Dye-doped nanoparticles have been investigated as bright, luminescent labels for super-resolution microscopy via localization methods. One key factor in super-resolution is the size of the luminescent label, which in some cases results in a frame shift between the label target and the label itself. Ag@SiO 2 core–shell nanoparticles, doped with organic fluorophores, have shown promise as super-resolution labels. One key aspect of these nanoparticles is that they blink under certain conditions, allowing super-resolution localization with a single excitation source in aqueous solution. In this work, we investigated the effects of both the Ag core and the silica (SiO 2 ) shell on the self-blinking properties of these nanoparticles. Both core size and shell thickness were manipulated by altering the reaction time to determine core and shell effects on photoblinking. Size and shell thickness were investigated individually under both dry and hydrated conditions and were then doped with a 1 mM solution of Rhodamine 110 for analysis. We observed that the cores themselves are weakly luminescent and are responsible for the blinking observed in the fully-synthesized metal-enhanced fluorescence nanoparticles. There was no statistically significant difference in photoblinking behavior—both intensity and duty cycle—with decreasing core size. This observation was used to synthesize smaller nanoparticles ranging from approximately 93 nm to 110 nm as measured using dynamic light scattering. The blinking particles were localized via super-resolution microscopy and show single particle self-blinking behavior. As the core size did not impact blinking performance or intensity, the nanoparticles can instead be tuned for optimal size without sacrificing luminescence properties.
more »
« less
Synthesis and Characterization of Dye-Doped Au@SiO 2 Core-Shell Nanoparticles for Super-Resolution Fluorescence Microscopy
Dye-doped nanoparticles have been investigated as bright, fluorescent probes for localization-based super-resolution microscopy. Nanoparticle size is important in super-resolution microscopy to get an accurate size of the object of interest from image analysis. Due to their self-blinking behavior and metal-enhanced fluorescence (MEF), Ag@SiO2and Au@Ag@SiO2nanoparticles have shown promise as probes for localization-based super-resolution microscopy. Here, several noble metal-based dye-doped core-shell nanoparticles have been investigated as self-blinking nanomaterial probes. It was observed that both the gold- and silver-plated nanoparticle cores exhibit weak luminescence under certain conditions due to the surface plasmon resonance bands produced by each metal, and the gold cores exhibit blinking behavior which enhances the blinking and fluorescence of the dye-doped nanoparticle. However, the silver-plated nanoparticle cores, while weakly luminescent, did not exhibit any blinking; the dye-doped nanoparticle exhibited the same behavior as the core fluorescent, but did not blink. Because of the blinking behavior, stochastic optical reconstruction microscopy (STORM) super-resolution analysis was able to be performed with performed on the gold core nanoparticles. A preliminary study on the use of these nanoparticles for localization-based super-resolution showed that these nanoparticles are suitable for use in STORM super resolution. Resolution enhancement was two times better than the diffraction limited images, with core sizes reduced to 15 nm using the hybrid Au–Ag cores.
