skip to main content
US FlagAn official website of the United States government
dot gov icon
Official websites use .gov
A .gov website belongs to an official government organization in the United States.
https lock icon
Secure .gov websites use HTTPS
A lock ( lock ) or https:// means you've safely connected to the .gov website. Share sensitive information only on official, secure websites.

Explore Research Products in the PAR
It may take a few hours for recently added research products to appear in PAR search results.


  • NSF Public Access
  • Search Results
  • Superconducting HfO 2 -added solution-derived YBa 2 Cu 3 O 7 nanocomposite films: the effect of colloidal nanocrystal shape and crystallinity on pinning mechanism
Title: Superconducting HfO 2 -added solution-derived YBa 2 Cu 3 O 7 nanocomposite films: the effect of colloidal nanocrystal shape and crystallinity on pinning mechanism
Abstract Two different types of monoclinic HfO 2 nanocrystals were employed in this work to study the effect of nanocrystal shape and crystallinity on the structural defects in the YBa2Cu3O7−δ (YBCO) matrix as it leads to an enhancement of pinning performances of solution-derived YBCO nanocomposite films. In this work the nanorod-like HfO 2 nanocrystals obtained from surfactant-controlled synthesis led to short intergrowths surrounding the particles, while spherical HfO 2 nanocrystals from the solvent-controlled synthesis led to the formation of long stacking faults in the YBCO matrix. It means that the small difference in crystallinity, lattice parameters, nanocrystal structures, core diameter of preformed nanocrystals in colloidal solutions have a strong influence on the formation of the structural defects around the particles in the YBCO matrix, leading to different pinning performances.  more » « less
Award ID(s):
1922234
PAR ID:
10384214
Author(s) / Creator(s):
; ; ; ; ; ; ;
Date Published:
Journal Name:
Superconductor Science and Technology
Volume:
35
Issue:
8
ISSN:
0953-2048
Page Range / eLocation ID:
084008
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ; ; ; (, Superconductor Science and Technology)
    Abstract BaZrO3(BZO) one-dimensional artificial pinning centers (1D-APCs) aligned along thec-axis of the YBa2Cu3O7(YBCO) have been adopted to enhance the magnetic vortex pinning in BZO/YBCO nanocomposite films. However, the pinning force densityFpof the BZO 1D-APCs remains moderate at temperatures near 77 K. A hypothesis of the major limiting factor is the defective BZO 1D-APCs/YBCO interface as a direct consequence of the large interfacial strain originated from the BZO/YBCO lattice mismatch of ∼7.7%. Herein, we explore enlarging thec-axis of the YBCO dynamically to reduce the lattice mismatch and hence to prevent formation of the defective BZO 1D-APCs/YBCO interface. Specifically, thec-axis enlargement was achieved by partial replacement of Cu with Ca on the YBCO lattice using strain-directed Ca diffusion into YBCO from two Ca0.3Y0.7Ba2Cu3O7−x(CaY-123) spacers of only 10 nm in thickness inserted into the 2 vol% BZO 1D-APC/YBCO nanocomposite thin films of ∼150 nm in total thickness. The achieved elongatedc-axis is attributed to the formation of stacking faults induced by Ca-replacement of Cu on YBCO lattice. The reduced BZO/YBCO lattice mismatch allows formation of a coherent BZO 1D-APC/YBCO interface with negligible defects. This leads to an enhancedFpvalue up to 98 GN m−3at 65 K, which is 70% higher than that of the reference 2 vol% BZO 1D-APC/YBCO sample. Furthermore, the benefit of the enhanced pinning of the BZO 1D-APCs with a coherent interface with YBCO can be extended to a large angular range of the magnetic field orientation. This study reveals the significant effect of the BZO/YBCO interface on the pinning efficiency of BZO 1D-APCs and provides a promising approach to achieve a coherent interface in BZO/YBCO nanocomposite films. 
