Abstract

Mechanical failure of π‐conjugated polymer thin films is unavoidable under cyclic loading conditions, due to intrinsic defects and poor resistance to crack propagation. Here, the first tear‐resistant and room‐temperature self‐healable semiconducting composite is presented, consisting of conjugated polymers and butyl rubber elastomers. This new composite displays both a record‐low elastic modulus (<1 MPa) and ultrahigh deformability with fracture strain above 800%. More importantly, failure behavior is not sensitive to precut notches under deformation. Autonomous self‐healing at room temperature, both mechanical and electronic, is demonstrated through the physical contact of two separate films. The composite film also shows device stability in the ambient environment over 5 months due to much‐improved barrier property to both oxygen and water. Butyl rubber is broadly applicable to various p‐type and n‐type semiconducting polymers for fabricating self‐healable electronics to provide new resilient electronics that mimic the tear resistance and healable property of human skin.

 
more » « less
PAR ID:
10457915
Author(s) / Creator(s):
 ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  ;  
Publisher / Repository:
Wiley Blackwell (John Wiley & Sons)
Date Published:
Journal Name:
Advanced Functional Materials
Volume:
30
Issue:
27
ISSN:
1616-301X
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    Semiconductors with both high stretchability and self‐healing capability are highly desirable for various wearable devices. Much progress has been achieved in designing highly stretchable semiconductive polymers or composites. The demonstration of self‐healable semiconductive composite is still rare. Here, an extremely soft, highly stretchable, and self‐healable hydrogen bonding cross‐linked elastomer, amide functionalized‐polyisobutylene (PIB‐amide) is developed, to enable a self‐healable semiconductive composite through compounding with a high‐performance conjugated diketopyrrolopyrrole (DPP‐T) polymer. The composite, consisting of 20% DPP‐T and 80% PIB‐amide, shows record high crack‐onset strain (COS ≈1500%), extremely low elastic modulus (E≈1.6 MPa), and unique ability to spontaneously self‐heal atroom temperature within 5 min. Unlike previous works, these unique composite materials also show strain‐independent charge mobility. An in‐depth morphological study based on multi‐model techniques indicate that all composites show blending ratio‐ and stretching‐independent fibril‐like aggregation due to the strong hydrogen bond in elastomer to enable the unique stable charge mobility. This study provides a new direction to develop highly healable and electronically stable semiconductive composite and will enable new applications of stretchable electronics.

     
    more » « less
  2. Abstract

    π‐Conjugated polymers have drawn broad interest in flexible electronics due to their solution processability, light weight, and a combination of conducting and light‐emitting properties. However, achieving mechanical endurance and stretchability in freestanding conjugated polymers is still difficult. Surface‐assembly‐induced light‐emitting polymer nanosheets with prodigious mechanical strength and charge transport are reported. Transferring freestanding polymer films onto various templates with conformal contact results in electrical and optical strain sensors with a gauge factor of ≈29. Subsequent geometric engineering into kirigami structures of the polymer sheets further extends the strain accommodations 20‐fold without compromising electric conductivity or fluorescence properties. These as‐prepared semiconducting polymers represent a possible new material for emerging stretchable electronics.

     
    more » « less
  3. Abstract

    Conjugated polymers consist of complex backbone structures and side‐chain moieties to meet various optoelectronic and processing requirements. Recent work on conjugated polymers has been devoted to studying the mechanical properties and developing new conjugated polymers with low modulus and high‐crack onset strain, while the thin film mechanical stability under long‐term external tensile strain is less investigated. Here we performed direct mechanical stress relaxation tests for both free‐standing and thin film floated on water surface on both high‐Tgand low‐Tgconjugated polymers, as well as a reference nonconjugated sample, polystyrene. We measured thin films with a range of film thickness from 38 to 179 nm to study the temperature and thickness effect on thin film relaxation, where an apparent enthalpy–entropy compensation effect for glassy polymer PS and PM6 thin films was observed. We also compared relaxation times across three different conjugated polymers and showed that both crystalline morphology and higher modulus reduce the relaxation rate besides higher glass transition temperature. Our work provides insights into the mechanical creep behavior of conjugated polymers, which will have an impact on the future design of stable functional organic electronics.

     
    more » « less
  4. Abstract

    Donor–acceptor (D–A) type semiconducting polymers have shown great potential for the application of deformable and stretchable electronics in recent decades. However, due to their heterogeneous structure with rigid backbones and long solubilizing side chains, the fundamental understanding of their molecular picture upon mechanical deformation still lacks investigation. Here, the molecular orientation of diketopyrrolopyrrole (DPP)‐based D–A polymer thin films is probed under tensile deformation via both experimental measurements and molecular modeling. The detailed morphological analysis demonstrates highly aligned polymer crystallites upon deformation, while the degree of backbone alignment is limited within the crystalline domain. Besides, the aromatic ring on polymer backbones rotates parallel to the strain direction despite the relatively low overall chain anisotropy. The effect of side‐chain length on the DPP chain alignment is observed to be less noticeable. These observations are distinct from traditional linear‐chain semicrystalline polymers like polyethylene due to distinct characteristics of backbone/side‐chain combination and the crystallographic characteristics in DPP polymers. Furthermore, a stable and isotropic charge carrier mobility is obtained from fabricated organic field‐effect transistors. This study deconvolutes the alignment of different components within the thin‐film microstructure and highlights that crystallite rotation and chain slippage are the primary deformation mechanisms for semiconducting polymers.

     
    more » « less
  5. Abstract

    Despite having favorable optoelectronic and thermomechanical properties, the wide application of semiconducting polymers still suffers from limitations, particularly with regards to their processing in solution which necessitates toxic chlorinated solvents due to their intrinsic low solubility in common organic solvents. This work presents a novel greener approach to the fabrication of organic electronics without the use of toxic chlorinated solvents. Low‐molecular‐weight non‐toxic branched polyethylene (BPE) is used as a solvent to process diketopyrrolopyrrole‐based semiconducting polymers, then the solvent‐induced phase separation (SIPS) technique is adopted to produce films of semiconducting polymers from solution for the fabrication of organic field‐effect transistors (OFETs). The films of semiconducting polymers prepared from BPE using SIPS show a more porous granular morphology with preferential edge‐on crystalline orientation compared to the semiconducting polymer film processed from chloroform. OFETs based on the semiconducting films processed from BPE show similar device characteristics to those prepared from chloroform without thermal annealing, confirming the efficiency and suitability of BPE to replace traditional chlorinated solvents for green organic electronics. This new greener processing approach for semiconducting polymers is potentially compatible with different printing techniques and is particularly promising for the preparation of porous semiconducting layers and the fabrication of OFET‐based electronics.

     