Title: Influence of Potassium Metal‐Support Interactions on Dendrite Growth
Abstract

Combined synchrotron X‐ray nanotomography imaging, cryogenic electron microscopy (cryo‐EM) and modeling elucidate how potassium (K) metal‐support energetics influence electrodeposit microstructure. Three model supports are employed: O‐functionalized carbon cloth (potassiophilic, fully‐wetted), non‐functionalized cloth and Cu foil (potassiophobic, nonwetted). Nanotomography and focused ion beam (cryo‐FIB) cross‐sections yield complementary three‐dimensional (3D) maps of cycled electrodeposits. Electrodeposit on potassiophobic support is a triphasic sponge, with fibrous dendrites covered by solid electrolyte interphase (SEI) and interspersed with nanopores (sub‐10 nm to 100 nm scale). Lage cracks and voids are also a key feature. On potassiophilic support, the deposit is dense and pore‐free, with uniform surface and SEI morphology. Mesoscale modeling captures the critical role of substrate‐metal interaction on K metal film nucleation and growth, as well as the associated stress state.

 
more » « less
NSF-PAR ID:
10415859
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Angewandte Chemie
Volume:
135
Issue:
23
ISSN:
0044-8249
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Combined synchrotron X‐ray nanotomography imaging, cryogenic electron microscopy (cryo‐EM) and modeling elucidate how potassium (K) metal‐support energetics influence electrodeposit microstructure. Three model supports are employed: O‐functionalized carbon cloth (potassiophilic, fully‐wetted), non‐functionalized cloth and Cu foil (potassiophobic, nonwetted). Nanotomography and focused ion beam (cryo‐FIB) cross‐sections yield complementary three‐dimensional (3D) maps of cycled electrodeposits. Electrodeposit on potassiophobic support is a triphasic sponge, with fibrous dendrites covered by solid electrolyte interphase (SEI) and interspersed with nanopores (sub‐10 nm to 100 nm scale). Lage cracks and voids are also a key feature. On potassiophilic support, the deposit is dense and pore‐free, with uniform surface and SEI morphology. Mesoscale modeling captures the critical role of substrate‐metal interaction on K metal film nucleation and growth, as well as the associated stress state.

     
    more » « less
  2. The physiochemical nature of reactive metal electrodeposits during the early stages of electrodeposition is rarely studied but known to play an important role in determining the electrochemical stability and reversibility of electrochemical cells that utilize reactive metals as anodes. We investigated the early-stage growth dynamics and reversibility of electrodeposited lithium in liquid electrolytes infused with brominated additives. On the basis of equilibrium theories, we hypothesize that by regulating the surface energetics and surface ion/adatom transport characteristics of the interphases formed on Li, Br-rich electrolytes alter the morphology of early-stage Li electrodeposits; enabling late-stage control of growth and high electrode reversibility. A combination of scanning electron microscopy (SEM), image analysis, X-ray photoelectron spectroscopy (XPS), electrochemical impedance spectroscopy (EIS), and contact angle goniometry are employed to evaluate this hypothesis by examining the physical–chemical features of the material phases formed on Li. We report that it is possible to achieve fine control of the early-stage Li electrodeposit morphology through tuning of surface energetic and ion diffusion properties of interphases formed on Li. This control is shown further to translate to better control of Li electrodeposit morphology and high electrochemical reversibility during deep cycling of the Li metal anode. Our results show that understanding and eliminating morphological and chemical instabilities in the initial stages of Li electroplating via deliberately modifying energetics of the solid electrolyte interphase (SEI) is a feasible approach in realization of deeply cyclable reactive metal batteries.

     
    more » « less
  3. Metal‐free electrocatalysts have been extensively developed to replace noble metal Pt and RuO2catalysts for the oxygen reduction reaction (ORR) and oxygen evolution reaction (OER) in fuel cells or metal–air batteries. These electrocatalysts are usually deposited on a 3D conductive support (e.g., carbon paper or carbon cloth (CC)) to facilitate mass and electron transport. For practical applications, it is desirable to create in situ catalysts on the carbon fiber support to simplify the fabrication process for catalytic electrodes. In this study, the first example of in situ exfoliated, edge‐rich, oxygen‐functionalized graphene on the surface of carbon fibers using Ar plasma treatment is successfully prepared. Compared to pristine CC, the plasma‐etched carbon cloth (P‐CC) has a higher specific surface area and an increased number of active sites for OER and ORR. P‐CC also displays good intrinsic electron conductivity and excellent mass transport. Theoretical studies show that P‐CC has a low overpotential that is comparable to Pt‐based catalysts, as a result of both defects and oxygen doping. This study provides a simple and effective approach for producing highly active in situ catalysts on a carbon support for OER and ORR.

     
    more » « less
  4. Abstract

    Repeated cold rolling and folding is employed to fabricate a metallurgical composite of sodium–antimony–telluride Na2(Sb2/6Te3/6Vac1/6) dispersed in electrochemically active sodium metal, termed “NST‐Na.” This new intermetallic has a vacancy‐rich thermodynamically stable face‐centered‐cubic structure and enables state‐of‐the‐art electrochemical performance in widely employed carbonate and ether electrolytes. NST‐Na achieves 100% depth‐of‐discharge (DOD) in 1mNaPF6in G2, with 15 mAh cm−2at 1 mA cm−2and Coulombic efficiency (CE) of 99.4%, for 1000 h of plating/stripping. Sodium‐metal batteries (SMBs) with NST‐Na and Na3V2(PO4)3 (NVP) or sulfur cathodes give significantly improved energy, cycling, and CE (>99%). An anode‐free battery with NST collector and NVP obtains 0.23% capacity decay per cycle. Imaging and tomography using conventional and cryogenic microscopy (Cryo‐EM) indicate that the sodium metal fills the open space inside the self‐supporting sodiophilic NST skeleton, resulting in dense (pore‐free and solid electrolyte interphase (SEI)‐free) metal deposits with flat surfaces. The baseline Na deposit consists of filament‐like dendrites and “dead metal”, intermixed with pores and SEI. Density functional theory calculations show that the uniqueness of NST lies in the thermodynamic stability of the Na atoms (rather than clusters) on its surface that leads to planar wetting, and in its own stability that prevents decomposition during cycling.

     
    more » « less
  5. Abstract

    The solid electrolyte interphase (SEI) forms on electrode surfaces from decomposition of the electrolyte. However, there is almost no atomistic detail of SEI formation on Li metal anode, a major obstacle in understanding the highly complex battery electrochemistry sufficiently to design high performance batteries. Herein, a realistic atomistic model (39 000 atoms) for the SEI formation at the interface between the Li metal anode and ionic liquid electrolyte using reactive molecular dynamics simulations is provided. A ≈10 nm thick SEI composed of a dense ordered inorganic layer near the Li‐metal anode and a porous organic layer near the electrolyte is found. These results provide new insights into a deeper understanding of the complex SEI that should be useful in developing a new generation of highly efficient batteries.

     
    more » « less