Polarization-induced two-dimensional electron gases (2DEGs) in AlN/GaN/AlN quantum well high-electron-mobility transistors on ultrawide bandgap AlN substrates offer a promising route to advance microwave and power electronics with nitride semiconductors. The electron mobility in thin GaN quantum wells embedded in AlN is limited by high internal electric field and the presence of undesired polarization-induced two-dimensional hole gases (2DHGs). To enhance the electron mobility in such heterostructures on AlN, previous efforts have resorted to thick, relaxed GaN channels with dislocations. In this work, we introduce n-type compensation δ-doping in a coherently strained single-crystal (Xtal) AlN/GaN/AlN heterostructure to counter the 2DHG formation at the GaN/AlN interface, and simultaneously lower the internal electric field in the well. This approach yields a δ-doped XHEMT structure with a high 2DEG density of ∼3.2×1013 cm−2 and a room temperature (RT) mobility of ∼855 cm2/Vs, resulting in the lowest RT sheet resistance 226.7 Ω/□ reported to date in coherently strained AlN/GaN/AlN HEMT heterostructures on the AlN platform.
more »
« less
High electron mobility in AlN:Si by point and extended defect management
High room temperature n-type mobility, exceeding 300 cm2/Vs, was demonstrated in Si-doped AlN. Dislocations and CN−1 were identified as the main compensators for AlN grown on sapphire and AlN single crystalline substrates, respectively, limiting the lower doping limit and mobility. Once the dislocation density was reduced by the growth on AlN wafers, C-related compensation could be reduced by controlling the process supersaturation and Fermi level during growth. While the growth on sapphire substrates supported only high doping ([Si] > 5 × 1018 cm−3) and low mobility (∼20 cm2/Vs), growth on AlN with proper compensation management enabled controlled doping at two orders of magnitude lower dopant concentrations. This work is of crucial technological importance because it enables the growth of drift layers for AlN-based power devices.
more »
« less
- PAR ID:
- 10439909
- Publisher / Repository:
- American Institute of Physics
- Date Published:
- Journal Name:
- Journal of Applied Physics
- Volume:
- 132
- Issue:
- 18
- ISSN:
- 0021-8979
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
-
To enhance the electron mobility in quantum-well high-electron-mobility transistors (QW HEMTs), we investigate the transport properties in AlN/GaN/AlN heterostructures on Al-polar single-crystal AlN substrates. Theoretical modeling combined with experiment shows that interface roughness scattering due to high electric field in the quantum well limits mobility. Increasing the width of the quantum well to its relaxed form reduces the internal electric field and scattering, resulting in a binary QW HEMT with a high two-dimensional electron gas (2DEG) density of 3.68×1013 cm–2, a mobility of 823 cm2/Vs, and a record-low room temperature (RT) sheet resistance of 206 Ω/□. Further reduction of the quantum well electric field yields a 2DEG density of 2.53×1013 cm–2 and RT mobility > 1000 cm2/V s. These findings will enable future developments in high-voltage and high-power microwave applications on the ultrawide bandgap AlN substrate platform.more » « less
-
The polarization difference and band offset between Al(Ga)N and GaN induce two-dimensional (2D) free carriers in Al(Ga)N/GaN heterojunctions without any chemical doping. A high-density 2D electron gas (2DEG), analogous to the recently discovered 2D hole gas in a metal-polar structure, is predicted in a N-polar pseudomorphic GaN/Al(Ga)N heterostructure on unstrained AlN. We report the observation of such 2DEGs in N-polar undoped pseudomorphic GaN/AlGaN heterostructures on single-crystal AlN substrates by molecular beam epitaxy. With a high electron density of ∼4.3 ×1013/cm2 that maintains down to cryogenic temperatures and a room temperature electron mobility of ∼450 cm2/V s, a sheet resistance as low as ∼320 Ω/◻ is achieved in a structure with an 8 nm GaN layer. These results indicate significant potential of AlN platform for future high-power RF electronics based on N-polar III-nitride high electron mobility transistors.more » « less
-
Ultra-wide bandgap (UWBG) Al0.65Ga0.35N channel high electron mobility transistors (HEMTs) were deposited using a close-coupled showerhead metal-organic chemical vapor deposition reactor on AlN-on-sapphire templates to investigate the effect of transport properties of the two-dimensional electron gas (2DEG) on the epitaxial structure design. The impact of various scattering phenomena on AlGaN channel HEMTs was analyzed with respect to the channel, buffer, and AlN interlayer design, revealing that the alloy disorder and ionized impurity scattering mechanisms were predominant, limiting the mobility of 2DEG up to 180 cm2/Vs for a sheet charge density of 1.1 × 1013 cm−2. A surface roughness of <1 nm (2 μm × 2 μm atomic force microscopy scan) was achieved for the epitaxial structures demonstrating superior crystalline quality. The fabricated HEMT device showed state-of-the-art contact resistivity (ρc = 8.35 × 10^−6 Ω · cm2), low leakage current (<10^−6 A/mm), high ION/IOFF ratio (>10^5), a breakdown voltage of 2.55 kV, and a Baliga's figure of merit of 260 MW/cm2. This study demonstrates the optimization of the structural design of UWBG AlGaN channel HEMTs and its effect on transport properties to obtain state-of-the-art device performance.more » « less
-
Comparative Spectroscopic Study of Aluminum Nitride Grown by MOCVD in H2 and N2 Reaction EnvironmentWe report a comparative spectroscopic study on the thin films of epitaxial aluminum nitride (AlN) on basal plane sapphire (Al2O3) substrates grown in hydrogen (H2) and nitrogen (N2) gas reaction environments. AlN films of similar thicknesses (~3.0 µm) were grown by metal-organic chemical vapor deposition (MOCVD) for comparison. The impact of the gas environment on the AlN epilayers was characterized using high-resolution X-ray diffraction (HR-XRD), X-ray photoelectron spectroscopy (XPS), Raman scattering (RS), secondary ion mass spectroscopy (SIMS), cathodoluminescence (CL), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The study showed that AlN layers grown in a N2 environment have 50% less stress (~0.5 GPa) and similar total dislocation densities (~109/cm2) as compared to the films grown in a H2 environment. On the other hand, AlN films grown in a H2 gas environment have about 33% lesser carbon and 41% lesser oxygen impurities than films grown in a N2 growth environment. The possible mechanisms that influenced the structural quality and impurity incorporation for two different gas environments to grow AlN epilayers in the MOCVD system on sapphire substrates were discussed.more » « less