  • Structural colors and physical properties of elytra in the jewel beetle, Chrysochroa fulgidissima , using surface analytical techniques
Title: Structural colors and physical properties of elytra in the jewel beetle, Chrysochroa fulgidissima , using surface analytical techniques

Structural coloration frequently originates from the interaction of light with multilayers of thin films in living organisms. One example where structural colors are created by multilayers is the jewel beetle,Chrysochroa fulgidissima, which has highly iridescent green elytra with longitudinal red stripes. We examine the structure, chemical information, and physical properties of the epicuticle of the jewel beetle by using atomic force microscopy (AFM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), nanoindentation, and time‐of‐flight secondary ion mass spectrometry (ToF‐SIMS). AFM and SEM were used to analyze the surface structures of the green elytra and red stripes of the jewel beetle's wing. SEM and TEM images obtained from the cross‐sectioned cuticle samples of green and red areas indicated that the color arises from interference reflectors and reflectors consist of successive repeating layers of different electronic densities. Nanoindentation results showed that the green area of the elytron possesses a higher hardness and reduced modulus compared with the red area. To analyze the surface of the elytra and to compare multilayers of the green area with those of the red area, mass spectra and depth profiles were acquired by ToF‐SIMS with C60and Ar cluster ion beams. The epicuticle consists of several layers with alternating high and low abundances of inorganic and organic fragment ions, with approximately 16 layers in the green and 12 layers in the red area. Therefore, ToF‐SIMS combined with other analytical techniques indicate that multilayer reflection is a major mechanism of the jewel beetle's iridescence causing structural coloration.

  more » « less
NSF-PAR ID:
10456677
Author(s) / Creator(s):
 ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Surface and Interface Analysis
Volume:
52
Issue:
10
ISSN:
0142-2421
Page Range / eLocation ID:
p. 656-664
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ( , Coatings)
    We report a comparative spectroscopic study on the thin films of epitaxial aluminum nitride (AlN) on basal plane sapphire (Al2O3) substrates grown in hydrogen (H2) and nitrogen (N2) gas reaction environments. AlN films of similar thicknesses (~3.0 µm) were grown by metal-organic chemical vapor deposition (MOCVD) for comparison. The impact of the gas environment on the AlN epilayers was characterized using high-resolution X-ray diffraction (HR-XRD), X-ray photoelectron spectroscopy (XPS), Raman scattering (RS), secondary ion mass spectroscopy (SIMS), cathodoluminescence (CL), atomic force microscopy (AFM), and scanning electron microscopy (SEM). The study showed that AlN layers grown in a N2 environment have 50% less stress (~0.5 GPa) and similar total dislocation densities (~109/cm2) as compared to the films grown in a H2 environment. On the other hand, AlN films grown in a H2 gas environment have about 33% lesser carbon and 41% lesser oxygen impurities than films grown in a N2 growth environment. The possible mechanisms that influenced the structural quality and impurity incorporation for two different gas environments to grow AlN epilayers in the MOCVD system on sapphire substrates were discussed. 
    more » « less
  2. ; ; ; ; ; ; ; ; ( , Advanced Functional Materials)
    Abstract

    A detailed investigation addressing the effects of functionalizing conjugated polymers with oligo(ethylene glycol) (EGn) sidechains on the performance and polymer‐electrolyte compatibility of electrochromic devices (ECDs) is reported. The electrochemistry for a series of donor‐acceptor copolymers having near‐infrared (NIR)‐optical absorption, where the donor fragment is 3,4‐ethylenedioxythiophene (EDOT) or an EGnfunctionalized bithiophene (g2T) and the acceptor fragment is diketopyrrolopyrrole (DPP) functionalized with branched alkyl or EGnsidechains, is extensively probed. ECDs are next fabricated and it is found that EGnsidechain incorporation must be finely balanced to promote polymer‐electrolyte compatibility and provide efficient ion exchange. Proper electrolyte‐cation pairing and polymer structural tuning affords a 2x increase in optical contrast (from 12% to 24%) and >60x reduction in switching time (from 20 to 0.3 s). Atomic force microscopy (AFM)/grazing incidence wide‐angle X‐ray scattering (GIWAXS) characterization of the polymer film morphology/microstructure reveals that an over‐abundance of EGnsidechains generates large polymer crystallites, which can suppress ion exchange. Lastly, time‐of‐flight secondary ion mass spectrometry (ToF‐SIMS) indicates sidechain/electrolyte identity does not influence the electrolyte penetration depth into the films, and EGnsidechain inclusion increases electrolyte cation uptake. The material structural design insight and guidelines regarding the polymer‐electrolyte ion insertion/expulsion dynamics reported here should be of significant utility for developing next‐generation mixed ionic‐electronic conducting materials.

