Title: Probing elemental diffusion and radiation tolerance of perovskite solar cells via non-destructive Rutherford backscattering spectrometry

Mixed organic–inorganic halide perovskite-based solar cells have attracted interest in recent years due to their potential for both terrestrial and space applications. Analysis of interfaces is critical to predicting device behavior and optimizing device architectures. Most advanced tools to study buried interfaces are destructive in nature and can induce further degradation. Ion beam techniques, such as Rutherford backscattering spectrometry (RBS), is a useful non-destructive method to probe an elemental depth profile of multilayered perovskite solar cells (PSCs) as well as to study the inter-diffusion of various elemental species across interfaces. Additionally, PSCs are becoming viable candidates for space photovoltaic applications, and it is critical to investigate their radiation-induced degradation. RBS can be simultaneously utilized to analyze the radiation effects induced by He+ beam on the device, given their presence in space orbits. In the present work, a 2 MeV He+ beam was used to probe the evidence of elemental diffusion across PSC interfaces with architecture glass/ITO/SnO2/Cs0.05(MA0.17FA0.83)0.95Pb(I0.83Br0.17)3/spiro-OMeTAD/MoO3/Au. During the analysis, the device active area was exposed to an irradiation equivalent of up to 1.62 × 1015 He+/cm2, and yet, no measurable evidence (with a depth resolution ∼1 nm) of beam-induced ion migration was observed, implying high radiation tolerance of PSCs. On the other hand, aged PSCs exhibited indications of the movement of diverse elemental species, such as Au, Pb, In, Sn, Br, and I, in the active area of the device, which was quantified with the help of RBS.

 
more » « less
Award ID(s):
2101181 2210722
NSF-PAR ID:
10498625
Author(s) / Creator(s):
; ; ; ; ; ; ;
Publisher / Repository:
American Physical Society
Date Published:
Journal Name:
APL Energy
Volume:
2
Issue:
1
ISSN:
2770-9000
Page Range / eLocation ID:
1, 026105-1
Subject(s) / Keyword(s):
Ion Beam, Ion implantation, Perovskite
Format(s):
Medium: X
Sponsoring Org:
National Science Foundation
More Like this
  1. Abstract

    The ever‐increasing demand for clean sustainable energy has driven tremendous worldwide investment in the design and exploration of new active materials for energy conversion and energy‐storage devices. Tailoring the surfaces of and interfaces between different materials is one of the surest and best studied paths to enable high‐energy‐density batteries and high‐efficiency solar cells. Metal‐halide perovskite solar cells (PSCs) are one of the most promising photovoltaic materials due to their unprecedented development, with their record power conversion efficiency (PCE) rocketing beyond 25% in less than 10 years. Such progress is achieved largely through the control of crystallinity and surface/interface defects. Rechargeable batteries (RBs) reversibly convert electrical and chemical potential energy through redox reactions at the interfaces between the electrodes and electrolyte. The (electro)chemical and optoelectronic compatibility between active components are essential design considerations to optimize power conversion and energy storage performance. A focused discussion and critical analysis on the formation and functions of the interfaces and interphases of the active materials in these devices is provided, and prospective strategies used to overcome current challenges are described. These strategies revolve around manipulating the chemical compositions, defects, stability, and passivation of the various interfaces of RBs and PSCs.

     
    more » « less
  2. Abstract

    The recent rapid increase in efficiency of organic–inorganic perovskite solar cells (PSCs) has resulted in a need to develop a clear understanding of their stability and working mechanisms. In particular, it has been suggested that ion migration contributes to the commonly observed hysteresis in the current–voltage measurements of PSCs, but the rate of ion migration and its effects on the electronic properties of PSCs remain to be addressed. In this work, electron‐beam‐induced current (EBIC) is used to directly map changes in local current extraction in organic–inorganic PSCs under applied voltage. By combining EBIC mapping, standard current–voltage measurements, and external quantum efficiency measurements, it is shown that between the two potential roles that point defects play in device enhancement under voltage biasing, the effects caused by defect‐mediated ion migration outweigh the effects from the filling of trap states caused by these defects. Evidence is also provided for ion migration preferentially at local features such as extended defects. The measured timescale of tens of seconds for migration across a full device imply that ion migration contributes indirectly to the electronic capacitance of perovskite devices through interface charging.

     
    more » « less
  3. Abstract

    With power conversion efficiencies now reaching 24.2%, the major factor limiting efficient electricity generation using perovskite solar cells (PSCs) is their long‐term stability. In particular, PSCs have demonstrated rapid degradation under illumination, the driving mechanism of which is yet to be understood. It is shown that elevated device temperature coupled with excess charge carriers due to constant illumination is the dominant force in the rapid degradation of encapsulated perovskite solar cells under illumination. Cooling the device to 20 °C and operating at the maximum power point improves the stability of CH3NH3PbI3solar cells over 100× compared to operation under open circuit conditions at 60 °C. Light‐induced strain originating from photothermal‐induced expansion is also observed in CH3NH3PbI3, which excludes other light‐induced‐strain mechanisms. However, strain and electric field do not appear to play any role in the initial rapid degradation of CH3NH3PbI3solar cells under illumination. It is revealed that the formation of additional recombination centers in PSCs facilitated by elevated temperature and excess charge carriers ultimately results in rapid light‐induced degradation. Guidance on the best methods for measuring the stability of PSCs is also given.

     
    more » « less
  4. Mechanical failure and chemical degradation of device heterointerfaces can strongly influence the long-term stability of perovskite solar cells (PSCs) under thermal cycling and damp heat conditions. We report chirality-mediated interfaces based onR-/S-methylbenzyl-ammonium between the perovskite absorber and electron-transport layer to create an elastic yet strong heterointerface with increased mechanical reliability. This interface harnesses enantiomer-controlled entropy to enhance tolerance to thermal cycling–induced fatigue and material degradation, and a heterochiral arrangement of organic cations leads to closer packing of benzene rings, which enhances chemical stability and charge transfer. The encapsulated PSCs showed retentions of 92% of power-conversion efficiency under a thermal cycling test (−40°C to 85°C; 200 cycles over 1200 hours) and 92% under a damp heat test (85% relative humidity; 85°C; 600 hours).

     
    more » « less
  5. Abstract

    Typical lead‐based perovskites solar cells show an onset of photogeneration around 800 nm, leaving plenty of spectral loss in the near‐infrared (NIR). Extending light absorption beyond 800 nm into the NIR should increase photocurrent generation and further improve photovoltaic efficiency of perovskite solar cells (PSCs). Here, a simple and facile approach is reported to incorporate a NIR‐chromophore that is also a Lewis‐base into perovskite absorbers to broaden their photoresponse and increase their photovoltaic efficiency. Compared with pristine PSCs without such an organic chromophore, these solar cells generate photocurrent in the NIR beyond the band edge of the perovskite active layer alone. Given the Lewis‐basic nature of the organic semiconductor, its addition to the photoactive layer also effectively passivates perovskite defects. These films thus exhibit significantly reduced trap densities, enhanced hole and electron mobilities, and suppressed illumination‐induced ion migration. As a consequence, perovskite solar cells with organic chromophore exhibit an enhanced efficiency of 21.6%, and substantively improved operational stability under continuous one‐sun illumination. The results demonstrate the potential generalizability of directly incorporating a multifunctional organic semiconductor that both extends light absorption and passivates surface traps in perovskite active layers to yield highly efficient and stable NIR‐harvesting PSCs.

     
    more » « less