Title: Contiguous and Atomically Thin Pt Film with Supra‐Bulk Behavior Through Graphene‐Imposed Epitaxy
Abstract

The nature of the atomic configuration and the bonding within epitaxial Pt‐graphene films is investigated. Graphene‐templated monolayer/few‐multilayers of Pt, synthesized as contiguous 2D films by room temperature electrochemical methods, is shown to exhibit a stable {100} structure in the 1–2 layer range. The fundamental question being investigated is whether surface Pt atoms rendered in these 2D architectures are as stable as those of their bulk Pt counterparts. Unsurprisingly, a single layer Pt on the graphene (Pt_1ML/GR) shows much larger Pt dissociation energy (−7.51 eV) than does an isolated Pt atom on graphene. However, the dissociation energy from Pt_1ML/GR is similar to that of bulk Pt(100), −7.77 eV, while in bi‐layer Pt on the graphene (Pt_2ML/GR), this energy changes to −8.63 eV, surpassing its bulk counterpart. At Pt_2ML/GR, the dissociation energy also slightly surpasses that of bulk Pt(111). Bulk‐like stability of atomically thin Pt–graphene results from a combination of interplanar PtC covalent bonding and inter/intraplanar metallic bonding. This unprecedented stability is also accompanied by a metal‐like presence of electronic states at the Fermi level. Such atomically thin metal‐graphene architectures can be a new stable platform for synthesizing 2D metallic films with various applications in catalysis, sensing, and electronics.

 
more » « less
PAR ID:
10453784
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Functional Materials
Volume:
29
Issue:
46
ISSN:
1616-301X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Gate-tunable spin-dependent properties could be induced in graphene at room temperature through the magnetic proximity effect by placing it in contact with a metallic ferromagnet. Because strong chemical bonding with the metallic substrate makes gating ineffective, an intervening passivation layer is needed. Previously considered passivation layers result in a large shift of the Dirac point away from the Fermi level, so that unrealistically large gate fields are required to tune the spin polarization in graphene (Gr). We show that a monolayer of Au or Pt used as the passivation layer between Co and graphene brings the Dirac point closer to the Fermi level. In the Co/Pt/Gr system the proximity-induced spin polarization in graphene and its gate control are strongly enhanced by the presence of a surface band near the Fermi level. Furthermore, the shift of the Dirac point could be eliminated entirely by selecting submonolayer coverage in the passivation layer. Our findings open a path towards experimental realization of an optimized two-dimensional system with gate-tunable spin-dependent properties. 
    more » « less
  2. Abstract

    Atomically thin 2D materials are good templates to grow organic semiconductor thin films with desirable features. However, the 2D materials typically exhibit surface roughness and spatial charge inhomogeneity due to nonuniform doping, which can affect the uniform assembly of organic thin films on the 2D materials. A hybrid template is presented for preparation of highly crystalline small‐molecule organic semiconductor thin film that is fabricated by transferring graphene onto a highly ordered self‐assembled monolayer. This hybrid graphene template has low surface roughness and spatially uniform doping, and it yields highly crystalline fullerene thin films with grain sizes >300 nm, which is the largest reported grain size for C60thin films on 2D materials. A graphene/fullerene/pentacene phototransistor fabricated directly on the hybrid template has five times higher photoresponsivity than a phototransistor fabricated on a conventional graphene template supported by a SiO2wafer.

     
    more » « less
  3. Abstract

    Over the past decades, the design of active catalysts has been the subject of intense research efforts. However, there has been significantly less deliberate emphasis on rationally designing a catalyst system with a prolonged stability. A major obstacle comes from the ambiguity behind how catalyst degrades. Several degradation mechanisms are proposed in literature,   but with a lack of systematic studies, the causal relations between degradation and those proposed mechanisms remain ambiguous. Here, a systematic study of a catalyst system comprising of small particles and single atoms of Pt sandwiched between graphene layers, GR/Pt/GR, is studied to  unravel the degradation mechanism of the studied electrocatalyst for oxygen reduction reaction(ORR). Catalyst suffers from atomic dissolution under ORR harsh acidic and oxidizing operation voltages. Single atoms trapped in point defects within the top graphene layer on their way hopping through toward the surface of GR/Pt/GR architecture. Trapping mechanism renders individual Pt atoms as single atom catalyst sites catalyzing ORR for thousands of cycles before washed away in the electrolyte. The GR/Pt/GR catalysts also compare favorably to state‐of‐the‐art commercial Pt/C catalysts and demonstrates a rational design of a hybrid nanoarchitecture with a prolonged stability for thousands of operation cycles.

     
    more » « less
  4. Ultrathin and two-dimensional (2D) metals can support strong plasmons, with concomitant tight field confinement and large field enhancement. Accordingly, 2D-metal nanostructures exhibiting plasmonic resonances are highly sensitive to the environment and intrinsically suitable for optical sensing. Here, based on a proof-of-concept numerical study, nano-engineered ultrathin 2D-metal films that support infrared plasmons are demonstrated to enable highly responsive refractive index (RI) sensing. For 3 nm-Au nanoribbons exhibiting plasmonic resonances at wavelengths around 1600 nm, a RI sensitivity of SRI > 650 nm per refractive index unit (RIU) is observed for a 100 nm-thick analyte layer. A parametric study of the 2D-Au system indicates the strong dependence of the RI sensitivity on the 2D-metal thickness. Furthermore, for an analyte layer as thin as 1 nm, a RI sensitivity up to 110 (90 nm/RIU) is observed in atomically thin 2D-In (2D-Ga) nanoribbons exhibiting highly localized plasmonic resonances at mid-infrared wavelengths. Our results not only reveal the extraordinary sensing characteristics of 2D-metal systems but also provide insight into the development of 2D-metal-based plasmonic devices for enhanced IR detection.

     
    more » « less
  5. Abstract

    This study reports successful deposition of high quantum efficiency (QE) bialkali antimonide K2CsSb photocathodes on graphene films. The results pave the way for an ultimate goal of encapsulating technologically relevant photocathodes for accelerator technology with an atomically thin protecting layer to enhance lifetime while minimizing QE losses. A QE of 17% at ≈3.1 eV (405 nm) is the highest value reported so far on graphene substrates and is comparable to that obtained on stainless steel and nickel reference substrates. The spectral responses of the photocathodes on graphene exhibit signature features of K2CsSb including the characteristic absorption at ≈2.5 eV. Materials characterization based on X‐ray fluorescence and X‐ray diffraction reveals that the composition and crystal quality of these photocathodes deposited on graphene is comparable to those deposited on a reference substrate. Quantitative agreement between optical calculations and QE measurements for the K2CsSb on free suspended graphene and a graphene‐coated metal substrate further confirms the high‐quality interface between the photocathodes and graphene. Finally, a correlation between the QE and graphene quality as characterized by Raman spectroscopy suggests that a lower density of atomistic defects in the graphene films leads to higher QE of the deposited K2CsSb photocathodes.

     
    more » « less