     
    more » « less
  3. ; ; ; ; ; ( , Frontiers in Medicine)
    null (Ed.)
    The dual threats posed by the COVID-19 pandemic and hospital-acquired infections (HAIs) have emphasized the urgent need for self-disinfecting materials for infection control. Despite their highly potent antimicrobial activity, the adoption of photoactive materials to reduce infection transmission in hospitals and related healthcare facilities has been severely hampered by the lack of scalable and cost-effective manufacturing, in which case high-volume production methods for fabricating aPDI-based materials are needed. To address this issue here, we examined the antimicrobial efficacy of a simple bicomponent spray coating composed of the commercially-available UV-photocrosslinkable polymer N -methyl-4(4'-formyl-styryl)pyridinium methosulfate acetal poly(vinyl alcohol) (SbQ-PVA) and one of three aPDI photosensitizers (PSs): zinc-tetra(4- N -methylpyridyl)porphine (ZnTMPyP 4+ ), methylene blue (MB), and Rose Bengal (RB). We applied these photodynamic coatings, collectively termed SbQ-PVA/PS, to a variety of commercially available materials. Scanning electron microscopy (SEM) and time-of-flight secondary ion mass spectrometry (ToF-SIMS) confirmed the successful application of the coatings, while inductively coupled plasma-optical emission spectroscopy (ICP-OES) revealed a photosensitizer loading of 0.09-0.78 nmol PS/mg material. The antimicrobial efficacy of the coated materials was evaluated against methicillin-susceptible Staphylococcus aureus ATCC-29213 and human coronavirus strain HCoV-229E. Upon illumination with visible light (60 min, 400-700 nm, 65 ± 5 mW/cm 2 ), the coated materials inactivated S. aureus by 97-99.999% and HCoV-229E by 92-99.999%, depending on the material and PS employed. Photobleaching studies employing HCoV-229E demonstrated detection limit inactivation (99.999%) even after exposure for 4 weeks to indoor ambient room lighting. Taken together, these results demonstrate the potential for photodynamic SbQ-PVA/PS coatings to be universally applied to a wide range of materials for effectively reducing pathogen transmission. 
    more » « less
  4. ; ; ( , 2019 AISTech Conference Proceedings)
    As more emphasis is placed on thinner gauges and stronger steel grades for more fuel efficient, and crash-worthy vehicles, corrosion becomes a more important consideration. This demand has led to the development of advanced high strength steel (AHSS) grades such as dual-phase (DP) and transformation-induced plasticity (TRIP) aided steels. To protect these steels from corrosion, a hot-dip galvanizing (HDG) or galvannealing (GA) process is employed. However, alloying with Mn and Si can cause complex surface oxides during annealing, which may result in defects in the zinc coating1-8. In order to increase AHSS galvanizability, selective oxidation of alloying elements in DP and TRIP-aided steel needs to be understood. Depending on annealing atmosphere, the mechanism (internal or external) of oxidation can change, as well as the thermodynamic stability of the oxide. Wagner’s theory of oxidation enables prediction of the mechanism of oxidation for binary oxide systems9. The defects can be present after pickling and fluxing, causing wettability issues during the HDG process. Coating defects may also form or be further exacerbated by the galvannealing operation. For this work, oxidation mechanism predictions were performed using Wagner’s theory of oxidation. In the present study a 0.07C-1.9Mn-0.2Si-0.3Cr galvannealed dual-phase steel which exhibited streaking defects in the coating was analyzed. Light optical metallography (LOM) and scanning electron microscopy (SEM) were performed to characterize defects within the galvannealed coating. Static spectra and 3-D profiling using time of flight secondary ion mass spectrometry (TOF-SIMS) was employed. It was found that Mn rich Si containing oxides are present on the steel-coating interface. It does not appear that these oxides affect wettability, however they may have an influence on intermetallic growth during galvannealing. This, combined with an influence from the micro-grooves of the sink roll in the Zn pot, may lead to the streaking defects observed. 
    more » « less
  5. ; ; ; ; ; ; ; ( , Advanced Energy Materials)
    Abstract

    Metal, nitrogen‐doped carbon materials have attracted interest as heterogenous catalysts that contain MNxactive sites that are analogous to molecular catalysts. Of particular interest is Ni,N‐doped carbon, a catalyst that is active for the electrochemical reduction of CO2to CO. Critical to the understanding of these materials is proof of single atomic sites and characterization of the environment surrounding the metal atom; however, directly probing this coordination remains challenging. This challenge is addressed by combining scanning transmission electron microscopy (STEM), single atom electron energy loss spectroscopy (EELS), and time‐of‐flight secondary ion mass spectrometry (ToF‐SIMS). Through STEM imaging, atomic dispersion of Ni in the carbon framework is confirmed and image analyses are utilized to give semiquantitative estimates of neighbor distance distributions and site densities of Ni atoms. Atomic resolution EELS demonstrates that N and Ni are colocated at the single Ni atom sites suggesting Ni–N coordination. ToF‐SIMS reveals a distribution of NiNxCy−fragments that reflect the Ni–N bonding environments within Ni,N‐doped carbon. The fragmentation from Ni,N‐doped carbon is similar to Ni phthalocyanine, suggesting the existence of heterogenized, molecular‐like NiN4active sites which motivates future studies that leverage insight from molecular catalysis design to develop next‐generation heterogeneous catalysts.

     
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email