Title: Growth and characterization of (Sc 2 O 3 ) x (Ga 2 O 3 ) 1−x by molecular beam epitaxy
(Sc 2 O 3 ) x (Ga 2 O 3 ) 1−x was grown by molecular beam epitaxy at low temperatures (100 °C) using a variety of growth sequences to avoid surface segregation of Ga. Continuous and digital growth techniques always produced Ga segregation. This surface segregation was attributed to the stronger bond between the Sc and O compared to the Ga and O. A digital growth technique (alternate opening of Sc and Ga shutters with the O shutter open continuously during the growth) was unsuccessful in eliminating this effect. The segregation was eliminated using a growth technique in which the Ga shutter was closed for a set amount of time toward the end of the growth while the O and Sc shutters remained open. Characterization with reflection high energy electron diffraction, x-ray diffraction, and transmission electron microscopy revealed the growth of a fine-grained polycrystalline film under these conditions. A third growth technique was used that involved closing the Ga shutter for a set amount of time toward the end of the growth while the O and Sc shutters were open continuously. This technique was successful in depositing a uniform film. However, the breakdown field was only 1.40 MV/cm (at 1 mA/cm 2 ). The addition of Ga to Sc 2 O 3 diminished the insulating properties of the film. These initial experiments indicate that phase segregation is likely to be a major issue with most growth techniques and that alloying Ga 2 O 3 with elements other than Sc, such as Gd or Al, might be a more successful approach.  more » « less
Award ID(s):
1856662
NSF-PAR ID:
10327528
Author(s) / Creator(s):
; ; ; ;
Date Published:
Journal Name:
Journal of Vacuum Science & Technology A
Volume:
40
Issue:
4
ISSN:
0734-2101
Page Range / eLocation ID:
043403
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Growths of monoclinic (AlxGa1−x)2O3thin films up to 99% Al contents are demonstrated via metalorganic chemical vapor deposition (MOCVD) using trimethylgallium (TMGa) as the Ga precursor. The utilization of TMGa, rather than triethylgallium, enables a significant improvement of the growth rates (>2.5 μm h−1) of β‐(AlxGa1−x)2O3thin films on (010), (100), and (01) β‐Ga2O3substrates. By systematically tuning the precursor molar flow rates, growth of coherently strained phase pure β‐(AlxGa1−x)2O3films is demonstrated by comprehensive material characterizations via high‐resolution X‐ray diffraction (XRD) and atomic‐resolution scanning transmission electron microscopy (STEM) imaging. Monoclinic (AlxGa1−x)2O3films with Al contents up to 99, 29, and 16% are achieved on (100), (010), and (01) β‐Ga2O3substrates, respectively. Beyond 29% of Al incorporation, the (010) (AlxGa1−x)2O3films exhibit β‐ to γ‐phase segregation. β‐(AlxGa1−x)2O3films grown on (01) β‐Ga2O3show local segregation of Al along (100) plane. Record‐high Al incorporations up to 99% in monoclinic (AlxGa1−x)2O3grown on (100) Ga2O3are confirmed from XRD, STEM, electron nanodiffraction, and X‐ray photoelectron spectroscopy measurements. These results indicate great promises of MOCVD development of β‐(AlxGa1−x)2O3films and heterostructures with high Al content and growth rates using TMGa for next‐generation high‐power and high‐frequency electronic devices.

