Flexible and low-cost poly(ethylene oxide) (PEO)-based electrolytes are promising for all-solid-state Li-metal batteries because of their compatibility with a metallic lithium anode. However, the low room-temperature Li-ion conductivity of PEO solid electrolytes and severe lithium-dendrite growth limit their application in high-energy Li-metal batteries. Here we prepared a PEO/perovskite Li 3/8 Sr 7/16 Ta 3/4 Zr 1/4 O 3 composite electrolyte with a Li-ion conductivity of 5.4 × 10 −5 and 3.5 × 10 −4 S cm −1 at 25 and 45 °C, respectively; the strong interaction between the F − of TFSI − (bis-trifluoromethanesulfonimide) and the surface Ta 5+ of the perovskite improves the Li-ion transport at the PEO/perovskite interface. A symmetric Li/composite electrolyte/Li cell shows an excellent cyclability at a high current density up to 0.6 mA cm −2 . A solid electrolyte interphase layer formed in situ between the metallic lithium anode and the composite electrolyte suppresses lithium-dendrite formation and growth. All-solid-state Li|LiFePO 4 and high-voltage Li|LiNi 0.8 Mn 0.1 Co 0.1 O 2 batteries with the composite electrolyte have an impressive performance with high Coulombic efficiencies, small overpotentials, and good cycling stability.
more »
« less
NASICON Li 1.2 Mg 0.1 Zr 1.9 (PO 4 ) 3 Solid Electrolyte for an All‐Solid‐State Li‐Metal Battery
A thin solid electrolyte with a high Li+conductivity is used to separate the metallic lithium anode and the cathode in an all‐solid‐state Li‐metal battery. However, most solid Li‐ion electrolytes have a small electrochemical stability window, large interfacial resistance, and cannot block lithium‐dendrite growth when lithium is plated on charging of the cell. Mg2+stabilizes a rhombohedral NASICON‐structured solid electrolyte of the formula Li1.2Mg0.1Zr1.9(PO4)3(LMZP). This solid electrolyte has Li‐ion conductivity two orders of magnitude higher at 25 °C than that of the triclinic LiZr2(PO4)3.7Li and6Li NMR confirm the Li‐ions in two different crystallographic sites of the NASICON framework with 85% of the Li‐ions having a relatively higher mobility than the other 15%. The anode–electrolyte interface is further investigated with symmetric Li/LMZP/Li cell testing, while the cathode–electrolyte interface is explored with an all‐solid‐state Li/LMZP/LiFePO4cell. The enhanced performance of these cells enabled by the Li1.2Mg0.1Zr1.9(PO4)3solid electrolyte is stable upon repeated charge/discharge cycling.
more » « less- Award ID(s):
- 1808517
- NSF-PAR ID:
- 10455736
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Small Methods
- Volume:
- 4
- Issue:
- 12
- ISSN:
- 2366-9608
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
more » « less
Abstract Solid‐state lithium metal batteries with garnet‐type electrolyte provide several advantages over conventional lithium‐ion batteries, especially for safety and energy density. However, a few grand challenges such as the propagation of Li dendrites, poor interfacial contact between the solid electrolyte and the electrodes, and formation of lithium carbonate during ambient exposure over the solid‐state electrolyte prevent the viability of such batteries. Herein, an ultrathin sub‐nanometer porous carbon nanomembrane (CNM) is employed on the surface of solid‐state electrolyte (SSE) that increases the adhesion of SSE with electrodes, prevents lithium carbonate formation over the surface, regulates the flow of Li‐ions, and blocks any electronic leakage. The sub‐nanometer scale pores in CNM allow rapid permeation of Li‐ions across the electrode–electrolyte interface without the presence of any liquid medium. Additionally, CNM suppresses the propagation of Li dendrites by over sevenfold up to a current density of 0.7 mA cm−2and enables the cycling of all‐solid‐state batteries at low stack pressure of 2 MPa using LiFePO4cathode and Li metal anode. The CNM provides chemical stability to the solid electrolyte for over 4 weeks of ambient exposure with less than a 4% increase in surface impurities.
