Linear-accelerator-based applications like x-ray free electron lasers, ultrafast electron diffraction, electron beam cooling, and energy recovery linacs use photoemission-based cathodes in photoinjectors for electron sources. Most of these photocathodes are typically grown as polycrystalline materials with disordered surfaces. In order to understand the mechanism of photoemission from such cathodes and completely exploit their photoemissive properties, it is important to develop a photoemission formalism that properly describes the subtleties of these cathodes. The Dowell–Schmerge (D–S) model often used to describe the properties of such cathodes gives the correct trends for photoemission properties like the quantum efficiency (QE) and the mean transverse energy (MTE) for metals; however, it is based on several unphysical assumptions. In the present work, we use Spicer’s three-step photoemission formalism to develop a photoemission model that results in the same trends for QE and MTE as the D–S model without the need for any unphysical assumptions and is applicable to defective thin-film semiconductor cathodes along with metal cathodes. As an example, we apply our model to Cs3Sb thin films and show that their near-threshold QE and MTE performance is largely explained by the exponentially decaying defect density of states near the valence band maximum.
The performance of x-ray free electron lasers and ultrafast electron diffraction experiments is largely dependent on the brightness of electron sources from photoinjectors. The maximum brightness from photoinjectors at a particular accelerating gradient is limited by the mean transverse energy (MTE) of electrons emitted from photocathodes. For high quantum efficiency (QE) cathodes like alkali-antimonide thin films, which are essential to mitigate the effects of non-linear photoemission on MTE, the smallest possible MTE and, hence, the highest possible brightness are limited by the nanoscale surface roughness and chemical inhomogeneity. In this work, we show that high QE Cs3Sb films grown on lattice-matched strontium titanate (STO) substrates have a factor of 4 smoother, chemically uniform surfaces compared to those traditionally grown on disordered Si surfaces. We perform simulations to calculate roughness induced MTE based on measured topographical and surface-potential variations on the Cs3Sb films grown on STO and show that these variations are small enough to have no consequential impact on the MTE and, hence, the brightness.
more » « less- NSF-PAR ID:
- 10366841
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Applied Physics Letters
- Volume:
- 120
- Issue:
- 19
- ISSN:
- 0003-6951
- Page Range / eLocation ID:
- Article No. 194102
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
more » « less
We report on the growth and characterization of a new class of photocathode structures for use as electron sources to produce high brightness electron beams for accelerator applications. The sources are realized using III-nitride materials and are designed to leverage the strong polarization field, which is characteristic of this class of materials when grown in their wurtzite crystal structure, to produce a negative electron affinity condition without the use of Cs, possibly allowing these materials to be operated in radio frequency guns. A Quantum Efficiency (QE) of about [Formula: see text] and an emitted electrons’ Mean Transverse Energy (MTE) of about 100 meV are measured at a wavelength of 265 nm. In a vacuum level of [Formula: see text] Torr, the QE does not decrease after more than 24 h of continuous operation. The lowest MTE of about 50 meV is measured at 300 nm along with a QE of [Formula: see text]. Surface characterizations reveal a possible contribution to the MTE from surface morphology, calling for more detailed studies.
