This review focuses on surface modifications to gallium‐based liquid metals (LMs), which are stretchable conductors with metallic conductivity and nearly unlimited extensibility due to their liquid nature. Despite the enormous surface tension of LM, it can be patterned into nonspherical shapes, such as wires, due to the presence of a native oxide shell. Incorporating inherently soft LM into elastomeric devices offers comfort, mechanical compliance, and stretchability. The thin oxide layer also enables the formation of stable liquid colloids and LM micro/nanosized droplets that do not coalesce easily. The oxide layer can also be exfoliated and chemically modified into semiconductor 2D materials to create and deposit atomically thin materials at room temperature. Thus, the interface and its manipulation are important. This review summarizes physical and chemical methods of modifying the surface of LM to tune its properties. The surface modification of LM provides unique applications, including use in soft biomedical sensors and actuators with mechanical properties similar to human tissue.
Pastes and “foams” containing liquid metal (LM) as the continuous phase (liquid metal foams, LMFs) exhibit metallic properties while displaying paste or putty‐like rheological behavior. These properties enable LMFs to be patterned into soft and stretchable electrical and thermal conductors through processes conducted at room temperature, such as printing. The simplest LMFs, featured in this work, are made by stirring LM in air, thereby entraining oxide‐lined air “pockets” into the LM. Here, it is reported that mixing small amounts of water (as low as 1 wt%) into such LMFs gives rise to significant foaming by harnessing known reactions that evolve hydrogen and produce oxides. The resulting structures can be ≈4–5× their original volume and possess a fascinating combination of attributes: porosity, electrical conductivity, and responsiveness to environmental conditions. This expansion can be utilized for a type of 4D printing in which patterned conductors “grow,” fill cavities, and change shape and density with respect to time. Excessive exposure to water in the long term ultimately consumes the metal in the LMF. However, when exposure to water is controlled, the metallic properties of porous LMFs can be preserved.
more » « less- PAR ID:
- 10488337
- Publisher / Repository:
- Wiley Blackwell (John Wiley & Sons)
- Date Published:
- Journal Name:
- Advanced Materials
- Volume:
- 36
- Issue:
- 34
- ISSN:
- 0935-9648
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
more » « less
-
Gallium-based liquid metals (LMs) are suitable for many potential applications due to their unique combination of metallic and liquid properties. However, due to their high surface tension and low viscosity, LMs are challenging to apply to substrates in useful shapes, such as dots, wires, and films. These issues are mitigated by mixing the LMs in air with other materials, such as mixing with solid particles to form LM solid pastes or mixing with gases to form LM foams. Underlying these deceivingly simple mixing processes are complex and highly intertwined microscale mechanisms. Air microbubbles are inevitably incorporated while making LM pastes, making them partly foams. On the other hand, for foaming of the LM to occur, a critical volume content of solid particles must be internalized first. Consequently, both LM pastes and foams are multiphase composites containing solid and fluid microcomponents. Here, we systematically study the impact of the mixing procedure, solid particle size, and volume fraction (SiO2) on the air content of the multiphase LM composites. We demonstrate that decreasing the particle size and increasing their volume fraction substantially decrease the composite density (i.e., increases air entrapment). The foaming process can also be enhanced with the use of high-speed mechanical mixing, although leading to the formation of a more disordered internal structure. In contrast, manual mixing with larger microparticles can promote the formation of more paste-like composites with minimal air content. We explain the microscopic mechanisms underlying these trends by correlating macroscopic measurements with cross-sectional electron microscopy of the internal structure.more » « less
-
more » « less
Abstract Gallium-based liquid metals (LM) have surface tension an order of magnitude higher than water and break up into micro-droplets when mixed with other liquids. In contrast, silicone oil readily mixes into LM foams to create oil-in-LM emulsions with oil inclusions. Previously, the LM was foamed through rapid mixing in air for an extended duration (over 2 hours). This process first results in the internalization of oxide flakes that form at the air-liquid interface. Once a critical fraction of these randomly shaped solid flakes is reached, air bubbles internalize into the LM to create foams that can internalize secondary liquids. Here, we introduce an alternative oil-in-LM emulsion fabrication method that relies on the prior addition of SiO2 micro-particles into the LM before mixing it with the silicone oil. This particle-assisted emulsion formation process provides a higher control over the composition of the LM-particle mixture before oil addition, which we employ to systematically study the impact of particle characteristics and content on the emulsions' composition and properties. We demonstrate that the solid particle size (0.8 µm to 5 µm) and volume fraction (1% to 10%) have a negligible impact on the internalization of the oil inclusions. The inclusions are mostly spherical with diameters of 20 to 100 µm diameter and are internalized by forming new, rather than filling old, geometrical features. We also study the impact of the particle characteristics on the two key properties related to the functional application of the LM emulsions in the thermal management of microelectronics. In particular, we measure the impact of particles and silicone oil on the emulsion's thermal conductivity and its ability to prevent deleterious gallium-induced corrosion and embrittlement of contacting metal substrates.
-
more » « less
Abstract This review discusses methods, challenges, and opportunities for direct‐write and 3D printing of low melting point, gallium‐based liquid metal alloys at room temperature. Alloys of gallium exhibit high conductivity and high stretchability making them well suited for use in soft circuitry for stretchable electronics and soft robotics. In addition, the liquid nature of the metal enables entirely new ways to pattern metals at room temperature; herein, the focus is placed on additive printing via nozzle‐based methods. Room temperature printing of liquid metals enables rapid fabrication of complex geometries (with dimensions as small as 10 µm) on a wide range of materials, such as polymers. These processes can be used to make metallic conductors for devices with self‐healing capabilities, soft/stretchable electrodes, and sensors.
-
more » « less
Gallium‐based metal alloys have high electrical conductivity in the liquid state at room temperature. These liquid metal conductors inspire unique electronic applications such as reconfigurable circuits and stretchable components with extremely high strain tolerance. Previously, liquid metals have been successfully patterned via direct‐writing, yielding metallically conductive features on‐demand at room temperature that do not require post‐processing, down to a resolution of ≈10 μm. While most direct‐write processes extrude materials from a nozzle via pressure or volumetric displacement, liquid metal is instead printed here by a shear‐driven mechanism that occurs when the oxide‐coated meniscus of the metal adheres to the printing substrate and is “pulled” from the nozzle at pressures that are well‐below that needed to extrude the metal in the absence of shear. Herein, the key operating parameters that enable shear‐driven printing of liquid metals including dispensing pressure, choice of substrate, print height, the surrounding environmental conditions, and the speed and acceleration of the print head are elucidated. A guide to the best practices as well as limitations for implementing shear‐driven printing of liquid metals at room temperature is provided in these studies.