Title: Artificial neural networks and phenomenological degradation models for fatigue damage tracking and life prediction in laser induced graphene interlayered fiberglass composites
The mechanical properties of fiber reinforced polymer matrix composites are known to gradually deteriorate as fatigue damage accumulates under cyclic loading conditions. While the steady degradation in elastic stiffness throughout fatigue life is a well-established and studied concept, it remains difficult to continuously monitor such structural changes during the service life of many dynamic engineering systems where composite materials are subjected to random and unexpected loading conditions. Recently, laser induced graphene (LIG) has been demonstrated to be a reliable, in-situ strain sensing and damage detection component in fiberglass composites under both quasi-static and dynamic loading conditions. This work investigates the potential of exploiting the piezoresistive properties of LIG interlayered fiberglass composites in order to formulate cumulative damage parameters and predict both damage progression and fatigue life using artificial neural networks (ANNs) and conventional phenomenological models. The LIG interlayered fiberglass composites are subjected to tension–tension fatigue loading, while changes in their elastic stiffness and electrical resistance are monitored through passive measurements. Damage parameters that are defined according to changes in electrical resistance are found to be capable of accurately describing damage progression in LIG interlayered fiberglass composites throughout fatigue life, as they display similar trends to those based on changes in elastic stiffness. These damage parameters are then exploited for predicting the fatigue life and future damage state of fiberglass composites using both trained ANNs and phenomenological degradation and accumulation models in both specimen-to-specimen and cycle-to-cycle schemes. When used in a specimen-to-specimen scheme, the predictions of a two-layer Bayesian regularized ANN with 40 neurons in each layer are found to be at least 60% more accurate than those of phenomenological degradation models, displaying R2 values greater than 0.98 and root mean square error (RMSE) values smaller than 10−3. A two-layer Bayesian regularized ANN with 25 neurons in each layer is also found to yield accurate predictions when used in a cycle-to-cycle scheme, displaying R2 values greater than 0.99 and RMSE values smaller than 2 × 10−4 once more than 30% of the initial measurements are used as inputs. The final results confirm that piezoresistive LIG interlayers are a promising tool for achieving accurate and continuous fatigue life predictions in multifunctional composite structures, specifically when coupled with machine learning algorithms such as ANNs.  more » « less
Award ID(s):
1762369
PAR ID:
10297129
Author(s) / Creator(s):
; ;
Date Published:
Journal Name:
Smart materials and structures
Volume:
30
Issue:
8
ISSN:
1361-665X
Page Range / eLocation ID:
085010
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. null (Ed.)
    The mechanical properties of fiber reinforced polymer matrix composites are known to gradually deteriorate as fatigue damage accumulates under cyclic loading conditions. While the steady degradation in elastic stiffness throughout fatigue life is a well-established and studied concept, it remains difficult to continuously monitor such structural changes during the service life of many dynamic engineering systems where composite materials are subjected to random and unexpected loading conditions. Recently, laser induced graphene (LIG) has been demonstrated to be a reliable, in-situ strain sensing and damage detection component in fiberglass composites under both quasi-static and dynamic loading conditions. This work investigates the potential of exploiting the piezoresistive properties of LIG interlayered fiberglass composites in order to formulate cumulative damage parameters and predict both damage progression and fatigue life using artificial neural networks (ANNs) and conventional phenomenological models. The LIG interlayered fiberglass composites are subjected to tension–tension fatigue loading, while changes in their elastic stiffness and electrical resistance are monitored through passive measurements. Damage parameters that are defined according to changes in electrical resistance are found to be capable of accurately describing damage progression in LIG interlayered fiberglass composites throughout fatigue life, as they display similar trends to those based on changes in elastic stiffness. These damage parameters are then exploited for predicting the fatigue life and future damage state of fiberglass composites using both trained ANNs and phenomenological degradation and accumulation models in both specimen-to-specimen and cycle-to-cycle schemes. When used in a specimen-to-specimen scheme, the predictions of a two-layer Bayesian regularized ANN with 40 neurons in each layer are found to be at least 60% more accurate than those of phenomenological degradation models, displaying R2 values greater than 0.98 and root mean square error (RMSE) values smaller than 10−3. A two-layer Bayesian regularized ANN with 25 neurons in each layer is also found to yield accurate predictions when used in a cycle-to-cycle scheme, displaying R2 values greater than 0.99 and RMSE values smaller than 2 × 10−4 once more than 30% of the initial measurements are used as inputs. The final results confirm that piezoresistive LIG interlayers are a promising tool for achieving accurate and continuous fatigue life predictions in multifunctional composite structures, specifically when coupled with machine learning algorithms such as ANNs. 
    more » « less
  2. null (Ed.)
