Long duration energy storage (LDES) is an economically attractive approach to accelerating clean renewable energy deployment. The newly emerged solid oxide iron–air battery (SOIAB) is intrinsically suited for LDES applications due to its excellent low‐rate performance (high‐capacity with high efficiency) and use of low‐cost and sustainable materials. However, rechargeability and durability of SOIAB are critically limited by the slow kinetics in iron/iron‐oxide redox couples. Here the use of combined proton‐conducting BaZr0.4Ce0.4Y0.1Yb0.1O3(BZC4YYb) and reduction‐promoting catalyst Ir to address the kinetic issues, is reported. It is shown that, benefiting from the facilitated H+diffusion and boosted FeO
Long duration energy storage (LDES) is economically attractive to accelerate widespread renewable energy deployment. But none of the existing energy storage technologies can meet LDES cost requirements. The newly emerged solid oxide iron air battery (SOIAB) with energy-dense solid Fe as an energy storage material is a competitive LDES-suitable technology compared to conventional counterparts. However, the performance of SOIAB is critically limited by the kinetics of Fe3O4reduction (equivalent to charging process) and the understanding of this kinetic bottleneck is significantly lacking in the literature. Here, we report a systematic kinetic study of Fe3O4-to-Fe reduction in H2/H2O environment, particularly the effect of catalyst (iridium) and supporting oxides (ZrO2and BaZr0.4Ce0.4Y0.1Yb0.1O3). With in situ created Fe3O4, the degree of reduction is measured by the change of H2O and H2concentrations in the effluent using a mass spectrometer, from which the kinetic rate constant is extracted as a function of inlet H2concentration and temperature. We find that kinetics can be nicely described by Johson-Mehl-Avrami (JMA) model. We also discuss the stepwise reduction mechanisms and activation energy for the reduction process.
more » « less- Award ID(s):
- 1801284
- NSF-PAR ID:
- 10468369
- Publisher / Repository:
- The Electrochemical Society
- Date Published:
- Journal Name:
- Journal of The Electrochemical Society
- Volume:
- 170
- Issue:
- 10
- ISSN:
- 0013-4651
- Format(s):
- Medium: X Size: Article No. 104504
- Size(s):
- ["Article No. 104504"]
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
Abstract x ‐reduction kinetics, the battery operated under 550 °C, 50% Fe‐utilization and 0.2 C, exhibits a discharge specific energy density of 601.9 Wh kg–1‐Fe with a round‐trip efficiency (RTE) of 82.9% for 250 h of a cycle duration of 2.5 h. Under 500 °C, 50% Fe‐utilization and 0.2 C, the same battery exhibits 520 Wh kg–1‐Fe discharge energy density with an RTE of 61.8% for 500 h. This level of energy storage performance promises that SOIAB is a strong candidate for LDES applications. -
Long duration electricity storage (LDES) with 10+ hour cycle duration is an economically competitive option to accelerate the penetration of renewable energy into the utility market. Unfortunately, none of the available energy storage technologies can meet the LDES’ requirements for duration and cost. We here report a focused kinetic study on Fe-oxide reduction process, which is a key step for solid oxide iron-air battery; the latter has been recently demonstrated as a LDES compatible battery. The study clearly shows that Ir is an excellent catalyst to boost the sluggish Fe-oxide reduction kinetics.more » « less
-
more » « less
Abstract Chemical looping air separation (CLAS) is a promising technology for oxygen generation with high efficiency. The key challenge for CLAS is to design robust oxygen sorbents with suitable redox properties and fast redox kinetics. In this work, perovskite-structured Sr1-xCaxFe1-yCoyO3oxygen sorbents were investigated and demonstrated for oxygen production with tunable redox properties, high redox rate, and excellent thermal/steam stability. Cobalt doping at B site was found to be highly effective, 33% improvement in oxygen productivity was observed at 500 °C. Moreover, it stabilizes the perovskite structure and prevents phase segregation under pressure swing conditions in the presence of steam. Scalable synthesis of Sr0.8Ca0.2Fe0.4Co0.6O3oxygen sorbents was carried out through solid state reaction, co-precipitation, and sol-gel methods. Both co-precipitation and sol-gel methods are capable of producing Sr0.8Ca0.2Fe0.4Co0.6O3sorbents with satisfactory phase purity, high oxygen capacity, and fast redox kinetics. Large scale evaluation of Sr0.8Ca0.2Fe0.4Co0.6O3, using an automated CLAS testbed with over 300 g sorbent loading, further demonstrated the effectiveness of the oxygen sorbent to produce 95% pure O2with a satisfactory productivity of 0.04 gO2gsorbent−1h−1at 600 °C.
