Title: Nanostructure of bioactive glass affects bone cell attachment via protein restructuring upon adsorption
Abstract

The nanostructure of engineered bioscaffolds has a profound impact on cell response, yet its understanding remains incomplete as cells interact with a highly complex interfacial layer rather than the material itself. For bioactive glass scaffolds, this layer comprises of silica gel, hydroxyapatite (HA)/carbonated hydroxyapatite (CHA), and absorbed proteins—all in varying micro/nano structure, composition, and concentration. Here, we examined the response of MC3T3-E1 pre-osteoblast cells to 30 mol% CaO–70 mol% SiO2porous bioactive glass monoliths that differed only in nanopore size (6–44 nm) yet resulted in the formation of HA/CHA layers with significantly different microstructures. We report that cell response, as quantified by cell attachment and morphology, does not correlate with nanopore size, nor HA/CHO layer micro/nano morphology, or absorbed protein amount (bovine serum albumin, BSA), but with BSA’s secondary conformation as indicated by its β-sheet/α-helix ratio. Our results suggest that the β-sheet structure in BSA interacts electrostatically with the HA/CHA interfacial layer and activates the RGD sequence of absorbed adhesion proteins, such as fibronectin and vitronectin, thus significantly enhancing the attachment of cells. These findings provide new insight into the interaction of cells with the scaffolds’ interfacial layer, which is vital for the continued development of engineered tissue scaffolds.

 
more » « less
NSF-PAR ID:
10217044
Author(s) / Creator(s):
; ; ;
Publisher / Repository:
Nature Publishing Group
Date Published:
Journal Name:
Scientific Reports
Volume:
11
Issue:
1
ISSN:
2045-2322
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    For hard tissue regeneration, the bioactivity of a material is measured by its ability to induce the formation of hydroxyapatite (HA) under physiological conditions. It depends on the dissolution behavior of the glass, which itself is determined by the composition and structure of glass. The enhanced HA growth on nanoporous than on nonporous glass has been attributed by some to greater specific surface area (SSA), but to nanopore size distribution by others. To decouple the influence of nanopore size and SSA on HA formation, we have successfully fabricated homogeneous 30CaO‐70SiO2(30C70S) model bioactive glass monoliths with different nanopore sizes, yet similar SSA via a combination of sol–gel, solvent exchange, and sintering processes. After incubation in PBS, HA, and Type‐B carbonated HA (HA/B‐CHA) form on nanoporous monoliths. The XPS, FTIR, and SEM analyses provide the first unambiguous demonstration of the influence of nanopore size alone on the formation pathway, growth rate, and microstructure of HA/CHA. Due to pore‐size limited diffusion of PO43−, two HA/CHA formation pathways are observed: HA/CHA surface deposition and/or HA/CHA incorporation into nanopores. HA/CHA growth rate on the surface of a nanoporous glass monolith is dominated by the pore‐size limited transport of Ca2+ions dissolved from nanoporous glass substrates. Furthermore, with increasing nanopore size, HA/CHA microstructures evolve from needle‐like, plate‐like, to flower‐like appearance. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 886–899, 2019.

     
    more » « less
  2. Coordination of clinically employed bisphosphonate, risedronate (RISE), to bioactive metals, Ca2+, Mg2+, and Zn2+, allowed the formation of bisphosphonate-based coordination complexes (BPCCs). Three RISE-based BPCCs, RISE-Ca, RISEMg, and RISE-Zn, were produced, and their structures were elucidated by single crystal X-ray difraction. Interestingly, the addition of an auxiliary ligand, etidronic acid (HEDP), resulted in the recrystallized protonated form of the ligand, H-RISE. The pH-dependent structural stability of the RISE-based BPCCs was measured by means of dissolution profles under neutral and acidic simulated physiological conditions (PBS and FaSSGF, respectively). In comparison to RISE (Actonel), the complexes showed a lower equilibrium solubility (∼70−85% in 18−24 h) in PBS, while a higher equilibrium solubility (∼100% in 3 h) in acidic media. The results point to the capacity to release this BP in a pH-dependent manner from the RISE-based BPCCs. Subsequently, the particle size of RISE-Ca was reduced, from 300 μm to ∼350 d.nm, employing the phase inversion temperature (PIT)-nanoemulsion method, resulting in nano-Ca@RISE. Aggregation measurements of nano-Ca@RISE in 1% fetal bovine serum (FBS):H2O was monitored after 24, 48, and 72 h to study the particle size longevity in physiological media, showing that the suspended material has the potential to maintain its particle size over time. Furthermore, binding assays were performed to determine the potential binding of nano-Ca@RISE to the bone, where results show higher binding (~1.7×) for the material to hydroxyapatite (HA, 30%) when compared to RISE (17%) in 1 d. The cytotoxicity efects of nano-Ca@RISE were compared to those of RISE against the human breast cancer MDA-MB-231 and normal osteoblast-like hFOB 1.19 cell lines by dose−response curves and relative cell viability assays in an in vitro setting. The results demonstrate that nano-Ca@RISE signifcantly decreases the viability of MDA-MB-231 with high specifcity, at concentrations ∼2−3× lower than the ones reported employing other third-generation BPs. This is supported by the fact that when normal osteoblast cells (hFOB 1.19), which are part of the tissue microenvironment at metastatic sites, were treated with nano-Ca@RISE no signifcant decrease in viability was observed. This study expands on the therapeutic potential of RISE beyond its antiresorptive activity through the design of BPCCs, specifcally nano-Ca@RISE, that bind to the bone and degrade in a pH-dependent manner under acidic conditions 
    more » « less
  3. null (Ed.)
    Background Volumetric tissue-engineered constructs are limited in development due to the dependence on well-formed vascular networks. Scaffold pore size and the mechanical properties of the matrix dictates cell attachment, proliferation and successive tissue morphogenesis. We hypothesize scaffold pore architecture also controls stromal-vessel interactions during morphogenesis. Methods The interaction between mesenchymal stem cells (MSCs) seeded on hydroxyapatite scaffolds of 450, 340, and 250 μm pores and microvascular fragments (MVFs) seeded within 20 mg/mL fibrin hydrogels that were cast into the cell-seeded scaffolds, was assessed in vitro over 21 days and compared to the fibrin hydrogels without scaffold but containing both MSCs and MVFs. mRNA sequencing was performed across all groups and a computational mechanics model was developed to validate architecture effects on predicting vascularization driven by stiffer matrix behavior at scaffold surfaces compared to the pore interior. Results Lectin staining of decalcified scaffolds showed continued vessel growth, branching and network formation at 14 days. The fibrin gel provides no resistance to spread-out capillary networks formation, with greater vessel loops within the 450 μm pores and vessels bridging across 250 μm pores. Vessel growth in the scaffolds was observed to be stimulated by hypoxia and successive angiogenic signaling. Fibrin gels showed linear fold increase in VEGF expression and no change in BMP2. Within scaffolds, there was multiple fold increase in VEGF between days 7 and 14 and early multiple fold increases in BMP2 between days 3 and 7, relative to fibrin. There was evidence of yap/taz based hippo signaling and mechanotransduction in the scaffold groups. The vessel growth models determined by computational modeling matched the trends observed experimentally. Conclusion The differing nature of hypoxia signaling between scaffold systems and mechano-transduction sensing matrix mechanics were primarily responsible for differences in osteogenic cell and microvessel growth. The computational model implicated scaffold architecture in dictating branching morphology and strain in the hydrogel within pores in dictating vessel lengths. 
    more » « less
  4. Abstract