     
    more » « less
  2. The in situ metalorganic chemical vapor deposition (MOCVD) growth of Al 2 O 3 dielectrics on β-Ga 2 O 3 and β-(Al x Ga 1−x ) 2 O 3 films is investigated as a function of crystal orientations and Al compositions of β-(Al x Ga 1−x ) 2 O 3 films. The interface and film qualities of Al 2 O 3 dielectrics are evaluated by high-resolution x-ray diffraction and scanning transmission electron microscopy imaging, which indicate the growth of high-quality amorphous Al 2 O 3 dielectrics with abrupt interfaces on (010), (100), and [Formula: see text] oriented β-(Al x Ga 1−x ) 2 O 3 films. The surface stoichiometries of Al 2 O 3 deposited on all orientations of β-(Al x Ga 1−x ) 2 O 3 are found to be well maintained with a bandgap energy of 6.91 eV as evaluated by high-resolution x-ray photoelectron spectroscopy, which is consistent with the atomic layer deposited (ALD) Al 2 O 3 dielectrics. The evolution of band offsets at both in situ MOCVD and ex situ ALD deposited Al 2 O 3 /β-(Al x Ga 1−x ) 2 O 3 is determined as a function of Al composition, indicating the influence of the deposition method, orientation, and Al composition of β-(Al x Ga 1−x ) 2 O 3 films on resulting band alignments. Type II band alignments are determined at the MOCVD grown Al 2 O 3 /β-(Al x Ga 1−x ) 2 O 3 interfaces for the (010) and (100) orientations, whereas type I band alignments with relatively low conduction band offsets are observed along the [Formula: see text] orientation. The results from this study on MOCVD growth and band offsets of amorphous Al 2 O 3 deposited on differently oriented β-Ga 2 O 3 and β-(Al x Ga 1−x ) 2 O 3 films will potentially contribute to the design and fabrication of future high-performance β-Ga 2 O 3 and β-(Al x Ga 1−x ) 2 O 3 based transistors using MOCVD in situ deposited Al 2 O 3 as a gate dielectric. 
    more » « less
  3. SiC and Ga 2 O 3 are promising wide band gap semiconductors for applications in power electronics because of their high breakdown electric field and normally off operation. However, lack of a suitable dielectric material that can provide high interfacial quality remains a problem. This can potentially lead to high leakage current and conducting loss. In this work, we present a novel atomic layer deposition process to grow epitaxially Mg x Ca 1− x O dielectric layers on 4H-SiC(0001) and β-Ga 2 O 3 $\left( {\bar 201} \right)$ substrates. By tuning the composition of Mg x Ca 1− x O toward the substrate lattice constant, better interfacial epitaxy can be achieved. The interfacial and epitaxy qualities were investigated and confirmed by cross-sectional transmission electron microscopy and X-ray diffraction studies. Mg 0.72 Ca 0.28 O film showed the highest epitaxy quality on 4H-SiC(0001) because of its closest lattice match with the substrate. Meanwhile, highly textured Mg 0.25 Ca 0.75 O films can be grown on β-Ga 2 O 3 $\left( {\bar 201} \right)$ with a preferred orientation of (111). 
    more » « less
  4. Phase pure β-(Al x Ga 1−x ) 2 O 3 thin films are grown on (001) oriented β-Ga 2 O 3 substrates via metalorganic chemical vapor deposition. By systematically tuning the precursor molar flow rates, the epitaxial growth of coherently strained β-(Al x Ga 1−x ) 2 O 3 films is demonstrated with up to 25% Al compositions as evaluated by high resolution x-ray diffraction. The asymmetrical reciprocal space mapping confirms the growth of coherent β-(Al x Ga 1−x ) 2 O 3 films (x < 25%) on (001) β-Ga 2 O 3 substrates. However, the alloy inhomogeneity with local segregation of Al along the ([Formula: see text]) plane is observed from atomic resolution STEM imaging, resulting in wavy and inhomogeneous interfaces in the β-(Al x Ga 1−x ) 2 O 3 /β-Ga 2 O 3 superlattice structure. Room temperature Raman spectra of β-(Al x Ga 1−x ) 2 O 3 films show similar characteristics peaks as the (001) β-Ga 2 O 3 substrate without obvious Raman shifts for films with different Al compositions. Atom probe tomography was used to investigate the atomic level structural chemistry with increasing Al content in the β-(Al x Ga 1−x ) 2 O 3 films. A monotonous increase in chemical heterogeneity is observed from the in-plane Al/Ga distributions, which was further confirmed via statistical frequency distribution analysis. Although the films exhibit alloy fluctuations, n-type doping demonstrates good electrical properties for films with various Al compositions. The determined valence and conduction band offsets at β-(Al x Ga 1−x ) 2 O 3 /β-Ga 2 O 3 heterojunctions using x-ray photoelectron spectroscopy reveal the formation of type-II (staggered) band alignment. 