-
New optical materials with efficient luminescence and scintillation properties have drawn a great deal of attention due to the demand for optoelectronic devices and medical theranostics. Their nanomaterials are expected to reduce the cost while incrementing the efficiency for potential lighting and scintillator applications. In this study, we have developed praseodymium-doped lanthanum hafnate (La 2 Hf 2 O 7 :Pr 3+ ) pyrochlore nanoparticles (NPs) using a combined co-precipitation and relatively low-temperature molten salt synthesis procedure. XRD and Raman investigations confirmed ordered pyrochlore phase for the as-synthesized undoped and Pr 3+ -doped La 2 Hf 2 O 7 NPs. The emission profile displayed the involvement of both the 3 P 0 and 1 D 2 states in the photoluminescence process, however, the intensity of the emission from the 1 D 2 states was found to be higher than that from the 3 P 0 states. This can have a huge implication on the design of novel red phosphors for possible application in solid-state lighting. As a function of the Pr 3+ concentration, we found that the 0.1%Pr 3+ doped La 2 Hf 2 O 7 NPs possessed the strongest emission intensity with a quantum yield of 20.54 ± 0.1%. The concentration quenching, in this case, is mainly induced by the cross-relaxation process 3 P 0 + 3 H 4 → 1 D 2 + 3 H 6 . Emission kinetics studies showed that the fast decaying species arise because of the Pr 3+ ions occupying the Hf 4+ sites, whereas the slow decaying species can be attributed to the Pr 3+ ions occupying the La 3+ sites in the pyrochlore structure of La 2 Hf 2 O 7 . X-ray excited luminescence (XEL) showed a strong red-light emission, which showed that the material is a promising scintillator for radiation detection. In addition, the photon counts were found to be much higher when the NPs are exposed to X-rays when compared to ultraviolet light. Altogether, these La 2 Hf 2 O 7 :Pr 3+ NPs have great potential as a good down-conversion phosphor as well as scintillator material.more » « less
-
more » « less
Abstract Vanadium multiredox‐based NASICON‐Na
z V2−y My (PO4)3(3 ≤z ≤ 4; M = Al3+, Cr3+, and Mn2+) cathodes are particularly attractive for Na‐ion battery applications due to their high Na insertion voltage (>3.5 V vs Na+/Na0), reversible storage capacity (≈150 mA h g−1), and rate performance. However, their practical application is hindered by rapid capacity fade due to bulk structural rearrangements at high potentials involving complex redox and local structural changes. To decouple these factors, a series of Mg2+‐substituted Na3+y V2−y Mgy (PO4)3(0 ≤y ≤ 1) cathodes is studied for which the only redox‐active species is vanadium. While X‐ray diffraction (XRD) confirms the formation of solid solutions between they = 0 and 1 end members, X‐ray absorption spectroscopy and solid‐state nuclear magnetic resonance reveal a complex evolution of the local structure upon progressive Mg2+substitution for V3+. Concurrently, the intercalation voltage rises from 3.35 to 3.45 V, due to increasingly more ionic VO bonds, and the sodium (de)intercalation mechanism transitions from a two‐phase fory ≤ 0.5 to a solid solution process fory ≥ 0.5, as confirmed by in operando XRD, while Na‐ion diffusion kinetics follow a nonlinear trend across the compositional series.