The optical and electrical performance of light trapping metallic electrodes is investigated. Reflection losses from metallic contacts are shown to be dramatically reduced compared to standard metallic contacts by leveraging total internal reflection at the surface of an added dielectric cover layer. Triangular wire arrays are shown to exhibit increased performance with increasing size, whereas cylindrical wires continue to exhibit diffractive losses as their size is increased. These trends are successfully correlated with radiation patterns from individual metallic wires. Triangular metallic electrodes with a metal areal coverage of 25% are shown to enable a polarization-averaged transmittance of >90% across the wavelength range 0.46-1.1 µm for an electrode width of 2 µm, with a peak transmission of 97%, a degree of polarization of <0.2%, and a sheet resistance of 0.35 Ω/sq. A new figure of merit is introduced to evaluate the light trapping potential of surface-shaped electrodes.
more »
« less
Light trapping transparent electrodes with a wide-angle response
The angle dependent transmission of light trapping transparent electrodes is investigated. The electrodes consist of triangular metallic wire arrays embedded in a dielectric cover layer. Normal incidence illumination of the structure produces light trapping via total internal reflection, virtually eliminating all shadowing losses. It is found that varying the external angle of incidence can affect the light trapping efficiency ηLTdue to partial loss of internal reflection and increased interaction with neighboring wires. Despite these effects, a judicious selection of geometry and materials can reduce shadowing losses by more than 85% over a surprisingly large angular range of 120°. It is demonstrated that the angle-averaged shadowing losses in an encapsulated silicon solar cell under illumination with unpolarized light can be reduced by more than a factor of two for incident angles between −60° and +60° off-normal across the entire AM1.5 solar spectrum.
more »
« less
- Award ID(s):
- 1650002
- PAR ID:
- 10278488
- Publisher / Repository:
- Optical Society of America
- Date Published:
- Journal Name:
- Optics Express
- Volume:
- 29
- Issue:
- 16
- ISSN:
- 1094-4087; OPEXFF
- Format(s):
- Medium: X Size: Article No. 24989
- Size(s):
- Article No. 24989
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Inclination of unpatterned, linearly polarized illumination in the plane of the electric field oscillation effected increased directional feature alignment and decreased off-axis order in Se–Te deposits generated by inorganic phototropic growth relative to that produced using normal incidence. Optically based growth simulations reproduced the experimental results indicating a photonic basis for the morphology change. Modeling of the light scattering at the growth interface revealed that illumination inclination enhances scattering that localizes the optical field along the polarization plane and suppresses cooperativity in defect-driven scattering. Thus, the symmetry of the deposited structures increased as the asymmetry of the illumination increased, as measured by the inclination of the illumination incidence away from the surface normal.more » « less
-
Photoelectrochemical (PEC) hydrogen generation is a promising solar energy harvesting technique to address the concerns about the ongoing energy crisis. Antimony selenide (Sb2Se3) with van der Waals‐bonded quasi‐1D (Q1D) nanoribbons, for instance, (Sb4Se6)n, has attracted considerable interest as a light absorber with Earth‐abundant elements, suitable bandgap, and a desired sunlight absorption coefficient. By tuning its anisotropic growth behavior, it is possible to achieve Sb2Se3films with nanostructured morphologies that can improve the light absorption and photogenerated charge carrier separation, eventually boosting the PEC water‐splitting performance. Herein, high‐quality Sb2Se3films with nanorod (NR) array surface morphologies are synthesized by a low‐cost, high‐yield, and scalable close‐spaced sublimation technique. By sputtering a nonprecious and scalable crystalline molybdenum sulfide (MoS2) film as a cocatalyst and a protective layer on Sb2Se3NR arrays, the fabricated core–shell structured MoS2/Sb2Se3NR PEC devices can achieve a photocurrent density as high as −10 mA cm−2at 0 VRHEin a buffered near‐neutral solution (pH 6.5) under a standard simulated air mass 1.5 solar illumination. The scalable manufacturing of nanostructured MoS2/Sb2Se3NR array thin‐film photocathode electrodes for efficient PEC water splitting to generate solar fuel is demonstrated.more » « less
-
Recently, reflection interference fringe (RIF) and transmission fringe (TIF) techniques have been introduced to investigate the origin of far-field interference fringe (IF) formation and to determine a droplet's contact angle and thickness by measuring the fringe radius. In this study, characteristics of the IF technique are analyzed based on the RIF and TIF by varying the schematics, such as configuration (transmission/reflection), the droplet's side (left-hand side/right-hand side), and the substrate types (flat/prism). The analysis also investigates the refraction effect at the droplet edge and the maximum incidence and contact angles. The schematic variation shows that the widest contact angle range can be measured in a transmission configuration with droplet's right-hand side, and that the fringe radius decreases with incidence angles on a prism substrate, consistent with the recent observation. Refraction at the droplet edge causes the fringe radius to increase or decrease depending on the degree of refraction. Based on the characteristics study, it is revealed that the IF technique can determine nanometer-scale thicknesses below 100 nm on droplets, corresponding to ultra-small contact angles of less than 0.01°, with an extended working distance of 3000 mm and an optimized incidence angle, assuming a spherical profile. This finding is significant, as it demonstrates that the nanoscale thickness can be determined in situ under ambient conditions using a simple optical configuration, without requiring a sophisticated setup, such as a microscope. It is anticipated that the IF technique can be combined with other nanoscale thickness measurement techniques to enhance its measurement reliability.more » « less
-
III–V‐based multijunction solar cells have become the leading power generation technology for space applications due to their high power conversion efficiency and reliable performance in extraterrestrial environments. Thinning down the absorber layers of multijunction solar cells can considerably reduce the production cost and improve their radiation hardness. Recent advances in ultrathin GaAs single‐junction solar cells suggest the development of light‐trapping nanostructures to increase light absorption in optically thin layers within III–V‐based multijunction solar cells. Herein, a novel and highly scalable nanosphere lithography‐assisted chemical etching method to fabricate light‐trapping nanostructures in InGaP/GaAs dual‐junction solar cells is studied. Numerical models show that integrating the nanostructured Al2O3/Ag rear mirror significantly enhances the broadband absorption within the GaAs bottom cell. Results demonstrate that the light‐trapping nanostructures effectively increase the short‐circuit current density in GaAs bottom cells from 14.04 to 15.06 mA cm−2. The simulated nanostructured InGaP/GaAs dual‐junction structure shows improved current matching between the GaAs bottom cell and the InGaP top cell, resulting in 1.12x higher power conversion efficiency. These findings highlight the potential of light‐trapping nanostructures to improve the performance of III‐V‐based multijunction photovoltaic systems, particularly for high‐efficiency applications in space.more » « less