Title: Wireless Humidity Sensor for Smart Packaging via One‐step Laser‐Induced Patterning and Nanoparticle Formation on Metallized Paper
Abstract

In this work, a scalable and rapid process is developed for creating a low‐cost humidity sensor for wireless monitoring of moisture levels within packaged goods. The sensor comprises a moisture‐sensitive interdigitated capacitor connected to a planar spiral coil, forming an LC circuit whose resonant frequency is a function of environmental humidity. The sensor is fabricated on a commercially available metallized parchment paper through selective laser ablation of the laminated aluminum (Al) film on the parchment paper substrate. The laser ablation process provides a unique one‐step patterning of the conductive Al layer on the paper while simultaneously creating high surface area Al2O3nanoparticles within the laser‐ablated regions. The intrinsic humidity‐responsive characteristics of the laser‐induced Al2O3nanostructures provide the wireless sensor with a tenfold higher sensitivity to humidity than a similar LC resonant sensor prepared by conventional photolithography‐based processes on FR‐4 substrates. The frequency change of the sensor is observed to be a linear function within the range of 0−85% RH, providing an average sensitivity of −87 kHz RH−1with good repeatability and stable performance. Furthermore, the employment of scalable laser fabrication processes using commercially available inexpensive materials renders these technologies viable for roll‐to‐roll manufacturing of low‐cost wireless sensors for smart packaging applications.

 
more » « less
Award ID(s):
1809520
NSF-PAR ID:
10445770
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Electronic Materials
Volume:
8
Issue:
7
ISSN:
2199-160X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. There has been an increasing need of technologies to manufacturing chemical and biological sensors for various applications ranging from environmental monitoring to human health monitoring. Currently, manufacturing of most chemical and biological sensors relies on a variety of standard microfabrication techniques, such as physical vapor deposition and photolithography, and materials such as metals and semiconductors. Though functional, they are hampered by high cost materials, rigid substrates, and limited surface area. Paper based sensors offer an intriguing alternative that is low cost, mechanically flexible, has the inherent ability to filter and separate analytes, and offers a high surface area, permeable framework advantageous to liquid and vapor sensing. However, a major drawback is that standard microfabrication techniques cannot be used in paper sensor fabrication. To fabricate sensors on paper, low temperature additive techniques must be used, which will require new manufacturing processes and advanced functional materials. In this work, we focus on using aerosol jet printing as a highresolution additive process for the deposition of ink materials to be used in paper-based sensors. This technique can use a wide variety of materials with different viscosities, including materials with high porosity and particles inherent to paper. One area of our efforts involves creating interdigitated microelectrodes on paper in a one-step process using commercially available silver nanoparticle and carbon black based conductive inks. Another area involves use of specialized filter papers as substrates, such as multi-layered fibrous membrane paper consisting of a poly(acrylonitrile) nanofibrous layer and a nonwoven poly(ethylene terephthalate) layer. The poly(acrylonitrile) nanofibrous layer are dense and smooth enough to allow for high resolution aerosol jet printing. With additively fabricated electrodes on the paper, molecularly-functionalized metal nanoparticles are deposited by molecularly-mediated assembling, drop casting, and printing (sensing and electrode materials), allowing full functionalization of the paper, and producing sensor devices with high surface area. These sensors, depending on the electrode configuration, are used for detection of chemical and biological species in vapor phase, such as water vapor and volatile organic compounds, making them applicable to human performance monitoring. These paper based sensors are shown to display an enhancement in sensitivity, as compared to control devices fabricated on non-porous polyimide substrates. These results have demonstrated the feasibility of paper-based printed devices towards manufacturing of a fully wearable, highly-sensitive, and wireless human performance monitor coupled to flexible electronics with the capability to communicate wirelessly to a smartphone or other electronics for data logging and analysis. 
    more » « less
  2. Metal oxide (MO) semiconductor thin films prepared from solution typically require multiple hours of thermal annealing to achieve optimal lattice densification, efficient charge transport, and stable device operation, presenting a major barrier to roll-to-roll manufacturing. Here, we report a highly efficient, cofuel-assisted scalable combustion blade-coating (CBC) process for MO film growth, which involves introducing both a fluorinated fuel and a preannealing step to remove deleterious organic contaminants and promote complete combustion. Ultrafast reaction and metal–oxygen–metal (M-O-M) lattice condensation then occur within 10–60 s at 200–350 °C for representative MO semiconductor [indium oxide (In2O3), indium-zinc oxide (IZO), indium-gallium-zinc oxide (IGZO)] and dielectric [aluminum oxide (Al2O3)] films. Thus, wafer-scale CBC fabrication of IGZO-Al2O3thin-film transistors (TFTs) (60-s annealing) with field-effect mobilities as high as ∼25 cm2V−1s−1and negligible threshold voltage deterioration in a demanding 4,000-s bias stress test are realized. Combined with polymer dielectrics, the CBC-derived IGZO TFTs on polyimide substrates exhibit high flexibility when bent to a 3-mm radius, with performance bending stability over 1,000 cycles.

