Ultrathin polyorganosilica membranes synthesized by oxygen-plasma treatment of polysiloxanes for H2/CO2 separation
Oxygen plasma treatment of polydimethylsiloxane (PDMS) induces an ultrathin polyorganosilica (POSi) layer (< 10 nm) on top of a PDMS membrane, leading to excellent H2/gas separation properties and providing a rapid and scalable way to fabricate robust silica membranes compared with conventional high-temperature and time-consuming sol-gel methods. Here, we thoroughly investigate POSi membranes derived from poly(dimethylsiloxane-co-methylhydroxidesiloxane) (poly(DMS-co-MHOS)) containing -SiOH groups that can be more easily converted to silica networks than the -SiCH3 in PDMS. The effect of the polysiloxane structure and plasma treatment conditions (including plasma generating powers, oxygen flowrate, chamber pressure, and treatment time) on the silica chemistry, structure, and H2/CO2 separation properties are systematically determined to derive structure/property relationships. An optimized membrane exhibits H2 permeance of 880 GPU and H2/CO2 selectivity of 67 at 150 ℃, superior to state-of-the-art polymeric membranes. The membrane retains H2/CO2 selectivity as high as 46 when challenged with simulated syngas containing 2.8 mol% water vapor at 150 ℃, demonstrating the potential of these POSi membranes for practical applications.
more »
« less
- PAR ID:
- 10483718
- Publisher / Repository:
- Elsevier
- Date Published:
- Journal Name:
- Journal of Membrane Science
- Volume:
- 688
- Issue:
- C
- ISSN:
- 0376-7388
- Page Range / eLocation ID:
- 122099
- Subject(s) / Keyword(s):
- Polyorganosilica membranes Oxygen plasma treatment H2/CO2 separation Polysiloxane Silica
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
Membrane-based separations offer the potential for the lowest energy demand requirements of all separation options. Among all nanoporous membranes, the carbon molecular sieves (CMS), metal-organic frameworks (MOFs), and mixed-matrix membranes (MMMs) with angstrom level molecular discrimination properties makes them appealing for separating a wide spectrum of gas-pairs. Here we present results of gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) in porous organic cages (POCs) incorporated into fluorinated copolyimides polymers (FCPs). The FCPs were synthesized by the iridization reaction of fluorinated dianhydrides, nonfluorinated dianhydride, and nonfluorinated diamine. Asymmetric hollow fiber membranes formed by the dry-jet/wet-quench spinning process. Once fresh FCP fibers were synthesized, they were crosslinked with POCs, vacuum dried at 90 °C. We investigated the uptake, gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) over synthesized POC-mixed matrixed membranes (POC-MMM) at 25 °C and pressures up to 1 bar. At 1 bar and 25 °C, C2H6, C2H4, C3H8, C3H6 adsorption capacities reached to 42.61, 2.56, 2.77 and 2.65 mmol/g over POC-MMM, respectively, while CO2, CH4, CO, N2 and H2 adsorption capacities of 1.48, 0.84, 0.33, 0.11, and 0.068 mmol/g, respectively. Furthermore, stable CMS membrane were formed by pyrolysis of POC-MMMs under an inert argon atmosphere at 1 atm. To test the gas transport properties of CMS-derived POC/MMM, a lab-scale hollow fiber module with two-five fibers was constructed. The results of longer-term operation of synthesized CMS membrane that was continuously operated for 264 h (10 days) with an equimolar binary H2/CO2, CH4/CO2 and C3H6/C3H8 feed at 25°C and 1 bar feed pressure. The modification yielded promising results in the reduction of physical aging of CMS membranes.more » « less
-
Here we present results of gas selectivity and diffusion of different gases (C2H6, C2H4, C3H8, C3H6, H2, N2, CO2, and CH4) in porous organic cages (POCs) incorporated into fluorinated copolyimides polymers (FCPs). The FCPs were synthesized by the thermal and chemical imidization reaction of fluorinated dianhydrides, nonfluorinated dianhydride, and nonfluorinated diamine. Asymmetric hollow fiber membranes formed by the dry-jet/wet-quench spinning process. Once fresh FCP fibers were synthesized, they were crosslinked with POCs, vacuum dried at 90 °C. We investigated the uptake, gas selectivity and diffusion of different gases (C3H8, C3H6, CO2, and H2) over synthesized POC-mixed matrixed membranes (POC-MMM) at 25 °C and pressures up to 1 bar. At 1 bar and 25 °C, C3H8, C3H6 adsorption capacities reached 2.77 and 2.65 mmol/g over POC-MMM, respectively, while CO2, CH4, CO, N2 and H2 adsorption capacities of 1.48, 0.84, 0.33, 0.11, and 0.068 mmol/g, respectively. Furthermore, stable CMS membrane was formed by pyrolysis of POC-MMMs under an inert argon atmosphere at 1 atm. To test the gas transport properties of CMS-derived POC/MMM, a lab-scale hollow fiber module with two-five fibers was constructed. The results of longer-term operation of synthesized CMS membrane that was continuously operated for 264 h (10 days) with an equimolar binary H2/CO2, CH4/CO2 and C3H6/C3H8 feed at 25°C and 1 bar feed pressure. The modification yielded promising results in the reduction of physical aging of CMS membranes.more » « less
-
The effect of the annealing temperature of polybenzimidazole (PBI) membranes on H2/CO2 gas separations was investigated. Membranes annealed from 250 ◦C to 400 ◦C were tested for gas permeation with pure H2, CO2, and N2 gases and a H2:CO2 (1:1) mixture at 35 ◦C, 100 ◦C, 200 ◦C, and 300 ◦C and at pressures up to 45 bar. Gas permeation data show that permeability and selectivity of the membranes is significantly impacted by the annealing temperature, the presence of adsorbed water, and remaining casting solvent (DMAc). At a testing temperature of 35 ◦C, ideal H2/CO2 selectivities of 50, 49, and 66 with pure H2 permeabilities of 1.5, 0.8, and 1.5 Barrer were obtained for membranes annealed at 250 ◦C, 300 ◦C, and 400 ◦C, respectively. At this temperature, high gas mixture H2/CO2 selectivities of 41, 73, and 47 with H2 permeabilities of 1.03, 0.26, and 0.50 Barrer were also obtained for these membranes. At testing temperatures of 300 ◦C, both the ideal and gas mixture H2/ CO2 selectivities dropped to 44, 28, and 30 (ideal, H2 = 45, 45, 44 Barrer) and to 19, 22, and 23 (mixture, H2 = 41, 43, and 44 Barrer) for membranes annealed at 250 ◦C, 300 ◦C, and 400 ◦C, respectively. As water was removed from the membranes at temperatures greater than 100 ◦C during permeation cycles, where the testing temperature was increased from 35 ◦C to 300 ◦C, the permselectivity properties of the membranes annealed at 400 ◦C became more reproducible. Permeabilities at 35 ◦C from a second permeability cycle increased, but H2/ CO2 selectivities decreased to 21 for gas mixtures (H2 = 1.4 Barrer) and to 34 for pure gases (H2 = 2.2 Barrer). The results suggest that high annealing temperatures may induce changes in the configuration and conformation of the polymer chains, imparting distinctive permselectivity properties to the membranes. Activation energies of permeability for H2, CO2, and N2 from pure gases and H2:CO2 mixtures correlated with these changes as well.more » « less
-
Efficient separation of hydrogen under steam reforming conditions is important for the development of clean energy sources. Although high-temperature and steam-stable membranes with high fluxes and large separation factors would be valuable for such an application, their fabrication remains a challenge. Silicon-based ceramic membranes are particularly promising due to their high temperature resistance and excellent chemical stability. In this study, we propose a new synthetic route for fabricating nanoporous, asymmetric membranes via the pyrolysis of silicon-containing polymer films deposited by initiated chemical vapor deposition (iCVD) on macroporous silicon carbide supports. Specifically, we systematically investigated the change in the chemical structure of poly(2,4,6,8-tetravinyl-2,4,6,8-tetramethyl cyclotetrasiloxane) films at different pyrolysis temperatures and found that the complete transition to a silica membrane occurred at ~1100 °C. Three different supports composed of silicon carbide powders of varying sizes were tested for membrane preparation. It was found that membranes formed with our process were microporous with separation factors several times above the corresponding Knudsen factors. Our synthetic route, therefore, offers a scalable and solventless method for producing silicon-based ceramic membranes for high-temperature separation and sensor applications.more » « less
- Free Publicly Accessible Full Text
-
Accepted Manuscript1.0
- Journal Article:
- https://doi.org/10.1016/j.memsci.2023.122099