The development of low-cost, highly efficient and stable electrocatalysts for the oxygen evolution reaction (OER) is of great significance for many promising energy storage and conversion applications, including metal–air batteries and water splitting technology. Here we report a layer-structured Ca 0.5 CoO 2 nanofibers composed of interconnected ultrathin nanoplates, synthesized using an electrospinning process. The OER activity of Ca 0.5 CoO 2 can be dramatically improved by iron doping, and the overpotential of Ca 0.5 Co 1− x Fe x O 2 ( x = 0.25) is only 346 mV at a current density of 10 mA cm −2 . The mass activity and intrinsic activity of Ca 0.5 Co 0.75 Fe 0.25 O 2 at 1.6 V are, respectively, ∼18.7 and ∼11.4 times higher than those of Ca 0.5 CoO 2 . Iron doping modifies the electronic structure of Ca 0.5 CoO 2 , resulting in partial oxidation of the surface cobalt and increased amount of highly oxidative species (O 2 2− /O 2 ). Consequently, Ca 0.5 Co 0.75 Fe 0.25 O 2 nanofibers with tuned electronic states have shown great potential as cost-effective and efficient electrocatalysts for OER.
more »
« less
Co 2‐x Rh x P Nanoparticles for Overall Water Splitting in Basic Media: Activation by Phase‐Segregation‐Assisted Nanostructuring at the Anode
Abstract The application of Co2‐xRhxP nanoparticles as electrocatalysts for the hydrogen evolution reaction (HER) and overall water splitting in basic media is reported. The experimental design seeks to dilute rhodium with earth‐abundant cobalt as a means to lower the cost of the material and achieve catalytic synergism, as reported for related bimetallic phosphides. The HER activity of Co2‐xRhxP is found to be composition‐dependent, with the rhodium‐rich compositions being more active as compared to their cobalt‐rich counterparts, with overpotentials (η) at 10 mA/cm2geometricof 58.1–63.9 mV vs. 82.1–188.1 mV, respectively. In contrast, Co‐rich Co2‐xRhxP nanoparticles are active for the oxygen evolution reaction (OER) process in basic media, with η= 290 mV for x=0.25. A full water electrolysis cell was created using the most active compositions for OER and HER as the anode and cathode, respectively, generating an overall η= 390 mV. Notably, the cell became more active over a 50 h stability test, increasing by 2 mV/cm2geometricat a constant applied voltage of 1.62 V vs NHE. This enhanced activity correlates with nanoscale phase segregation of Rh in the anode. Thus, the lower overpotential achieved for Co1.75Rh0.25P relative to Co2P, and the augmented activity over time in the former, may be a consequence of restructuring of the anode driven by Rh phase‐segregation. The augmentation in activity at the anode more than compensates for small losses at the cathode.
more »
« less
- Award ID(s):
- 1904775
- PAR ID:
- 10288054
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- ChemCatChem
- Volume:
- 13
- Issue:
- 19
- ISSN:
- 1867-3880
- Format(s):
- Medium: X Size: p. 4111-4119
- Size(s):
- p. 4111-4119
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
Abstract Abundant transition metal borides are emerging as substitute electrochemical hydrogen evolution reaction (HER) catalysts for noble metals. Herein, an unusual canonic‐like behavior of theclattice parameter in the AlB2‐type solid solution Cr1–xMoxB2(x= 0, 0.25, 0.4, 0.5, 0.6, 0.75, 1) and its direct correlation to the HER activity in 0.5 M H2SO4solution are reported. The activity increases with increasingx, reaching its maximum atx= 0.6 before decreasing again. At high current densities, Cr0.4Mo0.6B2outperforms Pt/C, as it needs 180 mV less overpotential to drive an 800 mA cm−2current density. Cr0.4Mo0.6B2has excellent long‐term stability and durability showing no significant activity loss after 5000 cycles and 25 h of operation in acid. First‐principles calculations have correctly reproduced the nonlinear dependence of theclattice parameter and have shown that the mixed metal/B layers, such as (110), promote hydrogen evolution more efficiently forx= 0.6, supporting the experimental results.more » « less
-
