An ultra-thin overcoating of zirconium oxide (ZrO2) film on CuO-ZnO-Al2O3(CZA) catalysts by atomic layer deposition (ALD) was proved to enhance the catalytic performance of CZA/HZSM-5 (H form of Zeolite Socony Mobil-5) bifunctional catalysts for hydrogenation of CO2to dimethyl ether (DME). Under optimal reaction conditions (i.e. 240 °C and 2.8 MPa), the yield of product DME increased from 17.22% for the bare CZA/HZSM-5 catalysts, to 18.40% for the CZA catalyst after 5 cycles of ZrO2ALD with HZSM-5 catalyst. All the catalysts modified by ZrO2ALD displayed significantly improved catalytic stability of hydrogenation of CO2to DME reaction, compared to that of CZA/HZSM-5 bifunctional catalysts. The loss of DME yield in 100 h of reaction was greatly mitigated from 6.20% (loss of absolute value) to 3.01% for the CZA catalyst with 20 cycles of ZrO2ALD overcoating. Characterizations including hydrogen temperature programmed reduction, x-ray powder diffraction, and x-ray photoelectron spectroscopy revealed that there was strong interaction between Cu active centers and ZrO2.
Comprehensive treatment of indoor contaminants such as volatile organic compounds (VOCs) and fine particulate matter (PM2.5) using transition metal oxide catalysts or functional fibrous filters has gained substantial attention recently. However, coupling VOC oxidation catalysts into high‐performance filter systems remains a challenge. Herein, an overall solution to strongly bind manganese dioxide (MnO2) nanocrystals onto polypropylene (PP) nonwoven fabrics is provided. For the first time, uniform heterogeneous nucleation and growth of MnO2onto PP nonwoven fabrics using intermediate inorganic nucleation films, including Al2O3, TiO2, and ZnO, formed conformally on the fabrics via atomic layer deposition (ALD) are demonstrated. How different ALD thin films influence the crystallinity, morphology, surface area, and surface oxygen species of the MnO2grown ALD‐coated PP fibers is further investigated. In addition to uniformity and integrity, ZnO thin films give rise to MnO2crystals with the largest fraction of available surface oxygen, enabling 99.5% catalytic oxidation of formaldehyde within 60 min. Moreover, the metal oxide filters provide excellent PM removal efficiencies (
- PAR ID:
- 10455757
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 30
- Issue:
- 42
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract Understanding the chemical mechanisms at play in atomic layer deposition (ALD) is critical for effective process development and expansion of ALD into more complex classes of materials. In this work, a mechanistic study of iron oxide deposited by ALD using
tert ‐butylferrocene and ozone as reactants is performed. Iron oxide ALD using ozone is a useful model system for mechanistic studies due to the prevalence of ozone‐based ALD processes and the uses of iron oxide in ternary and quaternary metal oxides. Results show that saturation conditions require significantly greater exposures of both reactants than is typically reported in the literature, and growths per cycle of greater than one monolayer of Fe2O3per cycle are observed and explained. A growth mechanism is proposed whereby increased ozone exposure results in uptake of superstoichiometric oxygen into the film. X‐ray characterizations reveal the presence of excess oxygen stored near the surface of films deposited with larger ozone exposures and show that increased ozone exposures cause crystalline domain rearrangement and conversion of the film from the γ‐maghemite phase to the α‐hematite phase. The mechanism described here has implications for the wider class of ozone‐based ALD processes, and potential applications of this growth phenomenon are discussed. -
more » « less
Abstract Converting CO2to value‐added chemicals,
e. g ., CH3OH, is highly desirable in terms of the carbon cycling while reducing CO2emission from fossil fuel combustion. Cu‐based nanocatalysts are among the most efficient for selective CO2‐to‐CH3OH transformation; this conversion, however, suffers from low reactivity especially in the thermodynamically favored low temperature range. We herein report ultrasmall copper (Cu) nanocatalysts supported on crystalline, mesoporous zinc oxide nanoplate (Cu@m ZnO) with notable activity and selectivity of CO2‐to‐CH3OH in the low temperature range of 200–250 °C. Cu@m ZnO nanoplates are prepared based on the crystal‐crystal transition of mixed Cu and Zn basic carbonates to mesoporous metal oxides and subsequent hydrogen reduction. Under the nanoconfinement of mesopores in crystalline ZnO frameworks, ultrasmall Cu nanoparticles with an average diameter of 2.5 nm are produced. Cu@m ZnO catalysts have a peak CH3OH formation rate of 1.13 mol h−1per 1 kg under ambient pressure at 246 °C, about 25 °C lower as compared to that of the benchmark catalyst of Cu−Zn−Al oxides. Our new synthetic strategy sheds some valuable insights into the design of porous catalysts for the important conversion of CO2‐to‐CH3OH. -
more » « less
Abstract The practical implementation of Li metal batteries is hindered by difficulties in controlling the Li metal plating microstructure. While previous atomic layer deposition (ALD) studies have focused on directly coating Li metal with thin films for the passivation of the electrode–electrolyte interface, a different approach is adopted, situating the ALD film beneath Li metal and directly on the copper current collector. A mechanistic explanation for this simple strategy of controlling the Li metal plating microstructure using TiO2grown on copper foil by ALD is presented. In contrast to previous studies where ALD‐grown layers act as artificial interphases, this TiO2layer resides at the copper–Li metal interface, acting as a nucleation layer to improve the Li metal plating morphology. Upon lithiation of TiO2, a Li
x TiO2complex forms; this alloy provides a lithiophilic surface layer that enables uniform and reversible Li plating. The reversibility of lithium deposition is evident from the champion cell (5 nm TiO2), which displays an average Coulombic efficiency (CE) of 96% after 150 cycles at a moderate current density of 1 mA cm−2. This simple approach provides the first account of the mechanism of ALD‐derived Li nucleation control and suggests new possibilities for future ALD‐synthesized nucleation layers. -
more » « less
Abstract Metal‐halide perovskites show promise as highly efficient solar cells, light‐emitting diodes, and other optoelectronic devices. Ensuring long‐term stability is now a major priority. In this study, an ultrathin (2 nm) layer of polyethylenimine ethoxylated (PEIE) is used to functionalize the surface of C60for the subsequent deposition of atomic layer deposition (ALD) SnO2, a commonly used electron contact bilayer for p–i–n devices. The enhanced nucleation results in a more continuous initial ALD SnO2layer that exhibits superior barrier properties, protecting Cs0.25FA0.75Pb(Br0.20I0.80)3films upon direct exposure to high temperatures (200 °C) and water. This surface modification with PEIE translates to more stable solar cells under aggressive testing conditions in air at 60 °C under illumination. This type of “built‐in” barrier layer mitigates degradation pathways not addressed by external encapsulation, such as internal halide or metal diffusion, while maintaining high device efficiency up to 18.5%. This nucleation strategy is also extended to ALD VO
x films, demonstrating its potential to be broadly applied to other metal oxide contacts and device architectures.