Carbon fiber reinforced polymer (CFRP) composites have been increasingly used to replace metal parts in many industries such as aerospace, marine, automotive, and sporting goods. The CFRP parts compared with their metallic counter parts have the advantages of lightweight, significantly higher tensile strength, stiffer, and corrosion resistant. On the other hand, compared with many metal parts, the CFRP parts have many well-known disadvantages including the lower toughness, lower through-thickness tensile and shear strengths, lower thermal conductivity, lower electrical conductivity, and lower operating temperature. These disadvantages have made the conversion from metal parts into CFRP parts challenging and costly to design, manufacture, and maintain.
The use of nanoparticles in polymer has been studied in the recent two decades. Carbon nanotubes (CNTs) and carbon nanofibers (CNFs) have been dispersed in various thermoset and thermoplastic polymers and improved the mechanical, electrical, and thermal properties; however, the properties were not comparable to CFRP. Later, researchers tried to infuse CNTs or CNFs into either carbon fiber preforms [1] or glass fiber preforms [2] for improving the mechanical properties. But the results were marginal and with great uncertainty due to the challenges of nanoparticle dispersion, filtering, and alignment while being infused through the fiber preform. The glass fiber preform experiments ended with relatively more consistent improvement than the carbon fiber preform experiments since that the glass fiber preform has significantly larger pores than the carbon fiber preform' s. The small pore size presented a great challenge for infusing millions of unaligned long CNTs or CNFs through the carbon fiber preform without being filtered.
To infuse long CNFs or CNTs through the carbon fiber preform and achieve reliable improvements, especially for 55% or higher carbon fiber volume fraction with increasingly tighter pores, an innovative plan for the processing and nano-reinforcing strategy is necessary. The z-threading strategy [3, 4, 5] has been reported to have consistent experimental successes in achieving the statistically meaningful improvement in multifunctional properties. The manufacturing steps of the CNF z-threaded CFRP (ZT-CFRP) are: (1) disperse the CNFs in a resin, (2) use a strong electrical field to align the CNFs in either the B-stage epoxy film or a CNF/resin impregnated sponge layer, whereas the CNFs are aligned in the through-thickness direction of the film or sponge layer. (3) place the resin film or sponge layer on a preheated dry carbon fiber fabric and press the resin film into the hot carbon fabric and allow the resin flow to carry the well-aligned CNFs to thread through the pores in the carbon fabric. (4) cool down the resin saturated and CNF z-threaded carbon fiber fabric to obtain the ZT-CFRP prepreg. (5) use the ZT-CFRP prepreg to make the ZT-CFRP laminate. Compared with the traditional CFRP, the ZT-CFRP laminates were reported of having improvement in the Mode-I delamination toughness, interlaminar shear strength, longitudinal compressive strength, through-thickness electrical conductivity, through-thickness thermal conductivity, and can reach the carbon fiber volume fraction of 55-80%. It is an effective approach to achieve a multifunctional CFRP for potentially expanding CFRP's applications.
more »
« less
Hierarchically Structured Composite Fibers for Real Nanoscale Manipulation of Carbon Nanotubes
Carbon nanotube (CNT)‐reinforced polymer fibers have broad applications in electrical, thermal, optical, and smart applications. The key for mechanically robust fibers is the precise microstructural control of these CNTs, including their location, dispersion, and orientation. A new methodology is presented here that combines dry‐jet‐wet spinning and forced assembly for scalable fabrication of fiber composites, consisting of alternating layers of polyacrylonitrile (PAN) and CNT/PAN. The thickness of each layer is controlled during the multiplication process, with resolutions down to the nanometer scale. The introduction of alternating layers facilitates the quality of CNT dispersion due to nanoscale confinement, and at the same time, enhances their orientation due to shear stress generated at each layer interface. In a demonstration example, with 0.5 wt% CNTs loading and the inclusion of 170 nm thick layers, a composite fiber shows a significant mechanical enhancement, namely, a 46.4% increase in modulus and a 39.5% increase in strength compared to a pure PAN fiber. Beyond mechanical reinforcement, the presented fabrication method is expected to have enormous potential for scalable fabrication of polymer nanocomposites with complex structural features for versatile applications.
