Title: Novel composite hydrogels containing fractionated, purified lignins for aqueous-based separations
Herein, a series of novel, lignin-based hydrogel composites was fabricated by incorporating ultraclean lignins (UCLs), of controlled molecular weight and low dispersity, into poly(vinyl alcohol) (PVA). The UCLs were obtained from a novel liquid–liquid fractionation of high dispersity crude bulk lignins (CBLs) obtained from Kraft black liquor. A complementary series of composite hydrogels was fabricated using these CBLs. Both the CBLs and UCLs were functionalized with vinyl-containing acrylate groups allowing the lignins to chemically crosslink with themselves, forming an interpenetrated network with the thermally-crosslinked network of PVA chains. Successful functionalization of the UCLs was demonstrated by proton and phosphorous nuclear magnetic resonance. PVA–lignin hydrogels containing 20 wt% UCL saw a reduction in methylene blue (MB) permeability by approximately two orders of magnitude when compared to neat PVA. Further, for composite hydrogels containing either 50 wt% UCL or CBL, no MB was detected in the receiving reservoir over the duration of the permeation experiment. In general, an increase in Young's moduli was observed in PVA–lignin hydrogels containing CBLs, where hydrogels composed of 50 wt% CBLs exhibited ∼40% increase when compared to neat PVA. In contrast, a ∼10% reduction in Young's moduli was observed for composite hydrogels containing 20 wt% UCLs or less, though these membranes exhibited the lowest MB permeabilities of all membranes investigated. However, the largest increase in membrane stiffness was observed for composite hydrogels containing 50 wt% UCLs, where a ∼70% increase in Young's modulus was observed. Finally, the concentration and functionalization of the lignins was seen to have a direct impact on the network structure of the soft composites, where in general, the molecular weight between crosslinks is seen to decrease with increasing lignin concentration.  more » « less
Award ID(s):
1915787
NSF-PAR ID:
10256989
Author(s) / Creator(s):
; ; ;
Date Published:
Journal Name:
Journal of Materials Chemistry A
Volume:
9
Issue:
2
ISSN:
2050-7488
Page Range / eLocation ID:
1025 to 1038
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Hierarchically microstructured tri-axial poly(vinyl alcohol)/graphene nanoplatelet (PVA/GNP) composite fibers were fabricated using a dry-jet wet spinning technique. The composites with distinct PVA/GNPs/PVA phases led to highly oriented and evenly distributed graphene nanoplatelets (GNPs) as a result of molecular chain-assisted interfacial exfoliation. With a concentration of 3.3 wt% continuously aligned GNPs, the composite achieved a ∼73.5% increase in Young's modulus (∼38 GPa), as compared to the pure PVA fiber, and an electrical conductivity of ∼0.38 S m −1 , one of the best mechanical/electrical properties reported for polymer/GNP nanocomposite fibers. This study has broader impacts on textile engineering, wearable robotics, smart sensors, and optoelectronic devices. 
    more » « less
  2. Abstract

    Petrol and biochemical plasticizers are added to poly(vinyl alcohol) (PVA) to improve its processability while tuning its moisture sensitivity. But those additives often reduce the mechanical performance of PVA products. In this study, the antiplasticization and properties of PVA containing additives from biorenewable sources are studied. PVA fibers are gel‐spun having up to 3 wt% glucarate salts and 30% lignin. Glucarate lowers the gel melting temperature of PVA and increases fiber draw ratio. Further, glucarate enhances the mechanical performance of PVA beyond that of neat fibers. Interestingly, the combination of lignin and glucarate causes phase separation among fiber—a PVA/glucarate phase as the fiber core and lignin/PVA phase as the fiber shell. Neat PVA partially dissolves in 85 °C water; whereas, fibers containing glucarate and/or lignin resist dissolution. Thus, the combination of glucarate and lignin can induce high strength and moisture resistance, which are desirable industrial fiber properties.

