Title: In‐situ observation of AlN formation from Ni‐Al solution using an electromagnetic levitation technique
Abstract

Aluminum nitride is a promising substrate material for AlGaN‐based UV‐LED. In order to develop a robust growth processing route for AlN single crystals, fundamental studies of solution growth experiments using Ni‐Al alloy melts as a new solution system were performed. Al can be stably kept in solution the Ni‐Al liquid even at high temperature; in addition, the driving force of the AlN formation reaction from solution can be controlled by solution composition and temperature. To investigate AlN crystal growth behavior we developed an in situ observation system using an electromagnetic levitation technique. AlN formation behavior, including nucleation and growth, was quantitatively analyzed by an image processing pipeline. The nucleation rate of AlN decreased with increasing growth temperature and decreasing aluminum composition. In addition, hexagonal c‐axis oriented AlN crystal successfully grew on the levitated Ni‐40 mol%Al droplet reacted at low driving force (1960 K), on the other hand, AlN crystal with dendritic morphology appeared on the sample with higher driving force (Ni‐50 mol%Al, 1960 K). Thus, the nucleation rate and crystal morphology were dominated by the driving force of the AlN formation reaction.

  more » « less
PAR ID:
10457882
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley-Blackwell
Date Published:
Journal Name:
Journal of the American Ceramic Society
Volume:
103
Issue:
4
ISSN:
0002-7820
Page Range / eLocation ID:
p. 2389-2398
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. ; ; ; ; ; ; ( , Crystals)
    As part of an effort to characterize clusters and intermediate phases likely to be encountered along solution reaction pathways that produce iron and aluminum oxide-hydroxides from Fe and Al precursors, the complete structure of Al10O14(OH)2 (akdalaite) was determined from a combination of single-crystal X-ray diffraction (SC-XRD) data collected at 100 K to define the Al and O positions, and solid-state nuclear magnetic resonance (NMR) and neutron powder diffraction (NPD) data collected at room temperature (~300 K) to precisely determine the nature of hydrogen in the structure. Two different synthesis routes produced different crystal morphologies. Using an aluminum oxyhydroxide floc made from mixing AlCl3 and 0.48 M NaOH, the product had uniform needle morphology, while using nanocrystalline boehmite (Vista Chemical Company Catapal D alumina) as the starting material produced hexagonal plates. Akdalaite crystallizes in the space group P63mc with lattice parameters of a = 5.6244(3) Å and c = 8.8417(3) Å (SC-XRD) and a = 5.57610(2) Å and c = 8.77247(6) Å (NPD). The crystal structure features Al13O40 Keggin clusters. The structural chemistry of akdalaite is nonideal but broadly conforms to that of ferrihydrite, the nanomineral with which it is isostructural. 
    more » « less
  2. ; ; ; ; ; ( , The Journal of Chemical Physics)
    The high density of aluminum nanocrystals (>10 21  m −3 ) that develop during the primary crystallization in Al-based metallic glasses indicates a high nucleation rate (∼10 18  m −3  s −1 ). Several studies have been advanced to account for the primary crystallization behavior, but none have been developed to completely describe the reaction kinetics. Recently, structural analysis by fluctuation electron microscopy has demonstrated the presence of the Al-like medium range order (MRO) regions as a spatial heterogeneity in as-spun Al 88 Y 7 Fe 5 metallic glass that is representative for the class of Al-based amorphous alloys that develop Al nanocrystals during primary crystallization. From the structural characterization, an MRO seeded nucleation configuration is established, whereby the Al nanocrystals are catalyzed by the MRO core to decrease the nucleation barrier. The MRO seeded nucleation model and the kinetic data from the delay time ( τ) measurement provide a full accounting of the evolution of the Al nanocrystal density (N v ) during the primary crystallization under isothermal annealing treatments. Moreover, the calculated values of the steady state nucleation rates ( J ss ) predicted by the nucleation model agree with the experimental results. Moreover, the model satisfies constraints on the structural, thermodynamic, and kinetic parameters, such as the critical nucleus size, the interface energy, and the volume-free energy driving force that are essential for a fully self-consistent nucleation kinetics analysis. The nucleation kinetics model can be applied more broadly to materials that are characterized by the presence of spatial heterogeneities. 
    more » « less
  3. ; ; ; ; ; ; ( , Applied Physics Letters)
    We report on the absence of strain relaxation mechanism in Al 0.6 Ga 0.4 N epilayers grown on (0001) AlN substrates for thickness as large as 3.5  μm, three-orders of magnitude beyond the Matthews–Blakeslee critical thickness for the formation of misfit dislocations (MDs). A steady-state compressive stress of 3–4 GPa was observed throughout the AlGaN growth leading to a large lattice bow (a radius of curvature of 0.5 m −1 ) for the thickest sample. Despite the large lattice mismatch-induced strain energy, the epilayers exhibited a smooth and crack-free surface morphology. These results point to the presence of a large barrier for nucleation of MDs in Al-rich AlGaN epilayers. Compositionally graded AlGaN layers were investigated as potential strain relief layers by the intentional introduction of MDs. While the graded layers abetted MD formation, the inadequate length of these MDs correlated with insignificant strain relaxation. This study emphasizes the importance of developing strain management strategies for the implementation of the single-crystal AlN substrate platform for III-nitride deep-UV optoelectronics and power electronics. 
    more » « less
  4. ; ; ; ; ; ( , npj Materials Degradation)
    Abstract Ni-based superalloys offer a unique combination of mechanical properties, corrosion resistance and high temperature performance. Near ambient pressure X-ray photoelectron spectroscopy was used to study in operando the initial steps of oxidation for Ni-5Cr, Ni-15Cr, Ni-30Cr and Ni-15Cr-6W at 500 °C, p(O 2 )=10 −6 mbar. The comparison of oxide evolution for these alloys quantifies the outsized impact of W in promoting chromia formation. For the binary alloys an increase in chromia due to Cr-surface enrichment is followed by NiO nucleation and growth thus seeding a dual-layer structure. The addition of W (Ni-15Cr-6W) shifts the reaction pathways towards chromia thus enhancing oxide quality. Density functional theory calculations confirm that W atoms adjacent to Cr create highly favorable oxygen adsorption sites. The addition of W supercharges the reactivity of Cr with oxygen essentially funneling oxygen atoms into Cr sites. The experimental results are discussed in the context of surface composition, chemistry, reactant fluxes, and microstructure. 
    more » « less
  5. ; ; ; ; ; ; ( , Journal of the American Ceramic Society)
    Abstract

    Aluminum nitride (AlN) is a promising material for electronic substrates and heat sinks. However, AlN powders react with water that adversely affects final part properties and necessitates processing in organic solvents, increasing the cost of AlN parts. Small quantities of yttrium oxide (Y2O3) are commonly added to AlN particles to enable liquid phase sintering. To mitigate the reaction of AlN particles with water, particle atomic layer deposition (ALD) was used to coat AlN powders with conformal films of Y2O3prior to densification and powder processing. When AlN particles were coated with 6 nm thick films of amorphous Y2O3, the hydrolysis reaction was significantly suppressed over 48 h, demonstrating that Y2O3nanofilms on AlN powders act as a barrier coating in an aqueous solution. AlN powders with Y2O3addition by particle ALD sintered to high relative densities (≥90% theoretical) after sintering at 1800°C for 50 min.

     
    more » « less
  • Citation Formats
  • MLA
  • APA
  • Chicago
  • BibTeX
  • Save / Share this Record
  • Send to Email