Title: Reviving the “Schottky” Barrier for Flexible Polymer Dielectrics with a Superior 2D Nanoassembly Coating
Abstract

The organic insulator–metal interface is the most important junction in flexible electronics. The strong band offset of organic insulators over the Fermi level of electrodes should theoretically impart a sufficient impediment for charge injection known as the Schottky barrier. However, defect formation through Anderson localization due to topological disorder in polymers leads to reduced barriers and hence cumbersome devices. A facile nanocoating comprising hundreds of highly oriented organic/inorganic alternating nanolayers is self‐coassembled on the surface of polymer films to revive the Schottky barrier. Carrier injection over the enhanced barrier is further shunted by anisotropic 2D conduction. This new interface engineering strategy allows a significant elevation of the operating field for organic insulators by 45% and a 7× improvement in discharge efficiency for Kapton at 150 °C. This superior 2D nanocoating thus provides a defect‐tolerant approach for effective reviving of the Schottky barrier, one century after its discovery, broadly applicable for flexible electronics.

 
more » « less
Award ID(s):
1726862
NSF-PAR ID:
10449365
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Materials
Volume:
33
Issue:
34
ISSN:
0935-9648
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Gate‐/wavelength‐dependent scanning photocurrent measurements of black phosphorous (BP)–MoS2heterojunctions have shown that the Schottky barrier at the MoS2–metal interface plays an important role in the photoresponse dynamics of the heterojunction. When the Fermi level is close to the conduction band of MoS2, photoexcited carriers can tunnel through the narrow depletion region at the MoS2–metal interface, leading to a short response time of 13 µs regardless of the incident laser wavelength. This response speed is comparable or better than that of other few‐layer BP–MoS2heterojunctions. Conversely, when the MoS2channel is in the off‐state, the resulting sizeable Schottky barrier and depletion width make it difficult for photoexcited carriers to overcome the barrier. This significantly delays the carrier transit time and thus the photoresponse speed, leading to a wavelength‐dependent response time since the photoexcited carriers induced by short wavelength photons have a higher probability to overcome the Schottky barrier at the MoS2–metal interface than long wavelength photons. These studies not only shed light on the fundamental understanding of photoresponse dynamics in BP–MoS2heterojunctions, but also open new avenues for engineering the interfaces between 2D materials and metal contacts to reduce the response time of 2D optoelectronics.

     
    more » « less
  2. Abstract

    Organic permeable‐base transistors (OPBTs) show potential for high‐speed, flexible electronics. Scaling laws of OPBTs are discussed and it is shown that OPBT performance can be increased by reducing their effective device area. Comparing the performance of optimized OPBTs with state‐of‐the‐art organic field‐effect transistors (OFETs), it is shown that OPBTs have a higher potential for an increased transit frequency. Not only do OPBTs reach higher transconductance values without the need for sophisticated structuring techniques, but they are also less sensitive to parasitic contact resistances. With the help of a 2D numerical model, the reduced contact resistances of OPBTs are explained by a homogeneous injection of current across the entire emitter electrode, compared to injection in a small area along the edge of the source of OFETs.

     
    more » « less
  3. Abstract

    The performance of electronic/optoelectronic devices is governed by carrier injection through metal–semiconductor contact; therefore, it is crucial to employ low‐resistance source/drain contacts. However, unintentional introduction of extrinsic defects, such as substoichiometric oxidation states at the metal–semiconductor interface, can degrade carrier injection. In this report, controlling the unintentional extrinsic defect states in layered MoS2is demonstrated using a two‐step chemical treatment, (NH4)2S(aq) treatment and vacuum annealing, to enhance the contact behavior of metal/MoS2interfaces. The two‐step treatment induces changes in the contact of single layer MoS2field effect transistors from nonlinear Schottky to Ohmic behavior, along with a reduction of contact resistance from 35.2 to 5.2 kΩ. Moreover, the enhancement ofIONand electron field effect mobility of single layer MoS2field effect transistors is nearly double forn‐branch operation. This enhanced contact behavior resulting from the two‐step treatment is likely due to the removal of oxidation defects, which can be unintentionally introduced during synthesis or fabrication processes. The removal of oxygen defects is confirmed by scanning tunneling microscopy and X‐ray photoelectron spectroscopy. This two‐step (NH4)2S(aq) chemical functionalization process provides a facile pathway to controlling the defect states in transition metal dichalcogenides (TMDs), to enhance the metal‐contact behavior of TMDs.

     
    more » « less
  4. Phase pure PbZr 0.52 Ti 0.48 O 3 (PZT) films with up to 13 mol. % Nb were prepared on Pt-coated Si substrates using chemical solution deposition; charge compensation for Nb was accomplished by reducing the concentration of lead in the film. For high Nb doping levels, (1) superoxidation of the PZT film surface makes the PZT/Pt interface more p-type and, hence reduces electron injection over the Schottky barrier, (2) the bulk charge transport mechanism changes from electron trapping by Ti 4+ to hole migration between lead vacancies, and (3) the ionic conductivity due to migration of oxygen vacancies decreases. For [Formula: see text] Nb, electrical degradation was controlled via field-induced accumulation of oxygen vacancies near the cathode, which, in turn, leads to Schottky barrier lowering and electron trapping by Ti 4+ . In phase pure 13 mol. % Nb doped PZT films, on the other hand, the increase in the leakage current during electrical degradation was dominated by hole migration between lead vacancies ([Formula: see text]. A much lower lifetime and drastic increase in the leakage current upon electrical degradation was observed in mixed phase PNZT films, which was attributed to (1) a more electrically conductive pyrochlore phase and (2) a high concentration of lead vacancies. 
    more » « less
  5. Ultrawide bandgap β-(AlxGa1−x)2O3 vertical Schottky barrier diodes on (010) β-Ga2O3 substrates are demonstrated. The β-(AlxGa1−x)2O3 epilayer has an Al composition of 21% and a nominal Si doping of 2 × 1017 cm−3 grown by molecular beam epitaxy. Pt/Ti/Au has been employed as the top Schottky contact, whereas Ti/Au has been utilized as the bottom Ohmic contact. The fabricated devices show excellent rectification with a high on/off ratio of ∼109, a turn-on voltage of 1.5 V, and an on-resistance of 3.4 mΩ cm2. Temperature-dependent forward current-voltage characteristics show effective Schottky barrier height varied from 0.91 to 1.18 eV while the ideality factor from 1.8 to 1.1 with increasing temperatures, which is ascribed to the inhomogeneity of the metal/semiconductor interface. The Schottky barrier height was considered a Gaussian distribution of potential, where the extracted mean barrier height and a standard deviation at zero bias were 1.81 and 0.18 eV, respectively. A comprehensive analysis of the device leakage was performed to identify possible leakage mechanisms by studying temperature-dependent reverse current-voltage characteristics. At reverse bias, due to the large Schottky barrier height, the contributions from thermionic emission and thermionic field emission are negligible. By fitting reverse leakage currents at different temperatures, it was identified that Poole–Frenkel emission and trap-assisted tunneling are the main leakage mechanisms at high- and low-temperature regimes, respectively. Electrons can tunnel through the Schottky barrier assisted by traps at low temperatures, while they can escape these traps at high temperatures and be transported under high electric fields. This work can serve as an important reference for the future development of ultrawide bandgap β-(AlxGa1−x)2O3 power electronics, RF electronics, and ultraviolet photonics.

     
    more » « less