Title: Influence of vanadium addition on corrosion behavior of high‐energy ball milled aluminum alloy 2024
Abstract

The effect of V addition on the hardness and corrosion of aluminum alloy 2024 (AA2024) produced by high‐energy ball milling has been investigated. High‐energy ball milled alloys exhibited enhanced solid solubility of alloying elements and ultrafine grains. The addition of V improved the corrosion resistance of the AA2024 alloy, which was attributed to the deposition of V on the cathodic particles and therefore decrease in their ability to sustain large cathodic currents.

 
more » « less
Award ID(s):
2131440
NSF-PAR ID:
10443329
Author(s) / Creator(s):
 ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Materials and Corrosion
Volume:
74
Issue:
2
ISSN:
0947-5117
Page Range / eLocation ID:
p. 285-292
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Supersaturated solid solutions of Al and corrosion-resistant alloying elements (M: V, Mo, Cr, Ti, Nb), produced by non-equilibrium processing techniques, have been reported to exhibit high corrosion resistance and strength. The corrosion mechanism for such improved corrosion performance has not been well understood. We present a fundamental understanding of the role of V in corrosion of an Al-V alloy, which will provide a theoretical background for developing corrosion-resistant Al alloys. High-energy ball milling of the elemental powder of Al and V produced an in situ consolidated Al-V alloy, which exhibited high solid solubility of V. The corrosion resistance of Al-V alloy was significantly higher than that of pure Al, which was attributed to the (1) enrichment of V at the passive film/substrate interface, (2) incorporation of V into the passive film, and (3) deposition of V on the iron-containing cathodic particles and therefore, retardation of cathodic reaction.

     
    more » « less
  2. Al-V alloys produced via high-energy ball milling have been reported to show simultaneous improvement of corrosion resistance and mechanical properties compared to traditional Al alloys. In these alloys, V content plays a crucial role in increasing or decreasing the corrosion resistance. Therefore, the effect of V and microstructure on corrosion of high-energy ball milled and subsequently spark plasma sintered Al-xV alloys (x = 2, 5, 10 at%) has been studied. Cyclic potentiodynamic polarization tests and electrochemical impedance spectroscopic analysis revealed the increment of V content up to 5 at% enhanced the corrosion resistance of the alloy. However, highly heterogeneous microstructure in Al-10 at%V resulted in significant localized corrosion over the immersion time. The electrochemical impedance spectroscopy studies over 14 days of immersion revealed underlying corrosion mechanisms.

     
    more » « less
  3. Nanocrystalline supersaturated Al-V alloys produced by high-energy ball milling have been reported to exhibit enhanced corrosion resistance and mechanical properties compared to commercial Al alloys. Corrosion of passive alloys such as Al-V alloy relies on the characteristics of the surface film, which is studied using scanning/transmission electron microscopy and time-of-flight secondary ion mass spectrometry. The effect of microstructure and composition on the surface film has been investigated after different immersion periods (30 min, 2 h, and 1 day) in 0.1 M NaCl. The surface film was complex and composed of oxidized Al and V. The heterogeneous surface film was observed due to the presence of secondary phases and initiation of localized corrosion. The void formation was observed beneath the surface film that would potentially cause pitting corrosion. The generation of nano-sized voids was dependent on grain orientation. Compared to pure Al, the chloride penetration is suppressed in Al-V alloys. The effect of composition and microstructure on surface film formation and attendant corrosion behavior is discussed herein.

     
    more » « less
  4. null (Ed.)
    In this work, nine nanocrystalline binary Mg alloys were synthesized by high-energy ball milling. The compositions, Mg-5 wt% M (M-Cr, Ge, Mn, Mo, Ta, Ti, V, Y, and Zn), were milled with the objective of achieving non-equilibrium alloying. The milled alloys were consolidated via cold compaction (CC) at 25°C and spark plasma sintering (SPS) at 300°C. X-ray diffraction (XRD) analysis indicated grain refinement below 100 nm, and the scanning electron microscopy revealed homogeneous microstructures for all compositions. XRD analysis revealed that most of the alloys showed a change in the lattice parameter, which indicates the formation of a solid solution. A significant increase in the hardness compared to unmilled Mg was observed for all of the alloys. The corrosion behavior was improved in all of the binary alloys compared to milled Mg. A significant decrease in the cathodic kinetics was evident due to Ge and Zn additions. The influence of the alloying elements on corrosion behavior has been categorized and discussed based on the electrochemical response of their respective binary Mg alloys. 
    more » « less
  5. Abstract

    Here, unbiased water splitting with 2% solar‐to‐hydrogen efficiency under AM 1.5 G illumination using new materials based on GaSb0.03P0.97alloy is reported. Freestanding GaSbxP1−xis grown using halide vapor phase epitaxy. The native conductivity type of the alloy is modified by silicon doping, resulting in an open‐circuit potential (OCP) of 750 mV, photocurrents of 7 mA cm−2at 10 sun illumination, and corrosion resistance in an aqueous acidic environment. Alloying GaP with Sb at 3 at% improves the absorption of high‐energy photons above 2.68 eV compared to pure GaP material. Electrochemical Impedance Spectroscopy and illuminated OCP measurements show that the conduction band of GaSbxP1−xis at −0.55 V versus RHE irrespective of the Sb concentration, while photocurrent spectroscopy indicates that only radiation with photon energies greater than 2.68 eV generate mobile and extractable charges, thus suggesting that the higher‐laying conduction bands in the Γ 1 valley of the alloys are responsible for exciton generation.

     
    more » « less