Magnetic nanoparticles are indispensable in many biomedical applications, but it remains unclear how the composition and structure will influence the application specific performance. We consider two compositions, ferrite and cobalt ferrite, synthesized under conditions that create aggregated multi‐core nanoparticles, called nanoflowers. Each nanoflower has an ionic surfactant or dextran to provide colloid stability in water. The composition, but not the coating, greatly impacts the heating output and the magnetic particle imaging tracer quality (with cobalt ferrite significantly reduced compared to ferrite). The cobalt ferrite nanoflowers have a core/shell structure with a reduced magnetization, which limits the effective magnetic anisotropy of the individual cobalt ferrite nanoflowers as well as the magnetic interactions among the nanoflowers. Both limitations significantly reduce the overall increase in the magnetic anisotropy with increasing magnetic field and consequently the nanoflowers’ efficacy for heating and imaging. Despite this, the formation of denser‐packed clusters and chains with external magnetic field in the ionic surfactant‐cobalt ferrite nanoflowers overcomes some of the shell's detrimental effects, resulting in better heating and imaging properties compared to the dextran‐cobalt ferrite. In short, the magnetic anisotropy dominates over physical and magnetic structure in the performance of the studied nanoflowers for heating and imaging applications.
Recent advancements in the study of intrinsic magnetic topological insulators and magnetic Weyl semimetals
- Award ID(s):
- 1917579
- PAR ID:
- 10233343
- Date Published:
- Journal Name:
- APL Materials
- Volume:
- 8
- Issue:
- 9
- ISSN:
- 2166-532X
- Page Range / eLocation ID:
- 090701
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Magnetic elastomers with hard or permanent magnetic particulate are able to achieve complex motion not possible from soft magnetic elastomers. Magnetic annealing and fused deposition modeling (FDM) have been used to increase the performance of magnetic composites. This research explores how the magnetoactive properties of hard magnetic elastomers are influenced by magnetic annealing and the addition of the soft magnetic particulate. Three compositions of the thermoplastic magnetic elastomer composite are explored: 15 vol. % SrFe 12 O 19 , 10 vol. % SrFe 12 O 19 /5 vol. % carbonyl iron, and 5 vol. % SrFe 12 O 19 /10 vol. % carbonyl iron. The material is then extruded into FDM filaments. During the extrusion process, some filament is magnetically annealed in an axial applied field. Magnetic hysteresis loops show that the saturation magnetization and coercivity change based on the relative amount of hard and soft magnetic particulate. The presence of only one coercive field indicates magnetic coupling between the hard and soft components. Magnetoactive testing measures each sample’s mechanical deflection angle as a function of transverse applied magnetic field strength. Qualitative and quantitative results reveal that magnetic annealing is critical to the magnetoactive performance of the hard magnetic elastomers. The results also demonstrate that magnetic annealing and increased carbonyl iron both improve the magnetoactive deflection angle for a given applied field. Scanning electron microscopy shows a stratification effect in a range of the filaments. Understanding these hard magnetic elastomers provides insight into how performance can be controlled and optimized by magnetic annealing and combining hard and soft magnetic particulate.more » « less