    Electrospinning is considered a powerful method for the production of fibers in the nanoscale size. Small pore size results in poor cell infiltration, cell migration inhibition into scaffold pores and low oxygen diffusion. Electrospun polycaprolactone/gelatin/nano‐hydroxyapatite (PCL/Gel/nHA) scaffolds were deposited into two types of fiber collectors (novel rotating disc and plate) to study fiber morphology, chemical, mechanical, hydrophilic, and biodegradation properties between each other. The proliferation and differentiation of MG‐63 cells into the bone phenotype were determined using MTT method, alizarin red staining and alkaline phosphatase (ALP) activity. The rates for disc rotation were 50 and 100 rpm. The pore size measurement results indicated that the fibers produced by the disc rotation collector with speed rate 50 rpm have larger pores as compared to fibers produced by disc rotation at 100 rpm and flat plate collectors. A randomly structure with controlled pore size (38.65 ±0.33 μm) and lower fiber density, as compared to fibers collected by disc rotation with speed rate 100 rpm and flat plate collectors, was obtained. Fibers collected on the rotating disc with speed rate 50 rpm, were more hydrophilic due to larger pore size and therefore, faster infiltration of water into the scaffold and the rate of degradation was higher. These results demonstrate that PCL/Gel/nHA scaffolds made through a rotating disc collector at 50 rpm are more feasible to be used in bone tissue engineering applications due to appropriate pore size and increased adhesion and proliferation of cells, ALP activity and mineral deposits. © 2018 Wiley Periodicals, Inc. J Biomed Mater Res Part B: Appl Biomater 107B: 933–950, 2019.

     
    more » « less
  5. Delivering stem/progenitor cells via a degradable synthetic membrane to devitalized allogenic tissue graft surfaces presents a promising allograft‐mediated tissue regeneration strategy. However, balancing degradability and bioactivity of the synthetic membrane with physical characteristics demanded for successful clinical translation is challenging. Here, well‐integrated composites of hydroxyapatite (HA) and amphiphilic poly(lactide‐co‐glycolide)‐b‐poly(ethylene glycol)‐b‐poly(lactide‐co‐glycolide) (PELGA) with tunable degradation rates are designed that stiffen upon hydration and exhibit excellent shape recovery ability at body temperature for efficiently delivering skeletal progenitor cells around bone grafts. Unlike conventional degradable polymers that weaken upon wetting, these amphiphilic composites stiffen upon hydration as a result of enhanced polyethylene glycol (PEG) crystallization. HA‐PELGA composite membranes support the attachment, proliferation, and osteogenesis of rat periosteum‐derived cells in vitro, as well as the facile transfer of confluent cell sheets of green fluorescent protein‐labeled bone marrow stromal cells. With efficient shape memory behaviors around physiological temperature, the composite membranes can be programmed with a permanent tubular configuration, deformed into a flat temporary shape desired for cell seeding/cell sheet transfer, and triggered to wrap around a femoral bone allograft upon 37 °C saline rinse and subsequently stiffen. These properties combined make electrospun HA‐PELGA promising smart synthetic periosteal membranes for augmenting allograft healing.

     
    more » « less