    more » « less
  2. ; ; ; ; ; ; ; ; ; (, Superconductor Science and Technology)
    Abstract One-dimensional c -axis-aligned BaZrO 3 (BZO) nanorods are regarded as strong one-dimensional artificial pinning centers (1D-APCs) in BZO-doped YaBa 2 Cu 3 O 7− x (BZO/YBCO) nanocomposite films. However, a microstructure analysis has revealed a defective, oxygen-deficient YBCO column around the BZO 1D-APCs due to the large lattice mismatch of ∼7.7% between the BZO (3a = 1.26 nm) and YBCO (c = 1.17 nm), which has been blamed for the reduced pinning efficiency of BZO 1D-APCs. Herein, we report a dynamic lattice enlargement approach on the tensile strained YBCO lattice during the BZO 1D-APCs growth to induce c -axis elongation of the YBCO lattice up to 1.26 nm near the BZO 1D-APC/YBCO interface via Ca/Cu substitution on single Cu-O planes of YBCO, which prevents the interfacial defect formation by reducing the BZO/YBCO lattice mismatch to ∼1.4%. Specifically, this is achieved by inserting thin Ca 0.3 Y 0.7 Ba 2 Cu 3 O 7− x (CaY-123) spacers as the Ca reservoir in 2–6 vol.% BZO/YBCO nanocomposite multilayer (ML) films. A defect-free, coherent BZO 1D-APC/YBCO interface is confirmed in transmission electron microscopy and elemental distribution analyses. Excitingly, up to five-fold enhancement of J c ( B ) at magnetic field B = 9.0 T// c -axis and 65 K–77 K was obtained in the ML samples as compared to their BZO/YBCO single-layer (SL) counterpart’s. This has led to a record high pinning force density F p together with significantly enhanced B max at which F p reaches its maximum value F p,max for BZO 1D-APCs at B // c -axis. At 65 K, the F p,max ∼158 GN m −3 and B max ∼ 8.0 T for the 6% BZO/YBCO ML samples represent a significant enhancement over F p,max ∼ 36.1 GN m −3 and B max ∼ 5.0 T for the 6% BZO/YBCO SL counterparts. This result not only illustrates the critical importance of a coherent BZO 1D-APC/YBCO interface in the pinning efficiency, but also provides a facile scheme to achieve such an interface to restore the pristine pinning efficiency of the BZO 1D-APCs. 
    more » « less
  3. ; ; ; ; ; ; (, IOP Conference Series: Materials Science and Engineering)
    Abstract C-axis aligned BaZrO3(BZO) nanorods formed via strain-mediated self-assembly in BZO-doped YaBa2Cu3O7-x(BZO/YBCO) nanocomposite films can provide strong pinning to the quantized magnetic vortices. While the strain initiated from the BZO/YBCO lattice mismatch plays a critical role in nucleation and evolution of the BZO nanorods, it also leads to a highly defective BZO/YBCO interface and hence reduced pinning efficiency of BZO nanorods. This work reports a recent study in probing the effect of BZO/YBCO interface on the pinning efficiency of the BZO nanorods as the interface is repaired dynamically during the BZO nanorod growth using Ca doping. Within the BZO doping range of 2-8 vol.%, significantly enhanced pinning efficiency of the BZO nanorods have been observed. A peak enhancement up to five-fold of critical current density at 9.0 T and 65-77 K has been obtained in the 6 vol.% BZO/YBCO nanocomposites after the interface repair. This result not only illustrates the critical importance of the BZO/YBCO interface in the pinning efficiency, but also provides a facile scheme to achieve such an interface to restore the pristine pinning efficiency of the BZO nanorods. 
    more » « less
  4. ; ; ; ; ; (, Materials Research Express)
    Abstract This work examines the pinning enhancement in BaZrO 3 (BZO) +Y 2 O 3 doubly-doped (DD) YBa 2 Cu 3 O 7 (YBCO) nanocomposite multilayer (DD-ML) films. The film consists of two 10 nm thin Ca 0.3 Y 0.7 Ba 2 Cu 3 O 7-x (CaY-123) spacers stacking alternatively with three BZO + Y 2 O 3 /YBCO layers of 50 nm each in thickness that contain 3 vol% of Y 2 O 3 and BZO doping in the range of 2–6 vol%. Enhanced magnetic vortex pinning and improved pinning isotropy with respect to the orientation of magnetic field (B) have been achieved in the DD-ML samples at lower BZO doping as compared to that in the single-layer counterparts (DD-SL) without the CaY-123 spacers. For example, the pinning force density ( F p ) of ∼58 GNm −3 in 2 vol.% of DD-ML film is ∼110% higher than in 2 vol% of DD-SL at 65 K and B // c -axis, which is attributed to the improved pinning efficiency by c -axis aligned BZO nanorods through diffusion of Calcium (Ca) along the tensile-strained channels at BZO nanorods/YBCO interface for improvement of the interface microstructure and hence pinning efficiency of BZO nanorods. An additional benefit is in the considerably improved J c ( θ ) and reduced J c anisotropy in the former over the entire range of the B orientations. However, at higher BZO doping, the BZO nanorods become segmented and misoriented, which may change the Ca diffusion pathways and reduce the benefit of Ca in improving the pinning efficiency of BZO nanorods. 
    more » « less
  5. ; ; ; ; (, Frontiers in Nanotechnology)
    Seed-mediated synthesis is a versatile method to prepare multimetallic nanocrystals for diverse applications. However, many fundamental questions remain on how the structural and chemical properties of nanocrystal seeds control the reaction pathways, especially for nonaqueous synthesis at elevated temperatures. Herein, we elucidate the role of surface ligands and crystallinity of Au nanocrystal seeds on the heterometallic seeded growth of Cu-based nanocrystals. We found that weakly coordinating ligands are critical to facilitate the diffusion between Au and Cu, which enables subsequent one-dimensional growth of Cu. Replacing multiple-twinned Au seeds with single-crystalline ones switched the growth pathway to produce heterostructured nanocrystals. Our work illustrates the importance of precise control of seed characteristics for the predictive synthesis of structurally complex multimetallic nanocrystals. 
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email