more » « less- Award ID(s):
- 1902172
- NSF-PAR ID:
- 10452491
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 31
- Issue:
- 14
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Abstract Pellet-based extrusion deposition of carbon fiber-reinforced composites at high material deposition rates has recently gained much attention due to its applications in large-scale additive manufacturing. The mechanical and physical properties of large-volume components largely depend on their reinforcing fiber length. However, very few studies have been done thus far to have a direct comparison of additively fabricated composites reinforced with different carbon fiber lengths. In this study, a new additive manufacturing (AM) approach to fabricate long fiber-reinforced polymer (LFRP) was first proposed. A pellet-based extrusion deposition method was implemented, which directly used thermoplastic pellets and continuous fiber tows as feedstock materials. Discontinuous long carbon fibers, with an average fiber length of 20.1 mm, were successfully incorporated into printed LFRP samples. The printed LFRP samples were compared with short fiber-reinforced polymer (SFRP) and continuous fiber-reinforced polymer (CFRP) counterparts through mechanical tests and microstructural analyses. The carbon fiber dispersion, distribution of carbon fiber length and orientation, and fiber wetting were studied. As expected, a steady increase in flexural strength was observed with increasing fiber length. The carbon fibers were highly oriented along the printing direction. A more uniformly distributed discontinuous fiber reinforcement was found within printed SFRP and LFRP samples. Due to decreased fiber impregnation time and lowered impregnation rate, the printed CFRP samples showed a lower degree of impregnation and worse fiber wetting conditions. The feasibility of the proposed AM methods was further demonstrated by fabricating large-volume components with complex geometries.more » « less
-
more » « less
Abstract Conventional dialyzer membranes typically comprise of unevenly distributed polydisperse, tortuous, rough pores, embedded in relatively thick ≈20–50 µm polymer layers wherein separation occurs via size exclusion as well as differences in diffusivity of the permeating species. However, transport in such polymeric pores is increasingly hindered as the molecule size approaches the pore dimension, resulting in significant retention of undesirable middle molecules (≥15–60 kDa) and uremic toxins. Enhanced removal of middle molecules is usually accompanied by high albumin loss (≈66 kDa) causing hypoalbuminemia. Here, the scalable bottom‐up fabrication of wafer‐scale carbon nanotube (CNT) membranes with highly aligned, low‐friction, straight‐channels/capillaries and narrow pore‐diameter distributions (≈0.5–4.5 nm) is demonstrated, to overcome persistent challenges in hemofiltration/hemodialysis. Using fluorescein isothiocyanate (FITC)‐Ficoll 70 and albumin in phosphate buffered saline (PBS) as well as in bovine blood plasma, it is shown that CNT membranes can allow for significantly higher hydraulic permeability (more than an order of magnitude when normalized to pore area) than commercial high‐flux hemofiltration/hemodialysis membranes (HF 400), as well as greatly enhance removal of middle molecules while maintaining comparable albumin retention. These findings are rationalized via an N‐pore transport model that highlights the critical role of molecular flexing and deformation during size‐selective transport within nanoscale confinements of the CNTs. The unique transport characteristics of CNTs coupled with size‐exclusion and wafer‐scale fabrication offer transformative advances for hemofiltration, and the obtained insight into molecular transport can aid advancements in several other bio‐systems/applications beyond hemofiltration/hemodialysis.
-
Reinforcing composite materials with carbon nanotubes (CNTs) has the potential to improve mechanical and/or multifunctional properties due to their nano-size. Research has been done on using CNTs to reinforce the interlaminar strength of carbon fiber reinforced composites (CFRPs), but most of the previous work is about randomly oriented carbon nanotubes. Currently, one of the main challenges regarding CNT integration into polymers is mitigating their agglomeration and controlling their dispersion in the polymer matrix. By aligning CNTs with an external field, more tailored structure control can be achieved, and a better understanding of how CNT agglomeration and dispersion relate to external field application and CNT concentration is needed. In this work, we studied the effects of magnetic field magnitude, CNT concentration, and matrix viscosity on CNT agglomeration and morphology. We measured the fracture toughness reinforcement of epoxy-CNT nanocomposites at various CNT concentrations (0.1 vol.% and 0.5 vol.%), magnetic field magnitudes (no field, 180 G, and 300 G), and matrix viscosities (older epoxy-hardener system with higher viscosity and newer epoxy-hardener system with lower viscosity). Our results demonstrated that aligning CNTs with a magnetic field can lead to extra reinforcement when compared to using randomly oriented CNTs if the field magnitude, CNT concentration, and matrix viscosity are selected accordingly. The maximum fracture toughness reinforcement achieved with the higher viscosity epoxy-hardener system (~72%) was with 0.5 vol.% of CNTs with a 180 G field, whereas the maximum reinforcement with the lower viscosity epoxy-hardener system (~62%) was observed for the samples fabricated with 0.1 vol.% of randomly oriented CNTs. COMSOL simulations were also conducted to understand the behavior of CNT agglomeration and alignment at different field magnitudes and CNT concentrations, and were compared with the experimental results. To maximize CNT reinforcement, more work needs to be conducted to address the challenge of CNT agglomeration and dispersion control in a polymer matrix, such as a more in-depth study of how different field magnitudes affect fracture toughness improvement and new methods to improve CNT dispersion.more » « less
-
more » « less
Abstract Highly conductive and mechanically strong microfibers are attractive in energy storage, thermal management, and wearable electronics. Here, a highly conductive and strong carbon nanotube/nanofibrillated cellulose (CNT–NFC) composite microfiber is developed via a fast and scalable 3D‐printing method. CNTs are successfully dispersed in an aqueous solution using 2,2,6,6‐tetramethylpiperidinyl‐1‐oxyl (TEMPO) oxidated NFCs, resulting in a mixture solution with an obvious shear‐thinning property. Both NFC and CNT fibers inside the all‐fiber‐based microfibers are well aligned, which helps to improve the interaction and percolation between these two building blocks, leading to a combination of high mechanical strength (247 ± 5 MPa) and electrical conductivity (216.7 ± 10 S cm−1). Molecular modeling is applied to offer further insights into the role of CNT–NFC fiber alignment for the excellent mechanical strength. The combination of high electrical conductivity, mechanical strength, and the fast yet scalable 3D‐printing technology positions the CNT–NFC composite microfiber as a promising candidate for wearable electronic devices.