Title: Influence of substrate roughness on particle adhesion and concentration
In this research study, the interaction of particles with substrates of different roughness magnitude was investigated. Particle surface treatment, relative humidity (RH), and surface roughness levels were controlled in order to achieve separation of different particles by applying removal forces. Three different approaches to reproducibly roughen surfaces were used. Initially, glass disks were laser engraved to create a reproducible, controlled roughness substrate. However, the laser engraving method produced surface features that were much greater in scale than the particles. These scale differences were such that the substrates produced were not of value to this research. The second option investigated to induce reproducible substrate roughness was to scratch the glass disk using sandpapers of known grain size. A third approach to establish reproducible roughness was to use fine stainless-steel wire mesh substrates. In tests with sanded glass disks, the interfacial energy of plasma-cleaned (hydrophilic) glass beads had a high variation at 40% RH, showing non-uniformity of area of contact between particles and substrates. As the RH increased, it was expected that the interfacial energy of hydrophilic particles would increase, but this behavior was not observed. In addition, comparing the interfacial energy results of hydrophilic particles with hydrophobic particles, a region with significant interfacial energy difference was not identified. In the case of the stainless-steel mesh substrate, the mesh asperities and particle dimensions were comparable. Thus, the smaller particles had more area of contact with the substrate than the larger particles. For the plasma-cleaned (hydrophilic) beads, the recovery values had an average of 92.5% recovery when the RH was between 46 and 85%. For the hydrophobic beads, the average recovery was 19.0% when the RH was between 46 and 75%. Thus, the hydrophobic characteristic of the particle influenced its lower interaction with the mesh substrate. The difference in recovery can be exploited to achieve separation of particles based upon adhesive forces.  more » « less
Award ID(s):
1805550
NSF-PAR ID:
10333095
Author(s) / Creator(s):
Date Published:
Journal Name:
Mining metallurgy exploration
Volume:
39
ISSN:
2524-3470
Page Range / eLocation ID:
3-12
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ( , Powder technology)
    null (Ed.)
    The mineral industry uses tremendous amounts of water every year in the processing of ores. Sustainable practices associated with the processing of ores are, therefore, of critical importance. The project described herein is the first step toward producing a dry, particle-separation process based upon control and exploitation of adhesive forces. In this research, the goal is to determine the surface energy of particles, and further, whether the solid sur- face energy can be used to understand the adhesion between these particles and surface-modified substrates. Glass spheres were chosen to represent silicate minerals, the most abundant type of minerals found in mineral deposits. The solid surface energy was found by using contact angle measurements and by applying the van Oss-Good-Chaudhury (VOGC) method. The VOGC method utilizes three-liquid triads to determine the Lifshitz- van der Waals, Lewis acid and Lewis base surface energy components. Surface energies from plasma-cleaned glass were between 40.2 and 60.2 mJ/m2; for the same glass with a hydrophobic chemical surface treatment, trichloro(octadecyl)silane (TCOD), the surface energy was between 20.8 and 20.9 mJ/m2; and for the glass with a hydrophilic chemical surface treatment (n1-(3-trimethoxysilylpropyl) diethylenetriamine (TMPA)) the surface energy was between 46.3 and 61.6 mJ/m2. The particle-substrate adhesion was also measured using a mechanical impact tester. Glass disks and beads were used, cleaned and surface treated with TCOD and TMPA. A custom horizontal impact tester was designed and used to measure the adhesion force between the glass spheres and a glass disk substrate. Impact of the disk/particle puck causes particle removal as tensile forces act on the particles. The tensile detachment force and adhesive force are equal at a critical particle size. Johnson- Kendall-Roberts (JKR) theory was used to determine the interfacial energy between the particles and the surface. The average interfacial energy of plasma cleaned glass, glass treated with TCOD and with TMPA were 44.8 mJ/m2, 21.6 mJ/m2, and 40.1 mJ/m2, respectively. These values are in good agreement with the literature values and with the interfacial energy determined using the VOGC method described above, demonstrating that two approaches compare favorably, despite the dramatically different methods (molecular vs mechanical) utilized. 
    more » « less
  2. ; ; ; ( , Minerals engineering)
    null (Ed.)
