Title: Surface Pressure-Area Mechanics of Water-Spread Block Copolymer Micelle Monolayers at the Air-Water Interface: Effect of Hydrophobic Block Chemistry
Amphiphilic block copolymer micelles can mimic the ability of natural lung surfactant to reduce the air–water interfacial tension down close to zero and prevent the Laplace pressure-induced alveolar collapse. In this work, we investigated the air–water interfacial behaviors of polymer micelles derived from eight different poly(ethylene glycol)(PEG)-based block copolymers having different hydrophobic block chemistries to elucidate the effect of the core block chemistry on the surface mechanics of the block copolymer micelles. Aqueous micelles of about 30 nm in hydrodynamic diameter were prepared from the PEG-based block copolymers via equilibrium nanoprecipitation and spread on water surface using water as the spreading medium. Surface pressure–area isotherm and quantitative Brewster angle microscopy measurements were performed to investigate how the micelle/monolayer structures change during lateral compression of the monolayer; widely varying structural behaviors were observed, including wrinkling/collapse of micelle monolayers, and deformation and/or desorption of individual micelles. By bivariate correlation regression analysis of surface pressure-area isotherm data, it was found that the rigidity and hydrophobicity of the hydrophobic core domain, which are quantified by glass transition temperature (Tg) and water contact angle (θ) measurements, respectively, are coupled factors that need to be taken into account concurrently in order to control the surface mechanical properties of polymer micelle monolayers; micelles having rigid and strongly hydrophobic cores exhibited high surface pressure and high compressibility modulus under high compression. High surface pressure and high compressibility modulus were also found to be correlated with the formation of wrinkles in the micelle monolayer (visualized by Brewster angle microscopy). From this study, we conclude that polymer micelles based on hydrophobic block materials having higher Tg and θ are more suitable for surfactant replacement therapy applications which require the therapeutic surfactant to produce high surface pressure and modulus at the alveolar air–water interface.  more » « less
Award ID(s):
2211843
NSF-PAR ID:
10448621
Author(s) / Creator(s):
; ; ; ; ;
Date Published:
Journal Name:
Langmuir
ISSN:
0743-7463
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    The effect of vortex‐induced mechanical stresses on the fluorescent properties of dye‐containing poly(ethylene glycol)‐block‐poly(lactic acid) (PEG‐b‐PLA) block copolymer micelles has been investigated. PEG‐b‐PLA block copolymer micelles containing fluorescent dyes, 3,3′‐dioctadecyloxacarbocyanine perchlorate (DiO) and/or 1,1′‐dioctadecyl‐3,3,3′,3′‐tetramethylindocarbocyanine perchlorate (DiI), are prepared by a simple one‐step procedure that involves the self‐assembly of block copolymers and spontaneous incorporation of hydrophobic dyes into the core of the micelles. Upon vortexing, the micelle dispersion samples showed a decrease in fluorescence intensity in a rotational speed‐ and time‐dependent manner. The results demonstrated that the vortexing can alter the fluorescent properties of the dye‐containing PEG‐b‐PLA block copolymer micelle dispersion samples, suggesting the potential utility of block copolymer micelles as a mechanical stress‐responsive nanomaterial.

     
    more » « less
  2. Abstract

    Aqueous self‐assembly of amphiphilic block copolymers form diverse nanostructured morphologies depending on block volume fraction and solvophilicity. Stimuli‐responsive motifs have been combined with self‐assembled micelles to afford spatiotemporal, on‐demand encapsulation and payload release. However, the role of modular polymer architecture (i.e., bottlebrushes) in stimuli‐responsive aqueous self‐assembly is not fully understood. The synthesis, aqueous self‐assembly, and photoirradiation of photolabile, amphiphilic bottlebrush block copolymers is presented herein. Specifically, the efficient photoscission ofo‐nitrobenzene motifs at the junction of a poly(norborneneo‐nitrobenzene polystyrene)‐block‐poly(norbornene polyethylene glycol) diblock bottlebrush side chain and backbone cleaved away hydrophobic polystyrene side chains and artificially increased the volume fraction of poly(ethylene glycol) (fPEG). In doing so, self‐assembled micelles readily degrade to micelle‐to‐micelle and micelle‐to‐aggregate structures after photoirradiation. Finally, this bottlebrush micelle system is used to demonstrate the efficient encapsulation and stimuli‐responsive release of Nile Red that is monitored by fluorescence spectroscopy and dynamic light scattering. The contribution of this work expands the utility of amphiphilic bottlebrush systems as highly efficient and responsive, hierarchically assembled nanomaterials.

