Fluorination of Li‐ion cathode materials is of significant interest as it is claimed to lead to significant improvements in long‐term reversible capacity. However, the mechanism by which LiF incorporates and improves performance remains uncertain. Indeed, recent evidence suggests that fluorine is often present as a coating layer rather than incorporated into the bulk of the material. In this work, first‐principles calculations are used to investigate the thermodynamics of fluorination in transition metal oxide cathodes to determine the conditions under which bulk fluorination is possible. It is found that unlike classic well‐ordered cathodes, which cannot incorporate fluorine, disordered rock salt‐structured materials achieve significant fluorination levels due to the presence of locally metal‐poor, lithium‐rich environments that are highly preferred for fluorine. As well as explaining the fluorination process in known materials, this finding is encouraging for the development of new disordered rock salt lithium‐excess transition metal oxides, a promising new class of Li‐ion battery cathode materials that offer superior practical capacity to traditional layered oxides. In particular, it is found that bulk fluorination may serve as an alternative source of Li‐excess in these compounds that can replace the conventional substitution of a heavy redox‐inactive element on the transition metal sublattice.
Fluorine substitution is a critical enabler for improving the cycle life and energy density of disordered rocksalt (DRX) Li‐ion battery cathode materials which offer prospects for high energy density cathodes, without the reliance on limited mineral resources. Due to the strong Li–F interaction, fluorine also is expected to modify the short‐range cation order in these materials which is critical for Li‐ion transport. In this work, density functional theory and Monte Carlo simulations are combined to investigate the impact of Li–F short‐range ordering on the formation of Li percolation and diffusion in DRX materials. The modeling reveals that F substitution is always beneficial at sufficiently high concentrations and can, surprisingly, even facilitate percolation in compounds without Li excess, giving them the ability to incorporate more transition metal redox capacity and thereby higher energy density. It is found that for F levels below 15%, its effect can be beneficial or disadvantageous depending on the intrinsic short‐range order in the unfluorinated oxide, while for high fluorination levels the effects are always beneficial. Using extensive simulations, a map is also presented showing the trade‐off between transition‐metal capacity, Li‐transport, and synthetic accessibility, and two of the more extreme predictions are experimentally confirmed.
more » « less- NSF-PAR ID:
- 10458018
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Energy Materials
- Volume:
- 10
- Issue:
- 10
- ISSN:
- 1614-6832
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract -
more » « less
Abstract Li‐excess disordered rocksalts (DRXs) are emerging as promising cathode materials for Li‐ion batteries due to their ability to use earth‐abundant transition metals. In this work, a new strategy based on partial Li deficiency engineering is introduced to optimize the overall electrochemical performance of DRX cathodes. Specifically, by using Mn‐based DRX as a proof‐of‐concept, it is demonstrated that the introduction of cation vacancies during synthesis (e.g., Li1.3‐
x Mn2+0.4‐x Mn3+x Nb0.3O1.6F0.4,x = 0, 0.2, and 0.4) improves both the discharge capacity and rate performance due to the more favored short‐range order in the presence of Mn3+. Density functional theory calculations and Monte Carlo simulations, in combination with spectroscopic tools, reveal that introducing 10% vacancies (Li1.1Mn2+0.2Mn3+0.2Nb0.3O1.6F0.4) enables both Mn2+/Mn3+redox and excellent Li percolation. However, a more aggressive vacancy doping (e.g., 20% vacancies in Li0.9Mn3+0.4Nb0.3O1.6F0.4) impairs performance because it induces phase separation between an Mn‐rich and a Li‐rich phase. -
more » « less
Abstract Lithium‐rich transition metal oxides with a cation‐disordered rocksalt structure (disordered rocksalt oxides or DRX) are promising candidates for sustainable, next‐generation Li‐ion cathodes due to their high energy densities and compositional flexibility, enabling Co‐ and Ni‐free battery chemistries. However, current methods to synthesize DRX compounds require either high temperature (≈1000 °C) sintering for several hours, or high energy ball milling for several days in an inert atmosphere. Both methods are time‐ and energy‐intensive, limiting the scale up of DRX production. The present study reports the rapid synthesis of various DRX compositions in ambient air via a microwave‐assisted solid‐state technique resulting in reaction times as short as 5 min, which are more than two orders of magnitude faster than current synthesis methods. The DRX compounds synthesized via microwave are phase‐pure and have a similar short‐ and long‐range structure as compared to DRX materials synthesized via a standard solid‐state route, resulting in nearly identical electrochemical performance. In some cases, microwave heating allows for better particle size and morphology control. Overall, the rapid and energy‐efficient microwave technique provides a more sustainable route to produce DRX materials, further incentivizes the development of next‐generation DRX cathodes, and is key to accelerating their optimization via high‐throughput studies.
-
more » « less
Abstract Metallic lithium is the most competitive anode material for next‐generation lithium (Li)‐ion batteries. However, one of its major issues is Li dendrite growth and detachment, which not only causes safety issues, but also continuously consumes electrolyte and Li, leading to low coulombic efficiency (CE) and short cycle life for Li metal batteries. Herein, the Li dendrite growth of metallic lithium anode is suppressed by forming a lithium fluoride (LiF)‐enriched solid electrolyte interphase (SEI) through the lithiation of surface‐fluorinated mesocarbon microbeads (MCMB‐F) anodes. The robust LiF‐enriched SEI with high interfacial energy to Li metal effectively promotes planar growth of Li metal on the Li surface and meanwhile prevents its vertical penetration into the LiF‐enriched SEI from forming Li dendrites. At a discharge capacity of 1.2 mAh cm−2, a high CE of >99.2% for Li plating/stripping in FEC‐based electrolyte is achieved within 25 cycles. Coupling the pre‐lithiated MCMB‐F (Li@MCMB‐F) anode with a commercial LiFePO4cathode at the positive/negative (P/N) capacity ratio of 1:1, the LiFePO4//Li@MCMB‐F cells can be charged/discharged at a high areal capacity of 2.4 mAh cm−2for 110 times at a negligible capacity decay of 0.01% per cycle.
-
more » « less
Abstract The recent discovery of Li‐excess cation‐disordered rock salt cathodes has greatly enlarged the design space of Li‐ion cathode materials. Evidence of facile lattice fluorine substitution for oxygen has further provided an important strategy to enhance the cycling performance of this class of materials. Here, a group of Mn3+–Nb5+‐based cation‐disordered oxyfluorides, Li1.2Mn3+0.6+0.5
x Nb5+0.2−0.5x O2−x Fx (x = 0, 0.05, 0.1, 0.15, 0.2) is investigated and it is found that fluorination improves capacity retention in a very significant way. Combining spectroscopic methods and ab initio calculations, it is demonstrated that the increased transition‐metal redox (Mn3+/Mn4+) capacity that can be accommodated upon fluorination reduces reliance on oxygen redox and leads to less oxygen loss, as evidenced by differential electrochemical mass spectroscopy measurements. Furthermore, it is found that fluorine substitution also decreases the Mn3+‐induced Jahn–Teller distortion, leading to an orbital rearrangement that further increases the contribution of Mn‐redox capacity to the overall capacity.