Title: Band Edge Control of Quasi‐2D Metal Halide Perovskites for Blue Light‐Emitting Diodes with Enhanced Performance
Abstract

Perovskite light‐emitting diodes (PeLEDs) have received great attention for their potential as next‐generation display technology. While remarkable progress has been achieved in green, red, and near‐infrared PeLEDs with external quantum efficiencies (EQEs) exceeding 20%, obtaining high performance blue PeLEDs remains a challenge. Poor charge balance due to large charge injection barriers in blue PeLEDs has been identified as one of the major roadblocks to achieve high efficiency. Here band edge control of perovskite emitting layers for blue PeLEDs with enhanced charge balance and device performance is reported. By using organic spacer cations with different dipole moments, that is, phenethyl ammonium (PEA), methoxy phenethyl ammonium (MePEA), and 4‐fluoro phenethyl ammonium (4FPEA), the band edges of quasi‐2D perovskites are tuned without affecting their band gaps. Detailed characterization and computational studies have confirmed the effect of dipole moment modification to be mostly electrostatic, resulting in changes in the ionization energies of ≈0.45 eV for MePEA and ≈ −0.65 eV for 4FPEA based thin films relative to PEA‐based thin films. With improved charge balance, blue PeLEDs based on MePEA quasi‐2D perovskites show twofold increase of the EQE as compared to the control PEA based devices.

 
more » « less
Award ID(s):
1912911
NSF-PAR ID:
10446527
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Functional Materials
Volume:
31
Issue:
45
ISSN:
1616-301X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    While there has been extensive investigation into modulating quasi‐2D perovskite compositions in light‐emitting diodes (LEDs) for promoting their electroluminescence, very few reports have studied approaches involving enhancement of the energy transfer between quasi‐2D perovskite layers of the film, which plays very important role for achieving high‐performance perovskite LEDs (PeLEDs). In this work, a bifunctional ligand of 4‐(2‐aminoethyl)benzoic acid (ABA) cation is strategically introduced into the perovskite to diminish the weak van der Waals gap between individual perovskite layers for promoting coupled quasi‐2D perovskite layers. In particular, the strengthened interaction between coupled quasi‐2D perovskite layers favors an efficient energy transfer in the perovskite films. The introduced ABA can also simultaneously passivate the perovskite defects by reducing metallic Pb for less nonradiative recombination loss. Benefiting from the advanced properties of ABA incorporated perovskites, highly efficient blue PeLEDs with external quantum efficiency of 10.11% and a very long operational stability of 81.3 min, among the best performing blue quasi‐2D PeLEDs, are achieved. Consequently, this work contributes an effective approach for high‐performance and stable blue PeLEDs toward practical applications.

     
    more » « less
  2. Abstract

    Quasi‐2D Ruddlesden–Popper halide perovskites with a large exciton binding energy, self‐assembled quantum wells, and high quantum yield draw attention for optoelectronic device applications. Thin films of these quasi‐2D perovskites consist of a mixture of domains having different dimensionality, allowing energy funneling from lower‐dimensional nanosheets (high‐bandgap domains) to 3D nanocrystals (low‐bandgap domains). High‐quality quasi‐2D perovskite (PEA)2(FA)3Pb4Br13films are fabricated by solution engineering. Grazing‐incidence wide‐angle X‐ray scattering measurements are conducted to study the crystal orientation, and transient absorption spectroscopy measurements are conducted to study the charge‐carrier dynamics. These data show that highly oriented 2D crystal films have a faster energy transfer from the high‐bandgap domains to the low‐bandgap domains (<0.5 ps) compared to the randomly oriented films. High‐performance light‐emitting diodes can be realized with these highly oriented 2D films. Finally, amplified spontaneous emission with a low threshold 4.16 µJ cm−2is achieved and distributed feedback lasers are also demonstrated. These results show that it is important to control the morphology of the quasi‐2D films to achieve efficient energy transfer, which is a critical requirement for light‐emitting devices.