-
more » « less
Abstract Solid‐state electrolytes (SEs) with high anodic (oxidation) stability are essential for achieving all‐solid‐state Li‐ion batteries (ASSLIBs) operating at high voltages. Until now, halide‐based SEs have been one of the most promising candidates due to their compatibility with cathodes and high ionic conductivity. However, the developed chloride and bromide SEs still show limited electrochemical stability that is inadequate for ultrahigh voltage operations. Herein, this challenge is addressed by designing a dual‐halogen Li‐ion conductor: Li3InCl4.8F1.2. F is demonstrated to selectively occupy a specific lattice site in a solid superionic conductor (Li3InCl6) to form a new dual‐halogen solid electrolyte (DHSE). With the incorporation of F, the Li3InCl4.8F1.2DHSE becomes dense and maintains a room‐temperature ionic conductivity over 10−4S cm−1. Moreover, the Li3InCl4.8F1.2DHSE exhibits a practical anodic limit over 6 V (vs Li/Li+), which can enable high‐voltage ASSLIBs with decent cycling. Spectroscopic, computational, and electrochemical characterizations are combined to identify a rich F‐containing passivating cathode‐electrolyte interface (CEI) generated in situ, thus expanding the electrochemical window of Li3InCl4.8F1.2DHSE and preventing the detrimental interfacial reactions at the cathode. This work provides a new design strategy for the fast Li‐ion conductors with high oxidation stability and shows great potential to high‐voltage ASSLIBs.
-
more » « less
Abstract A major challenge for lithium‐containing electrochemical systems is the formation of lithium carbonates. Solid‐state electrolytes circumvent the use of organic liquids that can generate these species, but they are still susceptible to Li2CO3formation from exposure to water vapor and carbon dioxide. It is reported here that trace quantities of Li2CO3, which are re‐formed following standard mitigation and handling procedures, can decompose at high charging potentials and degrade the electrolyte–cathode interface. Operando electrochemical mass spectrometry (EC–MS) is employed to monitor the outgassing of solid‐state batteries containing the garnet electrolyte Li7La3Zr2O12(LLZO) and using appropriate controls CO2and O2are identified to emanate from the electrolyte–cathode interface at charging potentials > 3.8 V (vs Li/Li+). The gas evolution is correlated with a large increase in cathode interfacial resistance observed by potential‐resolved impedance spectroscopy. This is the first evidence of electrochemical decomposition of interfacial Li2CO3in garnet cells and suggests a need to report “time‐to‐assembly” for cell preparation methods.
-
more » « less
Abstract NASICON‐type sodium vanadium phosphate (Na3V2(PO4)3, or NVP) cathode materials have great potential for fast charging and long cycling sodium‐ion batteries (SIBs) similar to lithium iron phosphate (LiFePO4, or LFP) cathode materials used in lithium‐ion batteries (LIBs). However, the cycle life and energy density in the full cell using NVP materials need to be significantly improved. This paper investigates the degradation mechanisms of NVP‐based SIBs and identifies the Na loss from the cathode to the anode solid electrolyte interphase (SEI) reactions as the main cause of capacity degradation. A new Na‐rich NVP cathode (e.g., Na4V2(PO4)3, or Na4VP) is developed to address the Na loss problem. Conventional NVP can be easily transformed into the Na4VP by a facile and fast chemical solution treatment (30 s). Na‐free‐anode Na4VP and hard carbon‐Na4VP full cells are assembled to evaluate the electrochemical properties of the Na‐rich NVP cathode. The Na4VP cathode provides excess Na to compensate for the Na loss, resulting much longer cycle life in the full cells (>400 cycles) and a high specific energy and power density. Good low‐temperature performance is also observed.