Poly(methyl methacrylate) (PMMA) is an important commodity polymer having a wide range of applications. Currently, only about 10% of PMMA is recycled. Herein, a simple two‐stage process for the chemical upcycling of PMMA is discussed. In this method PMMA is modified by transesterification with a bio‐derived, olefin‐bearing terpenoid, geraniol. In the second stage, olefin‐derivatized PMMA is reacted with sulfur to form a network composite by an inverse vulcanization mechanism. Inverse vulcanization of PGMA with elemental sulfur (90 wt.%) yielded the durable composite
Graphene oxide and functionalized graphenic materials (FGMs) have promise as platforms for imparting programmable bioactivity to poly(methyl methacrylate) (PMMA)‐based bone cement. To date, however, graphenic fillers have only been feasible in PMMA cements at extremely low loadings, limiting the bioactive effects. At higher loadings, graphenic fillers decrease cement strength by aggregating and interfering with curing process. Here, these challenges are addressed by combining bioactive FGM fillers with a custom cement formulation. These cements contain an order of magnitude more graphenic filler than previous reports. Even at 1 wt% FGM, these cements have compressive strengths of 78– 88 MPa, flexural strengths of 74–81 MPa, and flexural stiffnesses of 1.8–1.9 GPa, surpassing the ASTM requirements for bone cement and competing with traditional PMMA cement. Further, by utilizing designer FGMs with programmed bioactivity, these cements demonstrate controlled release of osteogenic calcium ions (releasing a total of 5 ± 2 µmol of Ca2+ per gram of cement over 28 d) and stimulate a 290% increase in expression of alkaline phosphatase in human mesenchymal stem cells in vitro. Also, design criteria are described to guide creation of future generations of bone cements that utilize FGMs as platforms to achieve dynamic biological activity.
more » « less- PAR ID:
- 10364249
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Healthcare Materials
- Volume:
- 10
- Issue:
- 2
- ISSN:
- 2192-2640
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract PGMA‐S . This composite was characterized by NMR spectrometry, IR spectroscopy, elemental analysis, thermogravimetric analysis, and differential scanning calorimetry. Composite water uptake, compressional strength analysis, flexural strength analysis, tensile strength analysis, and thermal recyclability are presented with comparison to current commercial structural materials.PGMA‐S exhibits a similar compressive strength (17.5 MPa) to that of Portland cement.PGMA‐S demonstrates an impressive flexural strength of 4.76 MPa which exceeds the flexural strength (>3 MPa) of many commercial ordinary Portland cements. This study provides a way to upcycle waste PMMA through combination with a naturally‐occurring olefin and industrial waste sulfur to yield composites having mechanical properties competitive with ecologically detrimental legacy building materials. -
null (Ed.)The balance of bacterial populations in the human body is critical for human health. Researchers have aimed to control bacterial populations using antibiotic substrates. However, antibiotic materials that non-selectively kill bacteria can compromise health by eliminating beneficial bacteria, which leaves the body vulnerable to colonization by harmful pathogens. Due to their chemical tunablity and unique surface properties, graphene oxide (GO)-based materials – termed “functional graphenic materials” (FGMs) – have been previously designed to be antibacterial but have the capacity to actively adhere and instruct probiotics to maintain human health. Numerous studies have demonstrated that negatively and positively charged surfaces influence bacterial adhesion through electrostatic interactions with the negatively charged bacterial surface. We found that tuning the surface charge of FGMs provides an avenue to control bacterial attachment without compromising vitality. Using E. coli as a model organism for Gram-negative bacteria, we demonstrate that negatively charged Claisen graphene (CG), a reduced and carboxylated FGM, is bacterio-repellent through electrostatic repulsion with the bacterial surface. Though positively charged poly- l -lysine (PLL) is antibacterial when free in solution by inserting into the bacterial cell wall, here, we found that covalent conjugation of PLL to CG (giving PLL n -G) masks the antimicrobial activity of PLL by restricting polypeptide mobility. This allows the immobilized positive charge of the PLL n -Gs to be leveraged for E. coli adhesion through electrostatic attraction. We identified the magnitude of positive charge of the PLL n -G conjugates, which is modulated by the length of the PLL peptide, as an important parameter to tune the balance between the opposing forces of bacterial adhesion and proliferation. We also tested adhesion of Gram-positive B. subtilis to these FGMs and found that the effect of FGM charge is less pronounced. B. subtilis adheres nondiscriminatory to all FGMs, regardless of charge, but adhesion is scarce and localized. Overall, this work demonstrates that FGMs can be tuned to selectively control bacterial response, paving the way for future development of FGM-based biomaterials as bacterio-instructive scaffolds through careful design of FGM surface chemistry.more » « less
-
