Organic–inorganic lead halide perovskite solar cells are regarded as one of the most promising technologies for the next generation of photovoltaics due to their high power conversion efficiency (PCE) and simple solution manufacturing. Among the different compositions, the formamidinium lead iodide (FAPbI3) photoactive phase has a bandgap of 1.4 eV, which enables the corresponding higher PCEs according to the Shockley–Queisser limit. However, the photoactive crystal phase of FAPbI3is not stable at room temperature. The most high‐performing compositions to date have reduced this problem by incorporating the methylammonium (MA) cation into the FAPbI3composition, although MA has poor stability at high temperatures and in humid environments, which can limit the lifetime of FA
The two‐step conversion process consisting of metal halide deposition followed by conversion to hybrid perovskite has been successfully applied toward producing high‐quality solar cells of the archetypal MAPbI3hybrid perovskite, but the conversion of other halide perovskites, such as the lower bandgap FAPbI3, is more challenging and tends to be hampered by the formation of hexagonal nonperovskite polymorph of FAPbI3, requiring Cs addition and/or extensive thermal annealing. Here, an efficient room‐temperature conversion route of PbI2into the α‐FAPbI3perovskite phase without the use of cesium is demonstrated. Using in situ grazing incidence wide‐angle X‐ray scattering (GIWAXS) and quartz crystal microbalance with dissipation (QCM‐D), the conversion behaviors of the PbI2precursor from its different states are compared. α‐FAPbI3forms spontaneously and efficiently at room temperature from P2(ordered solvated polymorphs with DMF) without hexagonal phase formation and leads to complete conversion after thermal annealing. The average power conversion efficiency (PCE) of the fabricated solar cells is greatly improved from 16.0(±0.32)% (conversion from annealed PbI2) to 17.23(±0.28)% (from solvated PbI2) with a champion device PCE > 18% due to reduction of carrier recombination rate. This work provides new design rules toward the room‐temperature phase transformation and processing of hybrid perovskite films based on FA+cation without the need for Cs+or mixed halide formulation.
more » « less- NSF-PAR ID:
- 10457679
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Functional Materials
- Volume:
- 30
- Issue:
- 11
- ISSN:
- 1616-301X
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
x MA1−x PbI3films. Csx FA1−x PbI3perovskites are also explored, but despite better stability they still lag in performance. Herein, the additive engineering of MA‐free organic−inorganic lead halide perovskites using divalent cations Sr2+and Ca2+to enhance the performances of Csx FA1−x PbI3perovskite compositions is explored. It is revealed that the addition of up to 0.5% of Sr2+and Ca2+leads to improvements in morphology and reduction in microstrain. The structural improvements observed correlate with improved solar cell performances at low additive concentrations. -
more » « less
Abstract Composition engineering is a particularly simple and effective approach especially using mixed cations and halide anions to optimize the morphology, crystallinity, and light absorption of perovskite films. However, there are very few reports on the use of anion substitutions to develop uniform and highly crystalline perovskite films with large grain size and reduced defects. Here, the first report of employing tetrafluoroborate (BF4−) anion substitutions to improve the properties of (FA = formamidinium, MA = methylammonium (FAPbI3)0.83(MAPbBr3)0.17) perovskite films is demonstrated. The BF4−can be successfully incorporated into a mixed‐ion perovskite crystal frame, leading to lattice relaxation and a longer photoluminescence lifetime, higher recombination resistance, and 1–2 orders magnitude lower trap density in prepared perovskite films and derived solar cells. These advantages benefit the performance of perovskite solar cells (PVSCs), resulting in an improved power conversion efficiency (PCE) of 20.16% from 17.55% due to enhanced open‐circuit voltage (
V OC) and fill factor. This is the highest PCE for BF4−anion substituted lead halide PVSCs reported to date. This work provides insight for further exploration of anion substitutions in perovskites to enhance the performance of PVSCs and other optoelectronic devices. -
more » « less
Abstract Although organic–inorganic hybrid perovskite solar cells (PVSCs) have achieved dramatic improvement in device efficiency, their long‐term stability remains a major concern prior to commercialization. To address this issue, extensive research efforts are dedicated to exploiting all‐inorganic PVSCs by using cesium (Cs)‐based perovskite materials, such as α‐CsPbI3. However, the black‐phase CsPbI3(cubic α‐CsPbI3and orthorhombic γ‐CsPbI3phases) is not stable at room temperature, and it tends to convert to the nonperovskite δ‐CsPbI3phase. Here, a simple yet effective approach is described to prepare stable black‐phase CsPbI3by forming a heterostructure comprising 0D Cs4PbI6and γ‐CsPbI3through tuning the stoichiometry of the precursors between CsI and PbI. Such heterostructure is manifested to enable the realization of a stable all‐inorganic PVSC with a high power conversion efficiency of 16.39%. This work provides a new perspective for developing high‐performance and stable all‐inorganic PVSCs.
-
more » « less
Abstract Molecular I2can be produced from iodide‐based lead perovskites under thermal stress; triiodide, I3−, is formed from this I2and I−. Triiodide attacks protic cation MA+‐ or FA+‐based lead halide perovskites (MA+, methylammonium; FA+, formamidinium) as explicated through solution‐based nuclear magnetic resonance (NMR) studies: triiodide has strong hydrogen‐bonding affinity for MA+or FA+, which leads to their deprotonation and perovskite decomposition. Triiodide is a catalyst for this decomposition that can be obviated through perovskite surface treatment with thiol reducing agents. In contrast to methods using thiol incorporation into perovskite precursor solutions, no penetration of the thiol into the bulk perovskite is observed, yet its surface application stabilizes the perovskite against triiodide‐mediated thermal stress. Thiol applied to the interface between FAPbI3and Spiro‐OMeTAD (“Spiro”) prevents oxidized iodine species penetration into Spiro and thus preserves its hole‐transport efficacy. Surface‐applied thiol affects the perovskite work function; it ameliorates hole injection into the Spiro overlayer, thus improving device performance. It helps to increase interfacial adhesion (“wetting”): fewer voids are observed at the Spiro/perovskite interface if thiols are applied. Perovskite solar cells (PSCs) incorporating interfacial thiol treatment maintain over 80% of their initial power conversion efficiency (PCE) after 300 h of 85 °C thermal stress.
-
more » « less
Abstract Recently, the stability of organic–inorganic perovskite thin films under thermal, photo, and moisture stresses has become a major concern for further commercialization due to the high volatility of the organic cations in the prototype perovskite composition (CH3NH3PbI3). All inorganic cesium (Cs) based perovskite is an alternative to avoid the release or decomposition of organic cations. Moreover, substituting Pb with Sn in the organic–inorganic lead halide perovskites has been demonstrated to narrow the bandgap to 1.2–1.4 eV for high‐performance perovskite solar cells. In this work, a series of CsPb1−
x Snx IBr2perovskite alloys via one‐step antisolvent method is demonstrated. These perovskite films present tunable bandgaps from 2.04 to 1.64 eV. Consequently, the CsPb0.75Sn0.25IBr2with homogeneous and densely crystallized morphology shows a remarkable power conversion efficiency of 11.53% and a highV ocof 1.21 V with a much improved phase stability and illumination stability. This work provides a possibility for designing and synthesizing novel inorganic halide perovskites as the next generation of photovoltaic materials.