     
    more » « less
  3. Abstract

    Blue electroluminescence is highly desired for emerging light‐emitting devices for display applications and optoelectronics in general. However, saturated, efficient, and stable blue emission has been challenging to achieve, particularly in mixed‐halide perovskites, where intrinsic ion motion and halide segregation compromises spectral purity. Here, CsPbBr3−xClxperovskites, polyelectrolytes, and a salt additive are leveraged to demonstrate pure blue emission from single‐layer light‐emitting electrochemical cells (LECs). The electrolytes transport the ions from salt additives, enhancing charge injection and stabilizing the inherent perovskite emissive lattice for highly pure and sustained blue emission. Substituting Cl into CsPbBr3tunes the perovskite luminescence from green through blue. Sky blue and saturated blue devices produce International Commission on Illumination coordinates of (0.105, 0.129) and (0.136, 0.068), respectively, with the latter meeting the US National Television Committee standard for the blue primary. Likewise, maximum luminances of 2900 and 1000 cd m−2, external quantum efficiencies (EQEs) of 4.3% and 3.9%, and luminance half‐lives of 5.7 and 4.9 h are obtained for sky blue and saturated blue devices, respectively. Polymer and LiPF6inclusion increases photoluminescence efficiency, suppresses halide segregation, induces thin‐film smoothness and uniformity, and reduces crystallite size. Overall, these devices show superior performance among blue perovskite light‐emitting diodes (PeLEDs) and general LECs.

     
    more » « less
  4. Abstract

    Metal halide perovskites have witnessed great success in green, red, and near‐infrared light‐emitting diodes (LEDs), yet blue LEDs still lag behind. Reducing undesired energetic disorders – broadn‐phases and halide segregation – is considered as the most critical strategy to further improve the performances. Here, the study reports a newly designed and synthesized di‐ammonium ligand with rigidπ‐conjugated rings and additional methyl groups to construct Dion–Jacobson (DJ) structure. Augmented coordination from the extra ammonium site and increased effective bulkiness from methyl groups lead to better distribution control over conventional mono‐ammonium ligands. This enhances the radiative recombination of blue emissions in the film with homogeneous energy landscape and improved surface morphology, as evidenced by a series of imaging and mapping techniques. As a result, it demonstrates DJ perovskite LEDs (PeLEDs) with peak external quantum efficiencies of ≈4% at 484 nm and ≈11% at 494 nm, which are among the top reported for pure DJ phase‐based PeLEDs in the corresponding wavelength regions. The results deepen the understanding of regulating energetic disorders in perovskite materials via molecular engineering.

     
    more » « less
  5. Abstract

    Perovskite light‐emitting diodes (LEDs) have recently attracted great research interest for their narrow emissions and solution processability. Remarkable progress has been achieved in green perovskite LEDs in recent years, but not blue or red ones. Here, highly efficient and spectrally stable red perovskite LEDs with quasi‐2D perovskite/poly(ethylene oxide) (PEO) composite thin films as the light‐emitting layer are reported. By controlling the molar ratios of organic salt (benzylammonium iodide) to inorganic salts (cesium iodide and lead iodide), luminescent quasi‐2D perovskite thin films are obtained with tunable emission colors from red to deep red. The perovskite/polymer composite approach enables quasi‐2D perovskite/PEO composite thin films to possess much higher photoluminescence quantum efficiencies and smoothness than their neat quasi‐2D perovskite counterparts. Electrically driven LEDs with emissions peaked at 638, 664, 680, and 690 nm have been fabricated to exhibit high brightness and external quantum efficiencies (EQEs). For instance, the perovskite LED with an emission peaked at 680 nm exhibits a brightness of 1392 cd m−2and an EQE of 6.23%. Moreover, exceptional electroluminescence spectral stability under continuous device operation has been achieved for these red perovskite LEDs.

     
    more » « less