Sulfur cements have drawn significant attention as binders because sulfur is a byproduct of fossil fuel refining. Sulfur cements that can be formed by the vulcanization of elemental sulfur and plant-derived olefins such as terpenoids are particularly promising from a sustainability standpoint. A range of terpenoid–sulfur cements have shown compressional and flexural properties exceeding those of some commercial structural mineral cements. Pozzolans such as fly ash (FA), silica fume (SF), and ground granulated blast furnace slag (GGBFS) and abundant clay resources such as metakaolin (MK) are attractive fines for addition to binders. Herein, we report 10 composites prepared by a combination of sulfur, terpenoids (geraniol or citronellol), and these pozzolans. This study reveals the extent to which the addition of the pozzolan fines to the sulfur–terpenoid cements influences their mechanical properties and chemical resistance. The sulfur–terpenoid composites CitS and GerS were prepared by the reaction of 90 wt% sulfur and 10 wt% citronellol or geraniol oil, respectively. The density of the composites fell within the range of 1800–1900 kg/m3 and after 24 h submersion in water at room temperature, none of the materials absorbed more than 0.7 wt% water. The compressional strength of the as-prepared materials ranged from 9.1–23.2 MPa, and the percentage of compressional strength retained after acid challenge (submersion in 0.1 M H2SO4 for 24 h) ranged from 80–100%. Incorporating pozzolan fines into the already strong CitS (18.8 MPa) had negligible effects on its compressional strength within the statistical error of the measurement. CitS-SF and CitS-MK had slightly higher compressive strengths of 20.4 MPa and 23.2 MPa, respectively. CitS-GGBFS and CitS-FA resulted in slightly lower compressive strengths of 17.0 MPa and 15.8 MPa, respectively. In contrast, the compressional strength of initially softer GerS (11.7 MPa) benefited greatly after incorporating hard mineral fines. All GerS derivatives had higher compressive strengths than GerS, with GerS-MK having the highest compressive strength of 19.8 MPa. The compressional strengths of several of the composites compare favorably to those required by traditional mineral cements for residential building foundations (17 MPa), whereas such mineral products disintegrate upon similar acid challenge.more » « less
-
Frederiksberg, Dr_Henrik_Rudolph (Ed.)Wound dressings based on natural materials, such as fish skin, represent an important strategy for the treatment of burns. Despite their utility, contamination of these natural materials with bacteria (planktonic and biofilm forms) introduces significant risks to patients under treatment. This disadvantage can be overcome by modifying the material’s surface to prevent bacterial deposition through chemical or physical interactions. In this work, functional graphenic materials (FGM) with tunable surface charges were incorporated into tilapia (Oreochromis niloticus) fish skin as a part of a strategy to control the biofilm adhesion on surfaces. The antibiofilm activity was evaluated against S. aureus and K. pneumoniae due to the biofilm-forming properties of these bacterial strains. FGM-modified tilapia skin samples possess a strong capacity to reduce biofilm formation on the tilapia fish skin with a higher antibiofilm activity against Gram-positive bacteria, compared to Gram-negative bacteria. Negatively charged FGMs were more effective than positively charged FGMs in preventing biofilm formation on the impregnated tilapia skin xenografts: negatively charged Claisen graphene achieved an 88.8% reduction in biofilm formation on the tilapia skin. Overall, this study demonstrates the utility of FGM-impregnated tilapia skins as a treatment for burn wounds due to their ability to modulate bacterial adhesion.more » « less
-
more » « less
Abstract Primary bone tumor resections often result in critical size defects, which then necessitate challenging clinical management approaches to reconstruct. One such intervention is the Masquelet technique, in which poly(methyl methacrylate) (PMMA) bone cement is placed as a spacer temporarily while adjuvant chemotherapeutics are administered systemically. The spacer is later removed and replaced with bone autograft. Local recurrence remains an important and devastating problem, therefore, a system capable of locally delivering chemotherapeutics will present unique advantages. In this work, a refillable chemotherapeutic (doxorubicin, DOX) delivery platform comprised of PMMA bone cement and insoluble
γ ‐cyclodextrin (γ ‐CD) polymeric microparticles is developed and explored towards application as a temporary adjuvant chemotherapeutic spacer. The system is characterized for porosity, mechanical strength, DOX filling and refilling capacity, elution kinetics, and cytotoxicity. Since residual chemotherapeutics can adversely impact bone healing, it is important that virtually all DOX be released from material. Composites containing 15 wt%γ ‐CD microparticles demonstrate 100% DOX release within 100 days, whereas only 6% DOX is liberated from PMMA with free DOX over same period. Refillable properties of PMMA composite system may find utility for customizing dosing regimens. Findings suggest that PMMA composites can have potential as chemotherapeutic delivery platforms to assist in bone reconstruction.