For wearable and implantable electronics applications, developing intrinsically stretchable polymer semiconductor is advantageous, especially in the manufacturing of large‐area and high‐density devices. A major challenge is to simultaneously achieve good electrical and mechanical properties for these semiconductor devices. While crystalline domains are generally needed to achieve high mobility, amorphous domains are necessary to impart stretchability. Recent progresses in the design of high‐performance donor–acceptor polymers that exhibit low degrees of energetic disorder, while having a high fraction of amorphous domains, appear promising for polymer semiconductors. Here, a low crystalline, i.e., near‐amorphous, indacenodithiophene‐
The backbone of diketopyrrolopyrrole‐thiophene‐vinylene‐thiophene‐based polymer semiconductors (PSCs) is modified with pyridine (Py) or bipyridine ligands to complex Fe(II) metal centers, allowing the metal–ligand complexes to act as mechanophores and dynamically crosslink the polymer chains. Mono‐ and bi‐dentate ligands are observed to exhibit different degrees of bond strengths, which subsequently affect the mechanical properties of these Wolf‐type‐II metallopolymers. The counter ion also plays a crucial role, as it is observed that Py‐Fe mechanophores with non‐coordinating BPh4–counter ions (Py‐FeB) exhibit better thin film ductility with lower elastic modulus, as compared to the coordinating chloro ligands (Py‐FeC). Interestingly, besides mechanical robustness, the electrical charge carrier mobility can also be enhanced concurrently when incorporating Py‐FeB mechanophores in PSCs. This is a unique observation among stretchable PSCs, especially that most reports to date describe a decreased mobility when the stretchability is improved. Next, it is determined that improvements to both mobility and stretchability are correlated to the solid‐state molecular ordering and dynamics of coordination bonds under strain, as elucidated via techniques of grazing‐incidence X‐ray diffraction and X‐ray absorption spectroscopy techniques, respectively. This study provides a viable approach to enhance both the mechanical and the electronic performance of polymer‐based soft devices.
more » « less- NSF-PAR ID:
- 10453880
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 31
- Issue:
- 11
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract co ‐benzothiadiazole (IDTBT) polymer and a semicrystalline thieno[3,2‐b ]thiophene‐diketopyrrolopyrrole (DPPTT) are compared, for mechanical properties and electrical performance under strain. It is observed that IDTBT is able to achieve both a high modulus and high fracture strain, and to preserve electrical functionality under high strain. Next, fully stretchable transistors are fabricated using the IDTBT polymer and observed mobility ≈0.6 cm2V−1s−1at 100% strain along stretching direction. In addition, the morphological evolution of the stretched IDTBT films is investigated by polarized UV–vis and grazing‐incidence X‐ray diffraction to elucidate the molecular origins of high ductility. In summary, the near‐amorphous IDTBT polymer signifies a promising direction regarding molecular design principles toward intrinsically stretchable high‐performance polymer semiconductor. -
more » « less
Abstract With the aim of constructing hydrogen‐bonding networks in synthetic complexes, two new ligands derived from
cis,cis ‐1,3,5‐triaminocyclohexane (TACH) have been prepared that feature pendant pyrrole or indole rings as outer‐sphere H‐bond donors. The TACH framework offers a facial arrangement of threeN ‐donors, thereby mimicking common coordination motifs in the active sites of nonheme Fe and Cu enzymes. X‐ray structural characterization of a series of CuI‐X complexes (X=F, Cl, Br, NCS) revealed that these neutral ligands (H3LR, R=pyrrole or indole) coordinate in the intended facialN 3manner, yielding four‐coordinate complexes with idealizedC 3symmetry. The N−H units of the outer‐sphere heterocycles form a hydrogen‐bonding cavity around the axial (pseudo)halide ligand, as verified by crystallographic, spectroscopic, and computational analyses. Treatment of H3Lpyrroleand H3Lindolewith divalent transition metal chlorides (MIICl2, M=Fe, Cu, Zn) causes one heterocycle to deprotonate and coordinate to the M(II) center, giving rise to tetradentate ligands with two remaining outer‐sphere H‐bond donors. Further ligand deprotonation is observed upon reaction with Ni(II) and Cu(II) salts with weakly coordinating counteranions. The reported complexes highlight the versatility of TACH‐based ligands with pendant H‐bond donors, as the resulting scaffolds can support multiple protonation states, coordination geometries, and H‐bonding interactions. -