    Many of the methods to classify and concentrate minerals and the subsequent extraction of metals takes place in water-based environments (aqueous solutions). Sustainable processing through the reduction of water consumption will become a key factor to make mining operations viable in the long term. In humid environments, capillary condensation of water can occur between the particle and substrate. The objective herein is to identify separation windows in which control of relative air humidity (RH) yields different substrate adhesion for hydrophilic and hydrophobic particles of different values of interfacial energy. Plasma cleaned glass beads, and trichloro(octadecyl)silane (TCOD) treated beads were poured on a plasma cleaned glass disk and an impact caused the detachment of particles. Impact tests performed under a range of RH showed that separation of plasma cleaned and TCOD treated particles can be achieved in 80% of the tests at humidity levels between 45% and 55%. The recovery of plasma cleaned particles was five times greater than TCOD treated particles at humidity levels between 50% and 55%. 
    more » « less
  3. ; ( , Proceedings of the ... International Conference on Nanochannels, Microchannels and Minichannels)
    Reduction of irrigation is a pressing issue in the food-water-energy nexus. Around two-third of global water withdrawals are used for irrigation in the areas with insufficient rainfall. In the U.S. Central High Plains, the Ogallala Aquifer is responsible for providing water for the production of corn, wheat, soybeans, andreducing the evaporation of water from soil provides an excellent opportunity to decrease the need for irrigation. In this paper, evaporation of sessile 4-μl water droplets from a single simulated soil pore was observed. Soil pores were created using three 2.35-mm hydrophilic glass or hydrophobic Teflon beads of the same size. The experiments were conducted at the same temperature (20° C) and two relative humidity levels, 45% and 60% RH. Evaporation times were recorded and the transport phenomena were captured using a high-speed camera. Relative humidity directly affected evaporation; evaporation times were lower at the lower RH. The glass surface had higher wettability and therefore the droplets were more stretched on the glass beads, more droplet-air areas were created and evaporation times were approximately 30 minutes at 60% RH. The Teflon surface was hydrophobic, for which air-water contact areas were lower, and evaporation times were longer – approximately 40 minutes at 60% RH. As evaporation progressed, a liquid island formed between two beads at both 45% and 60% RH in for glass and Teflon pores. The rate of decrease of the radius of the liquid island was shorter in Teflon than glass beads, which corresponded to lower evaporation rates from Teflon. 
    more » « less
  4. ; ; ; ( , Biomedical Sciences Instrumentation)
    Hydrophobic surfaces provide special characteristics for biomedical applications ranging from tunable protein adsorption, cellular interactions, and hemocompatibility to antibacterial coatings. In this research, we biomimic the hair-like micro-whisker structures of magnolia leaf using a synthetic polymeric formulation. Optical and scanning electron microscopy images revealed the presence of micro-whiskers resulting in higher water contact angles. The top layer of the magnolia leaf had a contact angle of 50º as compared to the hydrophobic bottom layer at 98º. A synthetic polymeric formulation was coated on different materials to study its effect on hydrophobicity. The coating was replicated (n=3) on each of the materials used such as glass, polymer, fabric, wood, and stainless steel. A surface tensiometer was used to measure the transition from hydrophilic to hydrophobic interactions between water and the substrate materials. Contact angle measurements revealed an increase in hydrophobicity for all the materials from their original uncoated surface. Glass displayed the highest increase in contact angle from 37º to 90º. Phase analysis of the coated region was performed to characterize the surface exposure of glass substrate to the synthetic polymeric formulation. An increase in the coated region showed a significant increase in contact angle from 50º to 95º. This research lays the foundation to develop and understand hydrophobic coatings for several biomedical applications including non-fouling implant surfaces, lab-on-chip devices, and other diagnostic tools. 
    more » « less
  5. ; ( , ASME 2020 18th International Conference on Nanochannels, Microchannels, and Minichannels collocated with the ASME 2020 Heat Transfer Summer Conference and the ASME 2020 Fluids Engineering Division Summer Meeting)
    Altering soil wettability by inclusion of hydrophobicity could be an effective way to restrict evaporation from soil, thereby conserving water resources. In this study, 4-μL sessile water droplets were evaporated from an artificial soil millipore comprised of three glass (i.e. hydrophilic) and Teflon (i.e. hydrophobic) 2.38-mm-diameter beads. The distance between the beads were kept constant (i.e. center-to-center spacing of 3.1 mm). Experiments were conducted in an environmental chamber at an air temperature of 20°C and 30% and 75% relative humidity (RH). Evaporation rates were faster (i.e. ∼19 minutes and ∼49 minutes at 30% and 75% RH) from hydrophilic pores than the Teflon one (i.e. ∼24 minutes and ∼52 minutes at 30% and 75% RH) due in part to greater air-water contact area. Rupture of liquid droplets during evaporation was analyzed and predictions were made on rupture based on contact line pinning and depinning, projected surface area just before rupture, and pressure difference across liquid-vapor interface. It was observed that, in hydrophilic pore, the liquid droplet was pinned on one bead and the contact line on the other beads continuously decreased by deforming the liquid-vapor interface, though all three gas-liquid-solid contact lines decreased at a marginal rate in hydrophobic pore. For hydrophilic and hydrophobic pores, approximately 1.7 mm2 and 1.8–2 mm2 projected area of the droplet was predicted at 30% and 75% RH just before rupture occurs. Associated pressure difference responsible for rupture was estimated based on the deformation of curvature of liquid-vapor interface. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email