-
more » « less
Abstract In the field of beam physics, two frontier topics have taken center stage due to their potential to enable new approaches to discovery in a wide swath of science. These areas are: advanced, high gradient acceleration techniques, and x-ray free electron lasers (XFELs). Further, there is intense interest in the marriage of these two fields, with the goal of producing a very compact XFEL. In this context, recent advances in high gradient radio-frequency cryogenic copper structure research have opened the door to the use of surface electric fields between 250 and 500 MV m−1. Such an approach is foreseen to enable a new generation of photoinjectors with six-dimensional beam brightness beyond the current state-of-the-art by well over an order of magnitude. This advance is an essential ingredient enabling an ultra-compact XFEL (UC-XFEL). In addition, one may accelerate these bright beams to GeV scale in less than 10 m. Such an injector, when combined with inverse free electron laser-based bunching techniques can produce multi-kA beams with unprecedented beam quality, quantified by 50 nm-rad normalized emittances. The emittance, we note, is the effective area in transverse phase space (
x ,p x /m ec ) or (y ,p y /m ec ) occupied by the beam distribution, and it is relevant to achievable beam sizes as well as setting a limit on FEL wavelength. These beams, when injected into innovative, short-period (1–10 mm) undulators uniquely enable UC-XFELs having footprints consistent with university-scale laboratories. We describe the architecture and predicted performance of this novel light source, which promises photon production per pulse of a few percent of existing XFEL sources. We review implementation issues including collective beam effects, compact x-ray optics systems, and other relevant technical challenges. To illustrate the potential of such a light source to fundamentally change the current paradigm of XFELs with their limited access, we examine possible applications in biology, chemistry, materials, atomic physics, industry, and medicine—including the imaging of virus particles—which may profit from this new model of performing XFEL science. -
more » « less
The quantum efficiency and mean transverse energy of electrons emitted from a cathode determine the quality of beams generated from photoinjectors. The nitrogen-incorporated ultrananocrystalline diamond, (N)UNCD, is a new class of robust semiconductor photocathodes, which has been considered in photoinjectors for high peak current extraction. In this work, we measure the spectral response in quantum efficiency, photoemission energy spectra, and mean transverse energy of the (N)UNCD photocathode using a photoemission electron microscope. The observed quantum efficiency was comparable to that of copper photocathodes. Photoemission spectra showed the evidence of scattering of electrons before emission. This relaxation of electrons due to scattering is also observed in the spectral response of the mean transverse energy. The mean transverse energy is limited to ∼70 meV at the threshold. We attribute this to the physical and chemical roughness of the (N)UNCD photocathode and, hence, smoother films will be required to further reduce the mean transverse energy obtained from the (N)UNCD photocathode.
-
BAlN films were grown by flow-rate modulation epitaxy on AlN. Figure 1 shows x-ray diffraction (XRD) peaks of 3-µm AlN/(0001) sapphire template layer and 45-nm BAlN layer at 2θ angles of 36.146o and 36.481o, corresponding to c-lattice constants of 4.966 and 4.922Å, respectively. The BAlN XRD peak is very clear and distinct given the small thickness, indicating good wurtzite crystallinity. It is not possible to directly calculate the B content from XRD alone because of uncertainty of the lattice parameters and strain. However, based on the angular separation of the XRD peaks and c-lattice constant difference, the B content is estimated to be ~7% [ ], which is considerably higher than those of high-quality wurtzite BAlN layers reported before [ , , ]. To obtain the accurate B content, Rutherford backscattering spectrometry (RBS) measurements are being made. Figures 2(a)-(b) show a high-resolution cross-sectional transmission electron microscopy (TEM) image with a magnification of 150 kx taken at a-zone axis ([11-20] projection) and diffraction pattern after fast-Fourier transform (FFT). A sharp interface between the AlN and BAlN layers is observed. In addition, the BAlN film exhibits a highly ordered lattice throughout the entire 45nm thickness without the polycrystalline columnar structures found in previous reports [1, ]. The FFT image confirms a wurtzite structure oriented along c-axis. Figure 3 shows a 5×5 µm2 atomic force microscopy (AFM) image of BAlN layer surface. The root-mean-square (RMS) surface roughness is ~1.7nm. Surface macro-steps were found on the surface due to longer diffusion length of group-III atoms than the expected step terrace width. This indicates there is potential to lower the growth temperature to create smoother surfaces while maintaining crystallinity which has been observed for AlN [ ]. In summary, a high-quality wurtzite BAlN layer with relatively high B content ~7% was demonstrated by MOCVD. Refractive index will be measured to facilitate design of distributed Bragg reflector (DBR) for deep UV vertical-cavity surface-emitting laser (VCSEL).more » « less