Abstract The main drawbacks of today's state‐of‐the‐art lithium–air (Li–air) batteries are their low energy efficiency and limited cycle life due to the lack of earth‐abundant cathode catalysts that can drive both oxygen reduction and evolution reactions (ORR and OER) at high rates at thermodynamic potentials. Here, inexpensive trimolybdenum phosphide (Mo3P) nanoparticles with an exceptional activity—ORR and OER current densities of 7.21 and 6.85 mA cm−2at 2.0 and 4.2 V versus Li/Li+, respectively—in an oxygen‐saturated non‐aqueous electrolyte are reported. The Tafel plots indicate remarkably low charge transfer resistance—Tafel slopes of 35 and 38 mV dec−1for ORR and OER, respectively—resulting in the lowest ORR overpotential of 4.0 mV and OER overpotential of 5.1 mV reported to date. Using this catalyst, a Li–air battery cell with low discharge and charge overpotentials of 80 and 270 mV, respectively, and high energy efficiency of 90.2% in the first cycle is demonstrated. A long cycle life of 1200 is also achieved for this cell. Density functional theory calculations of ORR and OER on Mo3P (110) reveal that an oxide overlayer formed on the surface gives rise to the observed high ORR and OER electrocatalytic activity and small discharge/charge overpotentials.more » « less
-
The two polymorphs of lithium cobalt oxide, LiCoO 2 , present an opportunity to contrast the structural requirements for reversible charge storage (battery function) vs. catalysis of water oxidation/oxygen evolution (OER; 2H 2 O → O 2 + 4H + + 4e − ). Previously, we reported high OER electrocatalytic activity from nanocrystals of the cubic phase vs. poor activity from the layered phase – the archetypal lithium-ion battery cathode. Here we apply transmission electron microscopy, electron diffraction, voltammetry and elemental analysis under OER electrolysis conditions to show that labile Li + ions partially deintercalate from layered LiCoO 2 , initiating structural reorganization to the cubic spinel LiCo 2 O 4 , in parallel with formation of a more active catalytic phase. Comparison of cubic LiCoO 2 (50 nm) to iridium (5 nm) nanoparticles for OER catalysis (commercial benchmark for membrane-based systems) in basic and neutral electrolyte reveals excellent performance in terms of Tafel slope (48 mV dec −1 ), overpotential ( η = ∼420 mV@10 mA cm −2 at pH = 14), faradaic yield (100%) and OER stability (no loss in 14 hours). The inherent OER activity of cubic LiCoO 2 and spinel LiCo 2 O 4 is attributed to the presence of [Co 4 O 4 ] n+ cubane structural units, which provide lower oxidation potential to Co 4+ and lower inter-cubane hole mobility. By contrast, the layered phase, which lacks cubane units, exhibits extensive intra-planar hole delocalization which entropically hinders the four electron/hole concerted OER reaction. An essential distinguishing trait of a truly relevant catalyst is efficient continuous operation in a real electrolyzer stack. Initial trials of cubic LiCoO 2 in a solid electrolyte alkaline membrane electrolyzer indicate continuous operation for 1000 hours (without failure) at current densities up to 400 mA cm −2 and overpotential lower than proven PGM (platinum group metal) catalysts.more » « less
-
The cobalt–seleno-based coordination complex, [Co{(SePiPr2)2N}2], is reported with respect to its catalytic activity in oxygen evolution and hydrogen evolution reactions (OER and HER, respectively) in alkaline solutions. An overpotential of 320 and 630 mV was required to achieve 10 mA cm−2 for OER and HER, respectively. The overpotential for OER of this CoSe4-containing complex is one of the lowest that has been observed until now for molecular cobalt(II) systems, under the reported conditions. In addition, this cobalt–seleno-based complex exhibits a high mass activity (14.15 A g−1) and a much higher turn-over frequency (TOF) value (0.032 s−1) at an overpotential of 300 mV. These observations confirm analogous ones already reported in the literature pertaining to the potential of molecular cobalt–seleno systems as efficient OER electrocatalysts.more » « less