more » « less- Award ID(s):
- 1849063
- NSF-PAR ID:
- 10376879
- Publisher / Repository:
- SAGE Publications
- Date Published:
- Journal Name:
- Applied Spectroscopy
- Volume:
- 76
- Issue:
- 11
- ISSN:
- 0003-7028
- Page Range / eLocation ID:
- p. 1367-1374
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
null (Ed.)Super resolution microscopy was developed to overcome the Abbe diffraction limit, which effects conventional optical microscopy, in order to study the smaller components of biological systems. In recent years nanomaterials have been explored as luminescent probes for super resolution microscopy, as many have advantages over traditional fluorescent dye molecules. This review will summarize several different types of nanomaterial probes, covering quantum dots, carbon dots, and dye doped nanoparticles. For the purposes of this review the term “nanoparticle” will be limited to polymer-based, protein-based, and silica-based nanoparticles, including core–shell structured nanoparticles. Luminescent nanomaterials have shown promise as super-resolution probes, and continued research in this area will yield new advances in both materials science and biochemical microscopy at the nanometer scale.more » « less
-
Abstract Silver nanowires (AgNWs) hold great promise for applications in wearable electronics, flexible solar cells, chemical and biological sensors, photonic/plasmonic circuits, and scanning probe microscopy (SPM) due to their unique plasmonic, mechanical, and electronic properties. However, the lifetime, reliability, and operating conditions of AgNW-based devices are significantly restricted by their poor chemical stability, limiting their commercial potentials. Therefore, it is crucial to create a reliable oxidation barrier on AgNWs that provides long-term chemical stability to various optical, electrical, and mechanical devices while maintaining their high performance. Here we report a room-temperature solution-phase approach to grow an ultra-thin, epitaxial gold coating on AgNWs to effectively shield the Ag surface from environmental oxidation. The Ag@Au core-shell nanowires (Ag@Au NWs) remain stable in air for over six months, under elevated temperature and humidity (80 °C and 100% humidity) for twelve weeks, in physiological buffer solutions for three weeks, and can survive overnight treatment of an oxidative solution (2% H 2 O 2 ). The Ag@Au core-shell NWs demonstrated comparable performance as pristine AgNWs in various electronic, optical, and mechanical devices, such as transparent mesh electrodes, surface-enhanced Raman spectroscopy (SERS) substrates, plasmonic waveguides, plasmonic nanofocusing probes, and high-aspect-ratio, high-resolution atomic force microscopy (AFM) probes. These Au@Ag core-shell NWs offer a universal solution towards chemically-stable AgNW-based devices without compromising material property or device performance.more » « less
-
The presence of dark states causes fluorescence intermittency of single molecules due to transitions between “on” and “off” states. Genetically encodable markers such as fluorescent proteins (FPs) exhibit dark states that make several super-resolved single-molecule localization microscopy (SMLM) methods possible. However, studies quantifying the timescales and nature of dark state behavior for commonly used FPs under conditions typical of widefield and total internal reflection fluorescence (TIRF) microscopy remain scarce and pre-date many new SMLM techniques. FusionRed is a relatively bright red FP exhibiting fluorescence intermittency and has thus been identified as a potential candidate for SMLM. We herein characterize the rates for dark-state conversion and the subsequent ground-state recovery of FusionRed and its 2.5-fold brighter descendent FusionRed L175M M42Q (FusionRed-MQ) at low irradiances (1–10 W cm −2 ), which were previously unexplored experimental conditions. We characterized the kinetics of dark state transitions in these two FPs by using single molecule blinking and ensemble photobleaching experiments bridged with a dark state kinetic model. We find that at low irradiances, the recovery process to the ground state is minimally light-driven and FusionRed-MQ has a 1.3-fold longer ground state recovery time indicating a conformationally restricted dark-state chromophore in comparison to FusionRed. Our studies indicate that the brighter FusionRed-MQ variant exhibits higher dark state conversion rates with longer ground state recovery lifetimes, thus it is potentially a better candidate for SMLM applications than its progenitor FusionRed.more » « less
-
more » « less
Abstract Dissipative self‐assembly of colloidal nanoparticles offers the prospect of creating reconfigurable artificial materials and systems, yet the phenomenon only occurs far from thermodynamic equilibrium. Therefore, it is usually difficult to predict and control. Here, a dissipative colloidal solution system, where anisotropic chains with different interparticle separations in two perpendicular directions transiently arise among largely disordered silver nanoparticles illuminated by a laser beam, is reported. The optical field creates a nonequilibrium dissipative state, where a disorder‐to‐order transition occurs driven by anisotropic electrodynamic interactions coupled with electrostatic interactions. Investigation of the temporal dynamics and spatial arrangements of the nanoparticle system shows that the optical binding strength and entropy of the system are two crucial parameters for the formation of the anisotropic chains and responsible for adaptive behaviors, such as self‐replication of dimer units. Formation of anisotropic nanoparticle chains is also observed among colloidal nanoparticles made from other metal (e.g., Au), polymer (e.g., polystyrene), ceramic (e.g., CeO2), and hybrid materials (e.g., SiO2@Au core–shell), suggesting that light‐driven self‐organization will provide a wide range of opportunities to discover new dissipative structures under thermal fluctuations and build novel anisotropic materials with nanoscale order.