Title: Direct Ink Writing of Polymer Composite Electrolytes with Enhanced Thermal Conductivities
Abstract

Proper distribution of thermally conductive nanomaterials in polymer batteries offers new opportunities to mitigate performance degradations associated with local hot spots and safety concerns in batteries. Herein, a direct ink writing (DIW) method is utilized to fabricate polyethylene oxide (PEO) composite polymers electrolytes (CPE) embedded with silane‐treated hexagonal boron nitride (S‐hBN) platelets and free of any volatile organic solvents. It is observed that the S‐hBN platelets are well aligned in the printed CPE during the DIW process. The in‐plane thermal conductivity of the printed CPE with the aligned S‐hBN platelets is 1.031 W−1K−1, which is about 1.7 times that of the pristine CPE with the randomly dispersed S‐hBN platelets (0.612 W−1K−1). Thermal imaging shows that the peak temperature (°C) of the printed electrolytes is 24.2% lower than that of the CPE without S‐hBN, and 10.6% lower than that of the CPE with the randomly dispersed S‐hBN, indicating a superior thermal transport property. Lithium‐ion half‐cells made with the printed CPE and LiFePO4cathode displayed high specific discharge capacity of 146.0 mAh g−1and stable Coulombic efficiency of 91% for 100 cycles at room temperature. This work facilitates the development of printable thermally‐conductive polymers for safer battery operations.

 
more » « less
Award ID(s):
1805938 1825626
NSF-PAR ID:
10454490
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Functional Materials
Volume:
31
Issue:
4
ISSN:
1616-301X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    This present study illustrates the synthesis and preparation of polyoxanorbornene‐based bottlebrush polymers with poly(ethylene oxide) (PEO) side chains by ring‐opening metathesis polymerization for solid polymer electrolytes (SPE). In addition to the conductive PEO side chains, the polyoxanorbornene backbones may act as another ion conductor to further promote Li‐ion movement within the SPE matrix. These results suggest that these bottlebrush polymer electrolytes provide impressively high ionic conductivity of 7.12 × 10−4S cm−1at room temperature and excellent electrochemical performance, including high‐rate capabilities and cycling stability when paired with a Li metal anode and a LiFePO4cathode. The new design paradigm, which has dual ionic conductive pathways, provides an unexplored avenue for inventing new SPEs and emphasizes the importance of molecular engineering to develop highly stable and conductive polymer electrolytes for lithium‐metal batteries (LMB).

     
    more » « less
  2. Ever-increasing demands for energy, particularly being environmentally friendly have promoted the transition from fossil fuels to renewable energy.1Lithium-ion batteries (LIBs), arguably the most well-studied energy storage system, have dominated the energy market since their advent in the 1990s.2However, challenging issues regarding safety, supply of lithium, and high price of lithium resources limit the further advancement of LIBs for large-scale energy storage applications.3Therefore, attention is being concentrated on an alternative electrochemical energy storage device that features high safety, low cost, and long cycle life. Rechargeable aqueous zinc-ion batteries (ZIBs) is considered one of the most promising alternative energy storage systems due to the high theoretical energy and power densities where the multiple electrons (Zn2+) . In addition, aqueous ZIBs are safer due to non-flammable electrolyte (e.g., typically aqueous solution) and can be manufactured since they can be assembled in ambient air conditions.4As an essential component in aqueous Zn-based batteries, the Zn metal anode generally suffers from the growth of dendrites, which would affect battery performance in several ways. Second, the led by the loose structure of Zn dendrite may reduce the coulombic efficiency and shorten the battery lifespan.5

    Several approaches were suggested to improve the electrochemical stability of ZIBs, such as implementing an interfacial buffer layer that separates the active Zn from the bulk electrolyte.6However, the and thick thickness of the conventional Zn metal foils remain a critical challenge in this field, which may diminish the energy density of the battery drastically. According to a theretical calculation, the thickness of a Zn metal anode with an areal capacity of 1 mAh cm-2is about 1.7 μm. However, existing extrusion-based fabrication technologies are not capable of downscaling the thickness Zn metal foils below 20 μm.

    Herein, we demonstrate a thickness controllable coating approach to fabricate an ultrathin Zn metal anode as well as a thin dielectric oxide separator. First, a 1.7 μm Zn layer was uniformly thermally evaporated onto a Cu foil. Then, Al2O3, the separator was deposited through sputtering on the Zn layer to a thickness of 10 nm. The inert and high hardness Al2O3layer is expected to lower the polarization and restrain the growth of Zn dendrites. Atomic force microscopy was employed to evaluate the roughness of the surface of the deposited Zn and Al2O3/Zn anode structures. Long-term cycling stability was gauged under the symmetrical cells at 0.5 mA cm-2for 1 mAh cm-2. Then the fabricated Zn anode was paired with MnO2as a full cell for further electrochemical performance testing. To investigate the evolution of the interface between the Zn anode and the electrolyte, a home-developed in-situ optical observation battery cage was employed to record and compare the process of Zn deposition on the anodes of the Al2O3/Zn (demonstrated in this study) and the procured thick Zn anode. The surface morphology of the two Zn anodes after circulation was characterized and compared through scanning electron microscopy. The tunable ultrathin Zn metal anode with enhanced anode stability provides a pathway for future high-energy-density Zn-ion batteries.