more » « less
Abstract The crystal structures of the charge‐transfer (CT) cocrystals formed by the π‐electron acceptor 1,3,4,5,7,8‐hexafluoro‐11,11,12,12‐tetracyanonaphtho‐2,6‐quinodimethane (F6TNAP) with the planar π‐electron‐donor molecules triphenylene (TP), benzo[
b ]benzo[4,5]thieno[2,3‐d ]thiophene (BTBT), benzo[1,2‐b :4,5‐b ′]dithiophene (BDT), pyrene (PY), anthracene (ANT), and carbazole (CBZ) have been determined using single‐crystal X‐ray diffraction (SCXRD), along with those of two polymorphs of F6TNAP. All six cocrystals exhibit 1:1 donor/acceptor stoichiometry and adopt mixed‐stacking motifs. Cocrystals based on BTBT and CBZ π‐electron donor molecules exhibit brickwork packing, while the other four CT cocrystals show herringbone‐type crystal packing. Infrared spectroscopy, molecular geometries determined by SCXRD, and electronic structure calculations indicate that the extent of ground‐state CT in each cocrystal is small. Density functional theory calculations predict large conduction bandwidths and, consequently, low effective masses for electrons for all six CT cocrystals, while the TP‐, BDT‐, and PY‐based cocrystals are also predicted to have large valence bandwidths and low effective masses for holes. Charge‐carrier mobility values are obtained from space‐charge limited current (SCLC) measurements and field‐effect transistor measurements, with values exceeding 1 cm2V−1s1being estimated from SCLC measurements for BTBT:F6TNAP and CBZ:F6TNAP cocrystals. -
more » « less
Abstract Nonconjugated segments in polymer semiconductors have been utilized to improve the processability of semiconducting polymers. Recently, several reports have described the improvement of stretchability of polymer semiconductors by incorporating nonconjugated spacers. However, the effect of relative flexibility of such conjugation breakers on mechanical and electrical properties has not yet been studied systematically. Here, conjugation breakers with different chain length and rigidity are incorporated into the backbone of diketopyrrolopyrrole‐based semiconductors. Interestingly, it is observed that the longer and more flexible conjugation breakers result in greater ductility and lower elastic modulus without significantly affecting mobility. The enhancement of stretchability is attributed to the reduced modulus and the decrease in crystallinity, as confirmed by X‐ray diffraction. With this newly established molecular design, transistors are prepared with a semiconducting polymer containing dodecyl segments as conjugation breakers. It is observed that this polymer retains a mobility of >0.36 cm2V−1s−1at 100% strain, and after 100 cycles at 50% strain. Finally, its high stability against strain is also observed with a fully stretchable transistor fabricated. Taken together, the above results indicate that molecular engineering of conjugated polymers, i.e., by incorporating suitable conjugation breakers, can effectively tune mechanical properties without significantly compromising their electrical properties.
-
more » « less
Abstract Electrochemical reduction of carbon dioxide (CO2RR) to value‐added products is a promising strategy to alleviate the greenhouse gas effect. Molecular catalysts, such as cobalt (II) phthalocyanine (CoPc), are known to be efficient electrocatalysts that are capable of converting CO2into carbon monoxide (CO). Herein, we report an axial modification strategy to enhance CoPc's CO2RR performance. After coordinating with axial ligands, the electron density of Co was depleted via π‐backbonding. This π‐backbonding weakened the Co‐CO bond, resulting in rapid desorption of CO. Also, the presence axial ligands elevated the Co dz2orbital energy, resulting in a significantly enhanced CO selectivity, evidenced by an increased faradaic efficiency (FE) from 82 % (CoPc) to 91 % and 94 % with the presence of pyridine (CoPc‐py) and imidizal ligands (CoPc‐im), respectively, at −0.82 V vs. RHE. Density functional theory calculations reveal that axial ligation of CoPc can reduce the energy barrier for CO2activation and facilitate the formation of*COOH.