes of copper-copper are produced at 52% and 68% strain to contain two layers. The amount of bonding at the metal-to-metal interfaces and grain structure are measured using optical microscopy. After detailed examination, only the copper-copper bimetal deformed to 68% strain is found bonded. The yield strength of the copper-copper tube extruded at 68% improves from 83 MPa to 481 MPa; a 480% increase. Surface preparation, as described by the thin film theory, and the amount of deformation imposed per extrusion pass are identified and discussed as key contributors to enact successful metal-to-metal bonding at the interface. Unlike in ARB, bonding in AEB does not occur at ~50% strain revealing the significant role of more complex geometry of tubes relative to sheets in solid-state bonding.more » « less
-
more » « less
Abstract Multiphase mixtures containing both liquid metal and solid inclusions in a soft polymeric matrix can exhibit unique combinations of mechanical, electrical, magnetic, and thermal properties. Gallium‐based liquid metals have excellent electrical and thermal properties, and incorporating additional conductive, magnetic, or other solid fillers into liquid metal‐embedded elastomers can yield heightened electrical and thermal conductivities, enhanced elasticity due to lowered percolation thresholds, and positive piezoconductivity. This emerging class of liquid metal + x composites, where x denotes any solid filler type, has applications in stretchable electronics, wearables, soft robotics, and energy harvesting and storage. In this review, the recent literature is consolidated on liquid metal + x composites and their potential to offer uniquely amplified or multiplied bulk properties is highlighted. The literature related to the materials and processing of liquid metal + x composites is reviewed, through which it is found that the properties of the resulting multiphase composites are sensitive to the sequence in which the distinct liquid metal and solid inclusions are incorporated into the continuous phase. This review further includes a summary of relevant predictive modeling approaches, as well as identifies grand challenges and opportunities to advance liquid metal + x composites.