Internal plasticization of poly(vinyl chloride) (PVC) was achieved in one‐step using copper‐mediated atom transfer radical polymerization to graft different ratios of random
Graft polymers with various sidechain lengths and grafting densities are prepared using
- Award ID(s):
- 2042494
- PAR ID:
- 10508369
- Publisher / Repository:
- Royal Society of Chemistry
- Date Published:
- Journal Name:
- Polymer Chemistry
- Volume:
- 14
- Issue:
- 43
- ISSN:
- 1759-9954
- Page Range / eLocation ID:
- 4927 to 4932
- Format(s):
- Medium: X
- Sponsoring Org:
- National Science Foundation
More Like this
-
Abstract n ‐butyl acrylate and 2–2‐(2‐ethoxyethoxy)ethyl acrylate copolymers from defect sites on the PVC chain. Five graft polymers were made with different ratios of poly(butyl acrylate) (PBA) and poly(2–2‐(2‐ethoxyethoxy)ethyl acrylate) (P2EEA); the glass transition temperatures (T g ) of functionalized PVC polymers range from − 25 to − 50°C. SingleT g values were observed for all polymers, indicating good compatibility between PVC and grafted chains, with no evidence of microphase separation. Plasticization efficiency is higher for polyether P2EEA moieties compared with PBA components. The resultant PVC graft copolymers are thermally more stable compared to unmodified PVC. Increasing the reaction scale from 2 to 14 g produces consistent and reproducible results, suggesting this method could be applicable on an industrial scale. -
Polymer nanoparticles are an emerging class of materials with potential impact in sensing, catalysis, imaging, cosmetics, and therapeutics. Here, a collection of graft polymers with conjugated polythiophene backbones were synthesized via a grafting-to approach. We functionalized polythiophene backbones with side chains of either poly(3-hexylthiophene) (P3HT), poly(ethylene oxide), or poly(methyl methacrylate) (PMMA) via copper-catalyzed azide–alkyne click chemistry. The backbones, graft polymers and a linear poly(3-hexylthiophene) were fabricated into nanoparticles through precipitation in aqueous media. We measured the absorption and emission spectra of the polymers dissolved in chloroform and as nanoparticles suspended in water. Compared to linear P3HT, all graft polymer nanoparticles exhibit higher quantum yields. Moreover, the addition of PMMA side chains increased the quantum yield by more than two orders of magnitude. This versatile approach to conjugated graft copolymer synthesis demonstrates a route for enhancing photoluminescence of conjugated polymer nanoparticles that could be beneficial for a variety of applications, such as biosensing and bioimaging.more » « less
-
ABSTRACT Shape memory polymers (SMPs) are a class of responsive polymers that have attracted attention in designing biomedical devices because of their potential to improve minimally invasive surgeries. Use of porous SMPs in vascular grafts has been proposed because porosity aids in transfer of fluids through the graft and growth of vascular tissue. However, porosity also allows blood to leak through grafts so preclotting the materials is necessary. Here hydrogels have been synthesized from acrylic acid and
N ‐hydroxyethyl acrylamide and coated around a porous SMP produced from lactose functionalized polyurea‐urethanes. The biocompatibility of the polymers used to prepare the cross‐linked shape memory material is demonstrated using anin vitro cell assay. As expected, the hydrogel coating enhanced fluid uptake abilities without hindering the shape memory properties. These results indicate that hydrogels can be used in porous SMP materials without inhibiting the shape recovery of the material. © 2019 Wiley Periodicals, Inc. J. Polym. Sci., Part A: Polym. Chem. 2019, 57, 1389–1395 -
While Si-containing polymers can often be deconstructed using chemical triggers such as fluoride, acids, and bases, they are resistant to cleavage by mild reagents such as biological nucleophiles, thus limiting their end-of-life options and potential environmental degradability. Here, using ring-opening metathesis polymerization, we synthesize terpolymers of (1) a “functional” monomer ( e.g. , a polyethylene glycol macromonomer or dicyclopentadiene); (2) a monomer containing an electrophilic pentafluorophenyl (PFP) substituent; and (3) a cleavable monomer based on a bifunctional silyl ether . Exposing these polymers to thiols under basic conditions triggers a cascade of nucleophilic aromatic substitution (S N Ar) at the PFP groups, which liberates fluoride ions, followed by cleavage of the backbone Si–O bonds, inducing polymer backbone deconstruction. This method is shown to be effective for deconstruction of polyethylene glycol (PEG) based graft terpolymers in organic or aqueous conditions as well as polydicyclopentadiene (pDCPD) thermosets, significantly expanding upon the versatility of bifunctional silyl ether based functional polymers.more » « less
-
Abstract The use of direct CH arylation cross‐coupling polymerization was evaluated for the synthesis of donor–acceptor conjugated co‐polymers using the novel donor 1,6‐didecylnaphtho[1,2‐
b :5,6‐b ']difuran and either thieno[3,4‐c ]pyrrole‐4,6‐dione (TPD) or 1,4‐diketopyrrolo[3,4‐c ]pyrrole (DPP) as the acceptor. Thiophene and furan moieties were used to flank the DPP group and the impact of these heterocycles on the polymers' properties was evaluated. The alkyl chains on the diketopyrrolopyrrole monomers were varied to engineer the solubility and morphology of the materials. All of the polymers have similar optoelectronic properties with narrow optical band gaps around 1.3 eV, which is ideal for solar energy harvesting. Unfortunately, these polymers also had high‐lying highest occupied molecular orbital levels of −4.8 to −5.1, and as a result bulk‐heterojunction photovoltaic cells fabricated using the soluble fullerene derivative PC71BM as the electron‐acceptor and these polymers as donor materials exhibited poor performance due to limited Vocvalues. An examination of the films from these blends indicates that film‐thickness and morphology were also a major hindrance to performance and a potential point of improvement for future materials.