One of the best magneto‐optical claddings for optical isolators in photonic integrated circuits is sputter deposited cerium‐doped terbium iron garnet (Ce:TbIG) which has a large Faraday rotation (≈−3500° cm−1at 1550 nm). Near‐ideal stoichiometry of Ce0.5Tb2.5Fe4.75O12is found to have a 44 nm magnetic dead layer that can impede the interaction of propagating modes with garnet claddings. The effective anisotropy of Ce:TbIG on Si is also important, but calculations using bulk thermal mismatch overestimate the effective anisotropy. Here, X‐ray diffraction measurements yield highly accurate measurements of strain that show anisotropy favors an in‐plane magnetization in agreement with the positive magnetostriction of Ce:TbIG. Upon doping TbIG with Ce, a slight decrease in compensation temperature occurs which points to preferential rare‐earth occupation in dodecahedral sites and an absence of cation redistribution between different lattice sites. The high Faraday rotation, large remanent ratio, large coercivity, and preferential in‐plane magnetization enable Ce:TbIG to be an in‐plane latched garnet, immune to stray fields with magnetization collinear to direction of light propagation.
Complex oxide films stabilized by epitaxial growth can exhibit large populations of point defects which have important effects on their properties. The site occupancy of pulsed laser‐deposited epitaxial terbium iron garnet (TbIG) films with excess terbium (Tb) is analyzed, in which the terbium:iron (Tb:Fe)ratio is 0.86 compared to the stoichiometric value of 0.6. The magnetic properties of the TbIG are sensitive to site occupancy, exhibiting a higher compensation temperature (by 90 K) and a lower Curie temperature (by 40 K) than the bulk Tb3Fe5O12garnet. Data derived from X‐ray core‐level spectroscopy, magnetometry, and molecular field coefficient modeling are consistent with occupancy of the dodecahedral sites by Tb3+, the octahedral sites by Fe3+, Tb3+and vacancies, and the tetrahedral sites by Fe3+and vacancies. Energy dispersive X‐ray spectroscopy in a scanning transmission electron microscope provides direct evidence of TbFeantisites. A small fraction of Fe2+is present, and oxygen vacancies are inferred to be present to maintain charge neutrality. Variation of the site occupancies provides a path to considerable manipulation of the magnetic properties of epitaxial iron garnet films and other complex oxides, which readily accommodate stoichiometries not found in their bulk counterparts.
more » « less- Award ID(s):
- 2028199
- NSF-PAR ID:
- 10419017
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Small
- Volume:
- 19
- Issue:
- 30
- ISSN:
- 1613-6810
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract Films of polycrystalline terbium iron garnet (TbIG), cerium‐substituted TbIG (CeTbIG), and bismuth‐substituted TbIG (BiTbIG) are grown on Si substrates by pulsed laser deposition. The films grow under tensile strain due to thermal mismatch with the Si substrate, resulting in a dominant magnetoelastic anisotropy which, combined with shape anisotropy, leads to in‐plane magnetization. TbIG has a compensation temperature of 253 K which is reduced by substitution of Ce and Bi. The Faraday rotation at 1550 nm of the TbIG, Ce0.36TbIG, and Bi0.03TbIG films is 5400 ± 600° cm−1, 4500 ± 100° cm–1, and 6200 ± 300° cm−1, respectively, while Ce0.36TbIG and Bi0.03TbIG exhibit lower optical absorption than TbIG, attributed to a reduction in Fe2+and Tb4+absorption pathways. The high Faraday rotation of the films, and in particular the high magneto‐optical figure of merit of the Bi0.03TbIG of 720° dB−1at 1550 nm, make these polycrystalline films valuable for applications in integrated photonics.