    Obama, B., The irreversible momentum of clean energy.Science2017,355(6321), 126-129.

    Goodenough, J. B.; Park, K. S., The Li-ion rechargeable battery: a perspective.J Am Chem Soc2013,135(4), 1167-76.

    Li, C.; Xie, X.; Liang, S.; Zhou, J., Issues and Future Perspective on Zinc Metal Anode for Rechargeable Aqueous Zinc‐ion Batteries.Energy & Environmental Materials2020,3(2), 146-159.

    Jia, H.; Wang, Z.; Tawiah, B.; Wang, Y.; Chan, C.-Y.; Fei, B.; Pan, F., Recent advances in zinc anodes for high-performance aqueous Zn-ion batteries.Nano Energy2020,70.

    Yang, J.; Yin, B.; Sun, Y.; Pan, H.; Sun, W.; Jia, B.; Zhang, S.; Ma, T., Zinc Anode for Mild Aqueous Zinc-Ion Batteries: Challenges, Strategies, and Perspectives.Nanomicro Lett2022,14(1), 42.

    Yang, Q.; Li, Q.; Liu, Z.; Wang, D.; Guo, Y.; Li, X.; Tang, Y.; Li, H.; Dong, B.; Zhi, C., Dendrites in Zn-Based Batteries.Adv Mater2020,32(48), e2001854.

    Acknowledgment

    This work was partially supported by the U.S. National Science Foundation (NSF) Award No. ECCS-1931088. S.L. and H.W.S. acknowledge the support from the Improvement of Measurement Standards and Technology for Mechanical Metrology (Grant No. 22011044) by KRISS.

    Figure 1

     

    more » « less
  3. Abstract

    The proliferation and miniaturization of portable electronics require energy‐storage devices that are simultaneously compact, flexible, and amenable to scalable manufacturing. In this work, mechanically flexible micro‐supercapacitor arrays are demonstrated via sequential high‐speed screen printing of conductive graphene electrodes and a high‐temperature hexagonal boron nitride (hBN) ionogel electrolyte. By combining the superlative dielectric properties of 2D hBN with the high ionic conductivity of ionic liquids, the resulting hBN ionogel electrolyte enables micro‐supercapacitors with exceptional areal capacitances that approach 1 mF cm−2. Unlike incumbent polymer‐based electrolytes, the high‐temperature stability of the hBN ionogel electrolyte implies that the printed micro‐supercapacitors can be operated at unprecedentedly high temperatures up to 180 °C. These elevated operating temperatures result in increased power densities that make these printed micro‐supercapacitors particularly promising for applications in harsh environments such as underground exploration, aviation, and electric vehicles. The combination of enhanced functionality in extreme conditions and high‐speed production via scalable additive manufacturing significantly broadens the technological phase space for on‐chip energy storage.

     
    more » « less
  4. Abstract

    The emergence of conductive 2D and less commonly 3D coordination polymers (CPs) and metal–organic frameworks (MOFs) promises novel applications in many fields. However, the synthetic parameters for these electronically complex materials are not thoroughly understood. Here we report a new 3D semiconducting CPFe5(C6O6)3, which is a fusion of 2D Fe‐semiquinoid materials and 3D cubicFex(C6O6)ymaterials, by using a different initial redox‐state of the C6O6linker. The material displays high electrical conductivity (0.02 S cm−1), broad electronic transitions, promising thermoelectric behavior (S2σ=7.0×10−9 W m−1 K−2), and strong antiferromagnetic interactions at room temperature. This material illustrates how controlling the oxidation states of redox‐active components in conducting CPs/MOFs can be a “pre‐synthetic” strategy to carefully tune material topologies and properties in contrast to more commonly encountered post‐synthetic modifications.

     
    more » « less
  5. Abstract

    The emergence of conductive 2D and less commonly 3D coordination polymers (CPs) and metal–organic frameworks (MOFs) promises novel applications in many fields. However, the synthetic parameters for these electronically complex materials are not thoroughly understood. Here we report a new 3D semiconducting CPFe5(C6O6)3, which is a fusion of 2D Fe‐semiquinoid materials and 3D cubicFex(C6O6)ymaterials, by using a different initial redox‐state of the C6O6linker. The material displays high electrical conductivity (0.02 S cm−1), broad electronic transitions, promising thermoelectric behavior (S2σ=7.0×10−9 W m−1 K−2), and strong antiferromagnetic interactions at room temperature. This material illustrates how controlling the oxidation states of redox‐active components in conducting CPs/MOFs can be a “pre‐synthetic” strategy to carefully tune material topologies and properties in contrast to more commonly encountered post‐synthetic modifications.

     
    more » « less