     
    more » « less
  3. null (Ed.)
    Recent developments in the field of polymer vesicles, i.e. polymersomes, have demonstrated that disrupting the equilibrium conditions of the milieu could lead to shape transformation into stable non-spherical morphologies, bringing on-demand shape control to reality and bearing great promise for cell mimicry and a variety of biomedical applications. Here, we studied the self-assembly behavior of glassy amphiphilic triblock copolymers, poly(ethylene glycol)- block -polystyrene- stat -poly(coumarin methacrylate)- block -poly(ethylene glycol) (PEG- b -P(S- stat -CMA)- b -PEG), and their response to various stimuli. By changing the respective molecular weights of both the hydrophobic P(S- stat -CMA) and the hydrophilic PEG blocks, we varied the hydrophobic volume fraction thereby accessing a range of morphologies from spherical and worm-like micelles, as well as polymersomes. For the latter, we observed that slow osmotic pressure changes induced by dialysis led to a decrease in size while rapid osmotic pressure changes by addition of a PEG fusogen led to morphological transformations into rod-like and tubular polymersomes. We also found out that chemically crosslinking the vesicles before inducing osmotic pressure changes led to the vesicles exhibiting hypotonic shock, atypical for glassy polymersomes. We believe that this approach combining the robustness of triblock copolymers and light-based transformations will help expand the toolbox to design ever more complex biomimetic constructs. 
    more » « less
  4. The morphology of self-assembled block copolymer aggregates is highly dependent on the relative volume fraction of the hydrophobic block. Thus, a dramatic change in the volume fraction of the hydrophobic block can elicit on-demand morphological transitions. Herein, a novel hydrophobic monomer containing a photolabile nitrobenzyl (Nb) protecting group was synthesized and incorporated into a block copolymer with poly(ethylene glycol) methacrylate. This motif allows for the hydrophobic volume fraction of the amphiphilic block copolymer to be dramatically reduced in situ to induce a morphological transition upon irradiation with UV light. Two amphiphilic block copolymers, Nb 94 and Nb 176, with hydrophobic weight fractions of 80% and 86%, respectively, were synthesized and their self-assembly in water studied. Nb 94 assembled into vesicles with R h = 235 nm and underwent a morphological transition after 21 minutes of UV irradiation to spherical micelles with R h = 27 nm, determined by dynamic light scattering and confirmed by transmission electron microscopy. At intermediate irradiation times (14–20 min), Nb 94 vesicles swelled to a larger size, but underwent a morphological transition over the course of hours or days, depending on the exact irradiation time. Nb 176 assembled into large compound vesicles with a hydrodynamic radius ( R h ) of 973 nm, as determined by dynamic light scattering (DLS), which decreased to ca. 700 nm after 300 minutes of UV irradiation with no apparent morphological transition. This study elucidates the mechanism and kinetics of the morphological transitions of block copolymer assemblies induced by a change in the hydrophobic volume fraction of the polymer. 
    more » « less
  5. Micelle fragmentation, one of the key mechanisms responsible for equilibration of kinetically trapped micelles, is investigated for block copolymer micelles in ionic liquids. In particular, the role of driving force for micelle fragmentation is studied by altering the solvent quality after micelle preparation, amounting to a jump in interfacial tension γ between solvent and the micelle core. Direct dissolution of a 1,2-polybutadiene-b-poly(ethylene oxide) copolymer (Mn = 17.5 kDa and fPEO = 0.38) in the ionic liquid [C2mim][TFSI] results in large micelles with average size 〖"〈" "R" _"h" "〉" 〗_"∘" " ≈ 68" nm and dispersity "Đ ≈ 1.27" . The solution of the as-prepared micelles is then diluted by the careful addition of a second ionic liquid [C10mim][TFSI] having lower γ with the micelle core, such that the micelles remain unaffected. The γ and hence the quality of the solvent mixture was controlled by the degree of dilution. The choice of the second solvent is based on the measurement of γ for a series of [Cxmim][TFSI] ILs with 1-2-polybutadiene homopolymer, carried out using a pendant drop test. Diluting the micelles by adding another ionic liquid with lower γ tends to decrease the equilibrium micelle size which, in turn, enhances the driving force for fragmentation of the bigger as-prepared micelles, represented by increase in the ratio of aggregation numbers Q/Qeq. Subjecting the diluted micellar solution to temperature-jump to 170 °C followed by thermal annealing leads to fragmentation of the as-prepared micelles to attain a near-equilibrium state. The micelles are characterized using in-situ dynamic light scattering technique to observe the time evolution of average micelle size, from which the relaxation time is obtained. Additionally, small-angle X-ray scattering and cryogenic transmission electron microscopy measurements were carried out to obtain the micelle core size and distribution in the micellar solutions before and after fragmentation. The enhancement in the driving force achieved by controlling the amount of low γ solvent resulted in faster fragmentation; the characteristic fragmentation time decreases monotonically on increasing the size ratio Q/Qeq from 1.2 to 5. 
    more » « less