     
    more » « less
  3. Abstract

    Here, an environmentally‐friendly and scalable process is reported to synthesize reduced graphene oxide (RGO) thin films for printed electronics applications. The films are produced by inkjet printing GO flakes dispersed binder‐free in aqueous solutions followed by treatment with a nonthermal, radio‐frequency (RF) plasma containing only argon (Ar) gas. The plasma process is found to heat the substrate to temperatures no greater than 138 °C, enabling RGO to be printed directly on a wide range of temperature‐sensitive substrate materials including photo paper. Unlike other low‐temperature methods such as electrochemical reduction, plasma reduction is friendly to moisture absorbent materials. Moreover, the plasma treatment can be performed on nonconducting substrates, eliminating the need for film transfer. From an applications perspective, the printed, plasma‐reduced RGO exhibits excellent electrical, mechanical, and electrochemical properties. As a technology demonstrator, the working electrodes of hydrogen peroxide (H2O2) sensors fabricated from plasma‐reduced GO show a sensitivity of 277 ± 80 µA mm−1cm−2, which is comparable to RGO working electrodes made by electrochemical reduction.

     
    more » « less
  4. Abstract

    Terahertz (THz) imaging has attracted much attention within the past decade as an emerging nondestructive evaluation technique. In this paper, we present a novel Laser-based Metamaterial Fabrication (LMF) process for high-throughput fabrication of transparent conducting surfaces on dielectric substrates such as glass, quartz and polymers to achieve tunable THz bandpass characteristics. The LMF process comprises two steps: (1) applying ultrathin-film metal deposition, with a typical thickness of 10 nm, on the dielectric substrate; (2) creating a ~100-micron feature pattern on the metal film using nanosecond pulsed laser ablation. Our results demonstrate the use of laser-textured ultra-thin film with newly integrated functional capabilities: (a) highly conductive with ~20 Ω/sq sheet resistance, (b) optically transparent with ~70% transmittance within visible spectrum, and (c) tunable bandpass filtering effect in the THz frequency range. A numerical analysis is performed to help determine the fundamental mechanism of THz bandpass filtering for the LMF-built samples. The scientific findings from this work render an economical and scalable manufacturing technique capable of treating large surface area for multi-functional metamaterials.

     
    more » « less
  5. Abstract

    Low‐power, open‐path gas sensors enable eddy covariance (EC) flux measurements in remote areas without line power. However, open‐path flux measurements are sensitive to fluctuations in air temperature, pressure, and humidity. Laser‐based, open‐path sensors with the needed sensitivity for trace gases like methane (CH4) and nitrous oxide (N2O) are impacted by additional spectroscopic effects. Corrections for these effects, especially those related to temperature fluctuations, often exceed the flux of gases, leading to large uncertainties in the associated fluxes. For example, the density and spectroscopic corrections arising from temperature fluctuations can be one or two orders of magnitude greater than background N2O fluxes. Consequently, measuring background fluxes with laser‐based, open‐path sensors is extremely challenging, particularly for N2O and gases with similar high‐precision requirements. We demonstrate a new laser‐based, open‐path N2O sensor and a general approach applicable to other gases that minimizes temperature‐related corrections for EC flux measurements. The method identifies absorption lines with spectroscopic effects in the opposite direction of density effects from temperature and, thus, density and spectroscopic effects nearly cancel one another. The new open‐path N2O sensor was tested at a corn (Zea maysL.) field in Southwestern Michigan, United States. The sensor had an optimal precision of 0.1 ppbv at 10 Hz and power consumption of 50 W. Field trials showed that temperature‐related corrections were 6% of density corrections, reducing EC random errors by 20‐fold compared to previously examined lines. Measured open‐path N2O EC fluxes showed excellent agreement with those made with static chambers (m = 1.0 ± 0.3;r2 = .96). More generally, we identified absorption lines for CO2and CH4 flux measurements that can reduce the temperature‐related corrections by 10–100 times compared to existing open‐path sensors. The proposed method provides a new direction for future open‐path sensors, facilitating the expansion of accurate EC flux measurements.

     
    more » « less