    Fiberglass-reinforced composite materials are commonly used in engineering structures subjected to dynamic loading, such as wind turbine blades, automobiles, and aircraft, where they experience a wide range of unpredictable operating conditions. The ability to monitor these structures while in operation and predict their remaining structural life without requiring their removal from service has the potential to drastically reduce maintenance costs and improve reliability. This work exploits piezoresistive laser induced graphene (LIG) integrated into fiberglass-reinforced composites for in-situ fatigue damage monitoring and lifespan prediction. The LIG is integrated within fiberglass composites using a transfer-printing process that is scalable with the potential for automation, thus reducing barriers for widespread application. The addition of the conductive LIG within the traditionally insulating fiberglass composites enables direct in-situ damage monitoring through simple passive resistance measurements during tension-tension fatigue loading. The accumulation and propagation of structural damage are detected throughout the fatigue life of the composite through changes to the electrical resistance measurements, and the measurement trends are further used to predict the onset of catastrophic composite failure. Thus, this work results in a scalable and multifunctional composite material with self-sensing capabilities for potential use in high-performing, dynamic, and flexible composite structures. 
    more » « less
  3. null (Ed.)
    Current in situ piezoresistive damage detection techniques for fiberglass-reinforced composites are limited in widespread application as they require complex processing techniques which inhibit the scalability of the methods. To eradicate such challenges and expand the use of piezoresistive monitoring of fiberglass composites, this work utilizes a simple, scalable process to coat electrically insulating commercial fiberglass prepreg with piezoresistive laser induced graphene (LIG) for the detection and localization of damage. Recently, LIG has attracted substantial research attention due to the simplicity of the methodology and the piezoresistance of the LIG. Here, the LIG is transfer printed onto commercial fiberglass prepreg which is subsequently used to localize damage in all three dimensions of the resultant fiberglass-reinforced composites while also maintaining the structural properties of the composites. A combination of in situ and ex-situ resistance measurements are used to accomplish this objective: First, in situ measurements are used to determine the relative location of damage in one-dimension under tensile loading. Subsequently, separate in situ measurements are used to locate damage through the thickness under flexural loading. Finally, ex-situ methods are used to calculate the two-dimensional location of a hole in a plate. The LIG is found to reliably and accurately localize the damage to the composite in each case thus demonstrating for the first time that transfer printed LIG enables self-sensing of damage location in fiberglass composites. The result of this work is thus a multifunctional material capable of locating damage in all three-dimensions which is notably fabricated using commercial materials and scalable methodology. 
    more » « less
  4. null (Ed.)
    Structural health monitoring of fiber-reinforced composite materials is of critical importance due to their use in challenging structural applications where low density is required and the designs typically use a low factor of safety. In order to reduce the need for external sensors to monitor composite structures, recent attention has turned to multifunctional materials with integrated sensing capabilities. This work use laser induced graphene (LIG) to create multifunctional structure with embedded piezoresistivity for the simultaneous and in-situ monitoring of both strain and damage in fiberglass-reinforced composites. The LIG layers are integrated during the fabrication process through transfer printing to the surface of the prepreg before being laid up into the ply stack, and are thus located in the interlaminar region of the fiberglass-reinforced composite. The methods used in this work are simple and require no treatment or modification to the commercial fiberglass prepreg prior to LIG transfer printing which is promising for industrial scale use. The performance of the piezoresistive interlayer in monitoring both strain and damage in-situ are demonstrated via three-point bend and tensile testing. Additionally, the interlaminar properties of the fiberglass composites were observed to be largely maintained with the LIG present in the interlaminar region of the composite, while the damping properties were found to be improved. This work therefore introduces a novel multifunctional material with high damping and fully integrated sensing capabilities through a cost-effective and scalable process. 
    more » « less
  5. Structural health monitoring of fiber-reinforced composite materials is of critical importance due to their use in challenging structural applications where low density is required and the designs typically use a low factor of safety. In order to reduce the need for external sensors to monitor composite structures, recent attention has turned to multifunctional materials with integrated sensing capabilities. This work use laser induced graphene (LIG) to create multifunctional structure with embedded piezoresistivity for the simultaneous and in-situ monitoring of both strain and damage in fiberglass-reinforced composites. The LIG layers are integrated dur-ing the fabrication process through transfer printing to the surface of the prepreg before being laid up into the ply stack, and are thus located in the interlaminar region of the fiberglass-reinforced composite. The methods used in this work are simple and require no treatment or modification to the commercial fiberglass prepreg prior to LIG transfer printing which is promising for industrial scale use. The performance of the piezoresistive interlayer in monitoring both strain and damage in-situ are demonstrated via three-point bend and tensile testing. Addi-tionally, the interlaminar properties of the fiberglass composites were observed to be largely maintained with the LIG present in the interlaminar region of the composite, while the damping properties were found to be improved. This work therefore introduces a novel multifunctional material with high damping and fully inte-grated sensing capabilities through a cost-effective and scalable process. 
    more » « less