-
more » « less
Abstract Iron nitrides are possible constituents of the cores of Earth and other terrestrial planets. Pressure‐induced magnetic changes in iron nitrides and effects on compressibility remain poorly understood. Here we report synchrotron X‐ray emission spectroscopy (XES) and X‐ray diffraction (XRD) results for ε‐Fe7N3and γ′‐Fe4N up to 60 GPa at 300 K. The XES spectra reveal completion of high‐ to low‐spin transition in ε‐Fe7N3and γ′‐Fe4N at 43 and 34 GPa, respectively. The completion of the spin transition induces stiffening in bulk modulus of ε‐Fe7N3by 22% at ~40 GPa, but has no resolvable effect on the compression behavior of γ′‐Fe4N. Fitting pressure‐volume data to the Birch‐Murnaghan equation of state yields
V 0 = 83.29 ± 0.03 (Å3),K 0 = 232 ± 9 GPa,K 0′ = 4.1 ± 0.5 for nonmagnetic ε‐Fe7N3above the spin transition completion pressure, andV 0 = 54.82 ± 0.02 (Å3),K 0 = 152 ± 2 GPa,K 0′ = 4.0 ± 0.1 for γ′‐Fe4N over the studied pressure range. By reexamining evidence for spin transition and effects on compressibility of other candidate components of terrestrial planet cores, Fe3S, Fe3P, Fe7C3, and Fe3C based on previous XES and XRD measurements, we located the completion of high‐ to low‐spin transition at ~67, 38, 50, and 30 GPa at 300 K, respectively. The completion of spin transitions of Fe3S, Fe3P, and Fe3C induces elastic stiffening, whereas that of Fe7C3induces elastic softening. Changes in compressibility at completion of spin transitions in iron‐light element alloys may influence the properties of Earth's and planetary cores. -
more » « less
Abstract Rare‐earth iron garnets (REIG) have recently become the materials platform of choice for spintronic studies on ferrimagnetic insulators. However, thus far the materials studied have mainly been REIG with a single rare earth species such as thulium, yttrium, or terbium iron garnets. In this study, magnetometry, ferromagnetic resonance, and magneto‐optical Kerr effect imaging is used to explore the continuous variation of magnetic properties as a function of composition for Y
x Tm3−x iron garnet (Yx Tm3−x IG) thin films grown by pulsed laser deposition on gadolinium gallium garnet substrates. It is reported that the tunability of the magnetic anisotropy energy, with full control achieved over the type of anisotropy (from perpendicular, to isotropic, to an in‐plane easy axis) on the same substrate. In addition, a nonmonotonic composition‐dependent anisotropy term is reported, which is ascribed to growth‐induced anisotropy similar to what is reported in garnet thin films grown by liquid‐phase epitaxy. Ferromagnetic resonance shows linear variation of the damping and the g‐factor across the composition range, consistent with prior theoretical work. Domain imaging reveals differences in reversal modes, remanant states, and domain sizes in Yx Tm3−x iron‐garnet thin films as a function of anisotropy. -
more » « less
Abstract Fe‐Al‐bearing bridgmanite may be the dominant host for ferric iron in Earth's lower mantle. Here we report the synthesis of (Mg0.5Fe3+0.5)(Al0.5Si0.5)O3bridgmanite (FA50) with the highest Fe3+‐Al3+coupled substitution known to date. X‐ray diffraction measurements showed that at ambient conditions, the FA50 adopted the LiNbO3structure. Upon compression at room temperature to 18 GPa, it transformed back into the bridgmanite structure, which remained stable up to 102 GPa and 2,600 K. Fitting Birch‐Murnaghan equation of state of FA50 bridgmanite yields
V 0 = 172.1(4) Å3,K 0 = 229(4) GPa withK 0′ = 4(fixed). The calculated bulk sound velocity of the FA50 bridgmanite is ~7.7% lower than MgSiO3bridgmanite, mainly because the presence of ferric iron increases the unit‐cell mass by 15.5%. This difference likely represents the upper limit of sound velocity anomaly introduced by Fe3+‐Al3+substitution. X‐ray emission and synchrotron Mössbauer spectroscopy measurements showed that after laser annealing, ~6% of Fe3+cations exchanged with Al3+and underwent the high‐ to low‐spin transition at 59 GPa. The low‐spin proportion of Fe3+increased gradually with pressure and reached 17–31% at 80 GPa. Since the cation exchange and spin transition in this Fe3+‐Al3+‐enriched bridgmanite do not cause resolvable unit‐cell volume reduction, and the increase of low‐spin Fe3+fraction with pressure occurs gradually, the spin transition would not produce a distinct seismic signature in the lower mantle. However, it may influence iron partitioning and isotopic fractionation, thus introducing chemical heterogeneity in the lower mantle.