“Anode‐free” solid‐state batteries (SSBs), which have no anode active material, can exhibit extremely high energy density (≈1500 Wh L−1). However, there is a lack of understanding of the lithium plating/stripping mechanisms at initially lithium‐free solid‐state electrolyte (SSE) interfaces because excess lithium metal is often used. Here, it is demonstrated that commercially relevant quantities of lithium (>5 mAh cm−2) can be reliably plated at moderate current densities (1 mA cm−2) using the sulfide SSE Li6PS5Cl. Investigations of lithium plating/stripping mechanisms, in conjunction with cryo‐focused ion beam (FIB) imaging, synchrotron tomography, and phase‐field modeling, reveal that the cycling stability of these cells is fundamentally limited by the nonuniform presence of lithium during stripping. Local lithium depletion causes isolated lithium regions toward the end of stripping, decreasing electrochemically active area and resulting in high local current densities and void formation. This accelerates subsequent filament growth and short circuiting compared to lithium‐excess cells. Despite this degradation mode, it is shown that anode‐free cells exhibit comparable Coulombic efficiency to lithium‐excess cells, and improved resistance to short circuiting is achieved by avoiding local lithium depletion through retention of thicker lithium at the interface. These new insights provide a foundation for engineering future high‐energy anode‐free SSBs.
The solid–solid electrode–electrolyte interface represents an important component in solid‐state batteries (SSBs), as ionic diffusion, reaction, transformation, and restructuring could all take place. As these processes strongly influence the battery performance, studying the evolution of the solid–solid interfaces, particularly in situ during battery operation, can provide insights to establish the structure–property relationship for SSBs. Synchrotron X‐ray techniques, owing to their unique penetration power and diverse approaches, are suitable to investigate the buried interfaces and examine structural, compositional, and morphological changes. In this review, we will discuss various surface‐sensitive synchrotron‐based scattering, spectroscopy, and imaging methods for the in situ characterization of solid–solid interfaces and how this information can be correlated to the electrochemical properties of SSBs. The goal is to overview the advantages and disadvantages of each technique by highlighting representative examples, so that similar strategies can be applied by battery researchers and beyond to study similar solid‐solid interface systems.
more » « less- NSF-PAR ID:
- 10304912
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Carbon Energy
- Volume:
- 3
- Issue:
- 5
- ISSN:
- 2637-9368
- Page Range / eLocation ID:
- p. 762-783
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract As solid‐state batteries (SSBs) with lithium (Li) metal anodes gain increasing traction as promising next‐generation energy storage systems, a fundamental understanding of coupled electro‐chemo‐mechanical interactions is essential to design stable solid‐solid interfaces. Notably, uneven electrodeposition at the Li metal/solid electrolyte (SE) interface arising from intrinsic electrochemical and mechanical heterogeneities remains a significant challenge. In this work, the thermodynamic origins of mechanics‐coupled reaction kinetics at the Li/SE interface are investigated and its implications on electrodeposition stability are unveiled. It is established that the mechanics‐driven energetic contribution to the free energy landscape of the Li deposition/dissolution redox reaction has a critical influence on the interface stability. The study presents the competing effects of mechanical and electrical overpotential on the reaction distribution, and demarcates the regimes under which stress interactions can be tailored to enable stable electrodeposition. It is revealed that different degrees of mechanics contribution to the forward (dissolution) and backward (deposition) reaction rates result in widely varying stability regimes, and the mechanics‐coupled kinetics scenario exhibited by the Li/SE interface is shown to depend strongly on the thermodynamic and mechanical properties of the SE. This work highlights the importance of discerning the underpinning nature of electro‐chemo‐mechanical coupling toward achieving stable solid/solid interfaces in SSBs.
-
more » « less
Abstract Solid‐state batteries (SSBs), utilizing a lithium metal anode, promise to deliver enhanced energy and power densities compared to conventional lithium‐ion batteries. Penetration of lithium filaments through the solid‐state electrolytes (SSEs) during electrodeposition poses major constraints on the safety and rate performance of SSBs. While microstructural attributes, especially grain boundaries (GBs) within the SSEs are considered preferential metal propagation pathways, the underlying mechanisms are not fully understood yet. Here, a comprehensive insight is presented into the mechanistic interactions at the mesoscale including the electrochemical‐mechanical response of the GB‐electrode junction and competing ion transport dynamics in the SSE. Depending on the GB transport characteristics, a highly non‐uniform electrodeposition morphology consisting of either cavities or protrusions at the GB‐electrode interface is identified. Mechanical stability analysis reveals localized strain ramps in the GB regions that can lead to brittle fracture of the SSE. For ionically less conductive GBs compared to the grains, a crack formation and void filling mechanism, triggered by the heterogeneous nature of electrochemical‐mechanical interactions is delineated at the GB‐electrode junction. Concurrently, in situ X‐ray tomography of pristine and failed Li7La3Zr2O12(LLZO) SSE samples confirm the presence of filamentous lithium penetration and validity of the proposed mesoscale failure mechanisms.
-
Electrification of the transportation sector relies on radical re-imagining of energy storage technologies to provide affordable, high energy density, durable and safe systems. Next generation energy storage systems will need to leverage high energy density anodes and high voltage cathodes to achieve the required performance metrics (longer vehicle range, long life, production costs, safety). Solid-state batteries (SSBs) are promising materials technology for achieving these metrics by enabling these electrode systems due to the underlying material properties of the solid electrolyte ( viz. mechanical strength, electrochemical stability, ionic conductivity). Electro-chemo-mechanical degradation in SSBs detrimentally impact the Coulombic efficiencies, capacity retention, durability and safety in SSBs restricting their practical implementation. Solid|solid interfaces in SSBs are hot-spots of dynamics that contribute to the degradation of SSBs. Characterizing and understanding the processes at the solid|solid interfaces in SSBs is crucial towards designing of resilient, durable, high energy density SSBs. This work provides a comprehensive and critical summary of the SSB characterization with a focus on in situ and operando studies. Additionally, perspectives on experimental design, emerging characterization techniques and data analysis methods are provided. This work provides a thorough analysis of current status of SSB characterization as well as highlights important avenues for future work.more » « less
-
Solid-state-batteries (SSBs) present a promising technology for next-generation batteries due to their superior properties including increased energy density, wider electrochemical window and safer electrolyte design. Commercialization of SSBs, however, will depend on the resolution of a number of critical chemical and mechanical stability issues. The resolution of these issues will in turn depend heavily on our ability to accurately model these systems such that appropriate material selection, microstructure design, and operational parameters may be determined. In this article we review the current state-of-the art modeling tools with a focus on chemo-mechanics. Some of the key chemo-mechanical problems in SSBs involve dendrite growth through the solid-state electrolyte (SSE), interphase formation at the anode/SSE interface, and damage/decohesion of the various phases in the solid-state composite cathode. These mechanical processes in turn lead to capacity fade, impedance increase, and short-circuit of the battery, ultimately compromising safety and reliability. The article is divided into the three natural components of an all-solid-state architecture. First, modeling efforts pertaining to Li-metal anodes and dendrite initiation and growth mechanisms are reviewed, making the transition from traditional liquid electrolyte anodes to next generation all-solid-state anodes. Second, chemo-mechanics modeling of the SSE is reviewed with a particular focus on the formation of a thermodynamically unstable interphase layer at the anode/SSE interface. Finally, we conclude with a review of chemo-mechanics modeling efforts for solid-state composite cathodes. For each of these critical areas in a SSB we conclude by highlighting the key open areas for future research as it pertains to modeling the chemo-mechanical behavior of these systems.more » « less