     
    more » « less
  3. null (Ed.)
    Background:: Sandwich structures are progressively being used in various engineering applications due to the superior bending-stiffness-to-weight ratio of these structures. We adapted a novel technique to incorporate carbon nanotubes (CNTs) and polyhedral oligomeric silsesquioxanes (POSS) into a sandwich composite structure utilizing a sonochemical and high temperature vacuum assisted resin transfer molding technique. Objective:: The objective of this work was to create a sandwich composite structure comprised of a nanophased foam core and reinforced nanophased face sheets, and to examine the thermal and mechanical properties of the structure. To prepare sandwich structure, POSS nanoparticles were sonochemically attached to CNTs and dispersed in a high temperature resin system to make the face sheet materials and also coated on expandable thermoplastic microspheres for the fabrication of foam core materials. Method:: The nanophased foam core was fabricated with POSS infused thermoplastic microspheres (Expancel) using a Tetrahedron MTP-14 programmable compression molder. The reinforced nanophased face sheet were fabricated by infusing POSS coated CNT in epoxy resin and then curing into a compression stainless steel mold. Result:: Thermal analysis of POSS-infused thermoplastic microspheres foam (TMF) showed an increase in thermal stability in both nitrogen and oxygen atmospheres, 19% increase in thermal residue were observed for 4 wt% GI-POSS TMF compared to neat TMF. Quasi-static compression results indicated significant increases (73%) in compressive modulus, and an increase (5%) in compressive strength for the 1 wt% EC-POSS/CNTs resin system. The nanophased sandwich structure constructed from the above resin system and the foam core system displayed an increase (9%) in modulus over the neat sandwich structure. Conclusion:: The incorporation of POSS-nanofillier in the foam core and POSS-coated nanotubes in the face sheet significantly improved the thermal and mechanical properties of sandwich structure. Furthermore, the sandwich structure that was constructed from nanophased resin system showed an increase in modulus, with buckling in the foam core but no visible cracking. 
    more » « less
  4. Abstract

    Boron nitride nanotubes (BNNT) uniformly dispersed in stretchable materials, such as poly(dimethylsiloxane) (PDMS), could create the next generation of composites with augmented mechanical, thermal, and piezoelectric characteristics. This work reports tunable piezoelectricity of multifunctional BNNT/PDMS stretchable composites prepared via co‐solvent blending with tetrahydrofuran (THF) to disperse BNNTs in PDMS while avoiding sonication or functionalization. The resultant stretchable BNNT/PDMS composites demonstrate augmented Young's modulus (200% increase at 9 wt% BNNT) and thermal conductivity (120% increase at 9 wt% BNNT) without losing stretchability. Furthermore, BNNT/PDMS composites demonstrate piezoelectric responses that are linearly proportional to BNNT wt%, achieving a piezoelectric constant (|d33|) of 18 pmV−1at 9 wt% BNNT without poling, which is competitive with commercial piezoelectric polymers. Uniquely, BNNT/PDMS accommodates tensile strains up to 60% without plastic deformation by aligning BNNTs, which enhances the composites’ piezoelectric response approximately five times. Finally, the combined stretchable and piezoelectric nature of the composite was exploited to produce a vibration sensor sensitive to low‐frequency (≈1 kHz) excitation. This is the first demonstration of multifunctional, stretchable BNNT/PDMS composites with enhanced mechanical strength and thermal conductivity and furthermore tunable piezoelectric response by varying BNNT wt% and applied strain, permitting applications in soft actuators and vibration sensors.

     
    more » « less
  5. Membrane separations are simple to operate, scalable, versatile, and energy efficient, but their broader use is curtailed by fouling or performance decline due to feed component depositing on the membrane surface. Surface functionalization with groups such as zwitterions can mitigate the adsorption of organic compounds, thus limiting fouling. This can be achieved by using surface-segregating copolymer additives during membrane manufacture, but there is a need for better understanding of how the polymer structure and architecture affect the effectiveness of these additives in improving membrane performance. In this study, we aim to explore the impact of the architecture of zwitterionic copolymer additives for polyvinylidene fluoride (PVDF)-based membranes in fouling mitigation and ionic strength response. We prepared membranes from blends of PVDF with zwitterionic (ZI) copolymers with two different architectures, random and comb-shaped. As the random copolymer, we used poly(methyl methacrylate- random- sulfobetaine-2-vinyl pyridine) (PMMA- r -SB2VP) synthesized by free radical polymerization. The comb-shaped copolymer was synthesized by grafting SB2VP side-chains from a PVDF backbone by controlled radical polymerization. Membranes were fabricated from PVDF-copolymer blends containing up to 5 wt% ZI copolymer. Compared to the additive-free PVDF membrane, water permeance increased five-fold with 5 wt% addition of either copolymer. The comb copolymer additive led to better resistance to fouling by a saline oil-in-water emulsion and to simulated protein adsorption in Atomic Force Microscopy (AFM) force measurements. The additive architecture had a significant influence on how membranes respond to changes in feed salinity, which is known to affect intra- and inter-molecular interactions in zwitterionic polymers. The random copolymer containing membrane showed a small and mostly reversible decrease in its permeance with salinity. In contrast, the comb copolymer-containing membrane underwent a conformational reorganization in saline solutions that leads to an irreversible permeance decrease, increased zwitterionic group content on the membrane surface, and smoother surface topography. The higher mobility of the zwitterionic groups in the comb-shaped architecture facilitates reorganization of the zwitterionic side-chains in response to ionic strength. Overall, this study establishes a new approach for developing highly fouling resistant membranes and defines how the architecture of a zwitterionic copolymer additive impacts the ionic strength response and fouling resistance of the membrane. 
    more » « less